以四硫代钼酸铵为原料、在甲酰胺-乙醇体系中,使用十六烷基三甲基溴化铵(CTAB)作为表面活性剂,通过溶剂热法成功制备出了球状MoS2,并对其进行SEM、TEM、XRD表征。结果表明,所制备样品为具有球状形貌、纯相的MoS2。同时将样品作为负极材料组装成扣式电池,并对其进行电化学性能测试。所制备的材料在0.28A/g的电流密度下首次充放电容量分别达到997.9mA·h/g、1179.1mA·h/g,库伦效率达到84.6%。经过100周恒流充放电循环后,材料的放电容量仍能达到740.8mA·h/g,样品表现出了良好的循环稳定性。
The spherical molybdenum disulfide was synthesized by solvothermal method used formamide-ethanol as solvent system,ammonium tetrathiomolybdate as raw material and hexadecyl trimethyl ammonium bromide (CTAB) as surfactant.The sample was characterized by XRD,SEM and TEM.The results showed that the prepared sample was pure MoS2 with spherical morphology.The sample was used as the cathode material assembled into a button cell and characterized by electrochemical performance test.The first charge/discharge capacity of material reached 997.9mA·h/g and 1179.1mA·h/g respectively under a current density of 0.28A/g and the coulombic efficiency reached 84.6%.After 100 cycles,the material retained the capacity of 740.8mA·h/g under the current density of 100 mA/g,the sample showed good cycling stability.
[1]Sharon M,Hsu W K,Kroto H W,et al.Camphor-based carbon nanotubes as an anode in lithium secondary batteries[J].Journal of Power Sources,2002,104(1):148-153.
[2]Jung D S,You N K,Kang Y C,et al.Recent progress in electrode materials produced by spray pyrolysis for next-generation lithium ion batteries[J].Advanced Powder Technology,2014,25(1):18-31.
[3]He L,Liao X Z,Yang K,et al.Electrochemical characteristics and intercalation mechanism of ZnS/C composite as anode active material for lithium-ion batteries[J].Electrochimica Acta,2011,56(3):1213-1218.
[4]Tenne R.Advances in the synthesis of inorganic nanotubes and fullerene-like nanoparticles[J].Angewandte Chemie International Edition,2003,42(42):5124-5132.
[5]Li X L,Li Y D.MoS2 nanostructures:synthesis and electrochemical Mg2+ intercalation[J].The Journal of Physical Chemistry B,2004,108(37):13893-13900.
[6]Hwang H,Kim H,Cho J.MoS2 nanoplates consisting of disordered graphene-like layers for high rate lithium battery anode materials[J].Nano Letters,2011,11(11):4826-4830.
[7]Du G,Guo Z,Wang S,et al.Superior stability and high capacity of restacked molybdenum disulfide as anode material for lithium ion batteries[J].Chemical Communications,2010,46(7):1106-1108.
[8]Zhao C,Kong J,Yao X,et al.Thin MoS2 nanoflakes encapsulated in carbon nanofibers as high-performance anodes for lithium-ion batteries[J].Acs Applied Materials & Interfaces,2014,6(9):6392-6398.
[9]Xie D,Xia X,Wang Y,et al.Nitrogen-doped carbon embedded MoS2 microspheres as advanced anodes for lithium- and sodium-ion batteries[J].Chemistry-A European Journal,2016,22(33):11617-11623.
[10]Ding J,Zhou Y,Li Y,et al.MoS2 nanosheet assembling superstructure with a three-dimensional ion accessible site:a new class of bifunctional materials for batteries and electrocatalysis[J].Chemistry of Materials,2016,28(7):2074-2080.
基金资助
国家自然科学基金(21671092)
PDF
(2563KB)