化工新型材料

化工新型材料 ›› 2018, Vol. 46 ›› Issue (5) : 140-143.

科学研究

可控形貌BiVO₄的合成及其光催化性能研究

作者信息 +

Facile synthesis of BiVO₄ with tunable morphology for high photocatalytic performance

Lv Rui, Hu Yingyuan, Zhang Xiaochao, Wang Yawen, Wang Yunfang, Li Shuangzhi

Author information +

文章历史 +

Received		Published
2017-03-02		2018-05-20
Issue Date	Revised Date
2018-07-03	2017-03-02

PDF (2185K)

摘要

通过在溶剂热法过程中使用不同的溶剂合成了一系列具有不同形貌的m-BiVO₄光催化剂。采用X射线衍射(XRD)、红外光谱分析(FT-IR)、扫描电子显微镜(SEM)和紫外-可见漫反射(UV-Vis DRS)对合成样品进行表征分析,并考察不同形貌光催化剂的活性大小。结果表明:不同溶剂不仅可以影响合成的m-BiVO₄的形貌,而且对m-BiVO₄沿(010)晶面的生长也具有重要的作用。其中,以乙二醇为溶剂时得到的m-BiVO₄在可见光下降解亚甲基蓝(MB)时具有最好的光催化活性。其反应速率的提高归功于有效的光致载流子的分离和对MB吸附量的增加。

Abstract

A series of m-BiVO₄ photocatalyst with different morphology were prepared by solvothermal method using different solvents.X-ray diffraction (XRD),fourier transform infrared spectra (FT-IR),scanning electron microscopy (SEM) and UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS) were applied to characterize the composition,morphology and optical property of as-prepared samples.Results indicated that different solvents had a great influence on the crystal growth of m-BiVO₄ along (010) facets,as well as the morphology of samples,which further affected their photocatalytic performance.The as-obtained BiVO₄ using ethylene glycol as solvent showed the best degradation efficiency for the removal of MB under visible light irradiation.The enhanced photocatalytic performance could be ascribed to the enhanced adsorption capability for MB and improved separation of photo-generated electron-hole pairs.

关键词

BiVO₄ / 形貌 / 光催化 / 水热法

Key words

BiVO₄ / morphology / photocatalysis / solvothermal method

引用本文

引用格式 ▾

可控形貌BiVO₄的合成及其光催化性能研究[J]. 化工新型材料, 2018, 46(5): 140-143 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] 曾凡刚,王玮,吴燕红,等.化石燃料燃烧产物对大气环境质量的影响及研究现状[J].中央民族大学学报:自然科学版,2001,10(2):113-120.
[2] 刘志逊,刘珍奇,黄文辉.中国化石燃料环境污染治理重点及措施[J].资源·产业,2005,7(5):49-52.
[3] 韩金霞,崔玉民.无机光催化技术研究进展[J].化学试剂,2004,26(2):76-80.
[4] Yu L H,Zhang X Y,Li G W,et al.Highly efficient Bi₂O₂CO₃/BiOCl photocatalyst based on heterojunction with enhanced dye-sensitization under visible light[J].Applied Catalysis B:Environmental,2016,187:301-309.
[5] Li K,Liang Y J,Yang J,et al.Controllable synthesis of {001} facet dependent foursquare BiOCl nanosheets:a high efficiency photocatalyst for degradation of methyl orange[J].Journal of Alloys and Compounds,2017,695:238-249.
[6] Hu Y Y,Li R,Fan C M,et al.One-step synthesis of porous BiOBr film and Bi nanopowder simultaneously from Bi plate via electrochemical method[J].Materials Letters,2015,161:41-44.
[7] Qin X Y,Cheng H F,Wang W J,et al.Three dimensional BiOX (X=Cl,Br and I) hierarchical architectures:facile ionic liquid-assisted solvothermal synthesis and photocatalysis towards organic dye degradation[J].Materials Letters,2013,100(6):285-288.
[8] Yang Z Y,Huang L,Xie Y Y,et al.Controllable synthesis of Bi₂WO₆ nanoplate self-assembled hierarchical erythrocyte microspheres via a one-pot hydrothermal reaction with enhanced visible light photocatalytic activity[J].Applied Surface Science,2017,403:326-334.
[9] Zhu Y Y,Ling Q,Liu Y F,et al.Photocatalytic performance of BiPO₄ nanorods adjusted via defects[J].Applied Catalysis B:Environmental,2016,187:204-211.
[10] Kumari S,Li X,Wu F,et al.Design of a provably secure biometrics-based multi-cloud-server authentication scheme[J].Future Generation Computer Systems,2017,68:320-330.
[11] Umar A,Ahmad R,Kumar R,et al.Bi₂O₂CO₃ nanoplates:fabrication and characterization of highly sensitive and selective cholesterol biosensor[J].Journal of Alloys and Compounds,2016,683:433-438.
[12] Zhao G S,Liu W,Dong M,et al.Synthesis of monoclinic sheet-like BiVO₄ with preferentially exposed (040) facets as a new yellow-green pigment[J].Dyes and Pigments,2016,134:91-98.
[13] Wang Y,Liu F Y,Hua Y J,et al.Microwave synthesis and photocatalytic activity of Tb³⁺ doped BiVO₄ microcrystals[J].Journal of Colloid and Interface Science,2016,483:307-313.
[14] Zhou D H,Zhu Z J,Liu B J.Solvothermal synthesis and characterization of a novel reduced graphene oxide (RGO)/BiVO₄/SiO₂ nanocomposites[J].Materials Letters,2016,185:32-35.
[15] Zhao G S,Liu W,Li J Y,et al.Facile synthesis of hierarchically structured BiVO₄,oriented along (010) facets with different morphologies and their photocatalytic properties[J].Applied Surface Science,2016,390:531-539.
[16] Li R,Gao X Y,Fan C M,et al.A facile approach for the tunable fabrication of BiOBr photocatalysts with high activity and stability[J].Applied Surface Science,2015,355:1075-1082.
[17] Wang M,Guo P Y,Chai T Y,et al.Effects of Cu dopants on the structures and photocatalytic performance of cocoon-like Cu-BiVO₄,prepared via ethylene glycol solvothermal method[J].Journal of Alloys and Compounds,2017,691:8-14.
[18] Chen F,Yang Q,Li X M,et al.Hierarchical assembly of graphene-bridged Ag₃PO₄/Ag/BiVO₄,(040) Z-scheme photocatalyst:an efficient,sustainable and heterogeneous catalyst with enhanced visible-light photoactivity towards tetracycline degradation under visible light irradiation[J].Applied Catalysis B:Environmental,2017,200:330-342.
[19] Cao J,Zhou C C,Lin H L,et al.Surface modification of m-BiVO₄,with wide band-gap semiconductor BiOCl to largely improve the visible light induced photocatalytic activity[J].Applied Surface Science,2013,284(11):263-269.
[20] Lv D D,Zhang D F,Pu X P,et al.One-pot combustion synthesis of BiVO₄/BiOCl composites with enhanced visible-light photocatalytic properties[J].Separation and Purification Technology,2017,174:97-103.
[21] Zhao J,Yan J H,Jia H J,et al.BiVO₄/g-C₃N₄,composite visible-light photocatalyst for effective elimination of aqueous organic pollutants[J].Journal of Molecular Catalysis A:Chemical,2016,424:162-170.