通过接触角法研究了推进剂用普通热塑性聚氨酯弹性体(BTPU)和改性后的热塑性聚氨酯弹性体(DTPU)粘合剂的表面性能,并通过进一步的分析比较了二者与推进剂中的高能硝胺黑索今(RDX)的相互作用大小,结果表明,DTPU的表面能(40.55mJ/m2)大于BTPU(34.59mJ/m2),DTPU与RDX的粘附功为81.83mJ/m2,BTPU与RDX的粘附功为72.30mJ/m2,DTPU与固体推进剂中RDX的粘结能力好于BTPU,更适用于用作固体推进剂的粘结剂。
Contact angle method was employed to investigate the surface properties of thermoplastic polyurethane elastomers(BTPU) and modified thermoplastic polyurethane elastomers(DTPU),both of which were used as binders for propellants.And the interactions of two kinds of thermoplastic polyurethane elastomers with high-energy ammonium nitrate hexogen (RDX) in propellants were further evaluated and compared.Results showed that the surface free energy of DTPU(40.55mJ/m2) was higher than BTPU(34.59mJ/m2),the interface adhesion energy between DTPU and RDX was 81.83mJ/m2 and the interface adhesion energy between BTPU and RDX was 72.30mJ/m2.That was to say that the adhesion energy between DTPU and RDX in solid propellants was better than that between BTPU and RDX.Thus DTPU was more suitable to be used as solid propellant binders than BTPU.
[1] 付小龙,樊学忠,张伟,等.端环氧聚丁二烯与固体填料之间表界面性能的研究[J].中国粘结剂,2015,24(7):22-25.
[2] Chen Y,Liu Y F,Shi L,et al.Study on the synthesis and interfacial interaction performance of novel dodecylamine-based bonding agents used for composite solid propellants[J].Propellants Explosives Pyrotechnics,2015,40(1):50-59.
[3] 张习龙,刘苗娥,王祝愿,等.BEBA对丁羟推进剂界面粘接作用的研究[J].固体火箭技术,2016,39(5):667-671.
[4] 郭惠丽,宁建会,王国强.提高复合推进剂力学性能的技术途径[J].火炸药学报,2008,31(4):67-71.
[5] 陈晓磊.固体聚合物表面接触角的测量及表面能研究[D].长沙:中南大学,2012.
[6] 吴伟,刘丹丹,徐志成,等.支链化甜菜碱和阳离子表面活性剂在聚甲基丙烯酸甲酯表面的吸附及其润湿性质[J].物理化学学报,2016,32(5):1214-1220.
[7] Colin A G,Peter C T,Michael D,et al.Estimating the mechanical properties of retinal tissue using contact angle measurements of a spreading droplet[J].Langmuir,2013,29(16):5080-5084.
[8] Tingey K G,Andrade J D.Probing microheterogeneity of poly (ether urethanes) in an aqueous environment[J].Langmuir,1991,7:2471-2478.
[9] Kwok D Y,Neumann A W.Contact angle measurement and contact angle interpretation[J].Advances in Colloid and Interface Science,1999,81:167-249.
[10] 王新平,陈志方,沈之荃.高分子表面动态行为与接触角时间依赖性[J].中国科学B辑,2005,35(1):64-69.
[11] 波丘斯 阿方萨斯V.粘结与胶黏剂技术导论[M].北京:化学工业出版社,2005,10-68.
[12] 胡福增,郑安呐.聚合物及其复合材料表界面[M].北京:中国轻工业出版社,2001,15-89.
[13] 张文雨,李晋庆,罗运军.具有键合功能热塑性聚氨酯的表面性能[J].高分子材料科学与工程,2012,28(2):28-31.
[14] Papadopoulou S K,Dritsas G,Karapanagiotis I,et al.Surface characterization of poly(2,2,3,3,3-pentafluoropropyl methacrylate) by inverse gas chromatography and contact angle measurements[J].European Polymer Journal,2010,46:202-208.
[15] 杜美娜.高能固体推进剂组分的界面性质研究[D].北京:北京理工大学,2008.
[16] 张文雨,李晋庆,罗运军,等.DBM和BDO为扩链剂的聚氨酯粘合剂性能[J].含能材料,2012,20(1):49-52.
基金资助
基础产品创新计划火炸药专项(A2220061373)
PDF
(1350KB)