化工新型材料

化工新型材料 ›› 2018, Vol. 46 ›› Issue (7) : 182-184.

科学研究

高比表面积氧化钒气凝胶纳米材料的常压制备及表征

^1,2

作者信息 +

Ambient pressure synthesis and characterization of vanadium oxide aerogel nanomaterial with high surface area

Cui Chaojun^1,2, Duan Linbo², Sun Xingchuan²

Author information +

文章历史 +

Received		Published
2017-11-20		2018-07-20
Issue Date	Revised Date
2018-08-07	2017-11-20

PDF (3289K)

摘要

以氧化钒(V₂O₅)粉末、纯度30%的过氧化氢(H₂O₂)、乙醇为原料,采用溶胶-凝胶法和溶剂替换工艺,在常压条件下制备了高比表面积V₂O₅气凝胶纳米材料。借助扫描电子显微镜、透射电镜、红外光谱、拉曼光谱、X射线衍射、比表面积以及热重分析测试技术对V₂O₅气凝胶的形貌及微观结构进行了系统表征。测试结果表明:经100℃热处理后的V₂O₅气凝胶纳米材料由直径20nm左右的纳米棒组成,呈三维网状结构,平均孔洞直径约18.7nm,比表面积为395m²/g。

Abstract

Vanadium oxide aerogel with high-surface area was prepared by sol-gel process used V₂O₅ power,H₂O₂ and ethanol as the starting materials and dried at ambient pressure.The morphology and microstructure of as-prepared samples were characterized and analyzed using SEM,TEM,XRD,FT-IR,Raman,BET and TG-DSC techniques.The results indicated that the resulted aerogels had a nanorods-like tridimensional network structure,the average pore diameter was about 18.7nm,the specific surface area was 395m²/g.

关键词

氧化钒 / 气凝胶 / 常压干燥 / 高比表面积

Key words

vanadium oxide / aerogel / ambient pressure drying / high surface area

引用本文

引用格式 ▾

高比表面积氧化钒气凝胶纳米材料的常压制备及表征[J]. 化工新型材料, 2018, 46(7): 182-184 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] 王真,戴珍,赵宁,等.气凝胶材料研究的新进展[J].高分子通报,2013(9):50-55.
[2] 刘守新,鄂雷,李伟,等.炭气凝胶研究现状及其发展前景[J].林业工程学报,2017,2(2):1-8.
[3] 吴国友,程璇,余煜玺,等.常压干燥制备二氧化硅气凝胶[J].化学进展,2010,22(10):1892-1900.
[4] 李明明,王坤杰,张晓虎.纤维增强SiO₂气凝胶复合材料研究进展[J].化工新型材料,2017,45(3):19-21.
[5] 陈宇卓,欧忠文,刘朝辉,等.隔热材料SiO₂气凝胶改性研究进展[J].化工新型材料,2017,45(8):45-47.
[6] 田军,乔秀丽,迟彩霞.石墨烯气凝胶的水热法制备及表征[J].应用化工,2017,46(7):1351-1358.
[7] 刘念平,沈军,关大勇,等.碳气凝胶活化对于电极嵌锂性能的影响[J].物理化学学报,2013,29(5):966-972.
[8] 张志华,王文琴,祖国庆,等.SiO₂气凝胶材料的制备、性能及其低温保温隔热应用[J].航空材料学报,2015,35(1):87-96.
[9] Passerini S,Ressler J J,Le D B,et al.High rate electrodes of V₂O₅ aerogel[J].Electrochimica Acta,1999,44(1999):2209-2217.
[10] 房兴梅,吴广明,王爱荣,等.锂电池阴极材料V₂O₅常压干燥气凝胶的制备及离子输运特性[J].功能材料与器件学报,2007,13(6):522-528.
[11] Fabrice C,Jong-Min Lee,Stefano P,et al.V₂O₅ aerogel-like lithium intercalation host[J].Solid State Ionics,1999,116(3):279-291.
[12] 张明霞,昊广明,孙娟萍,等.过氧化法常压干燥制备的V₂O₅气凝胶的性能探究[J].材料导报,2009,23(8):102-105.
[13] 王爱荣,吴广明,杨辉宇,等.多壁碳纳米管复合V₂O₅材料的制备及性能研究[J].材料导报,2008,22(8):108-119.
[14] Wang Ying,Cao Guozhong.Synthesis and enhanced intercalation properties of nanostructured vanadium oxides[J].Chem Mater,2006,18:2787-2804.
[15] 刘旭华,贾献峰,王际童,等.碳纳米管增强Al₂O₃-SiO₂气凝胶制备及性能研究[J].化工新型材料,2017,45(5):244-246.
[16] 李志华,张艳舞.同一体系内水热合成VO_x·nH₂O纳米线和纳米带[J].唐山师范学院学报,2009,31(2):16-18.
[17] 崔朝军,王磊,牛永生,等.水热合成温度对氧化钒纳米管的影响[J].化工新型材料,2013,41(6):75-77.
[18] 崔朝军,吴广明,张明霞,等.锂钒氧化物纳米管的合成与表征[J].无机材料学报,2009,24(4):787-792.
[19] Gao Guohua,Wu Guangming.Synthesis,structure and electrochemical properties of VO_x nanosheets prepared from V₂O₅ and carbon aerogels[J].Rare Metal Materials and Engineering,2016,45(S1):315-319.