在粉煤灰改性的基础上,通过与丙烯酸、丙烯酰胺共聚,水溶液聚合法制备了复合高吸水性树脂。通过对中和度、引发剂用量、交联剂用量、单体质量比和改性粉煤灰用量等实验条件的优化,确定了最佳反应条件。结果表明:在最佳反应条件下,该吸水树脂具有好的吸水性和耐盐性,其在蒸馏水和0.9% NaCl中的吸水率分别为543.7和178.6g/g。并使用红外光谱法对其结构进行了表征与分析。
The resin was synthesized by the aqueous solution copolymerization of acrylic acid,acrylamide and fly ash after pretreatment.The optimal reaction conditions were determined by optimizing the experimental conditions such as acrylic acid neutral degree,initiator and crosslinker dosages,the ratio of acrylamide to acrylic acid,and the amount of modified fly ash.Under the optimal reaction condition,the water absorbency was 543.7g/g for water and 178.6g/g for 0.9% salt solution,respectively.The resin had higher water absorbency and stronger salt resistance.The structure of resin was also characterized by FT-IR.
[1] 徐继红,许少薇,周加深,等.GA-g-PAMPS/APT高吸水性树脂的合成和溶胀行为[J].精细化工,2016,33(7):753-760.
[2] 贺龙强,胡鹏,刘中阳.绿色耐盐性淀粉/膨润土基复合高吸水性树脂的制备[J].现代化工,2015,35(6):84-87.
[3] 孟龙,孙宾宾,高红军.高吸水性树脂的研究进展[J].广东化工,2014,41(3):92-93.
[4] 梁瑞婷,李锦凤,周新华,等.凹凸棒/膨润土/聚丙烯酸钠复合吸水树脂的合成及其吸水速率[J].化工新型材料,2008,36(3):36-38.
[5] 刘艳军,李亚峰,张佩泽.改性粉煤灰处理含铬废水的研究[J].工业安全与环保,2008,34(6):45-45.
[6] 周托,张忠孝,乌晓江,等.粉煤灰合成沸石去除废水中铜离子的研究[J].煤炭转化,2011,34(2):76-81.
[7] 付克明,朱虹,张勤善,等.湿法加碱-煅烧粉煤灰合成P沸石的研究[J].武汉理工大学学报,2010,32(6):32-35.
[8] 李铭杰,李仲谨,郝明德,等.AC/XG-g-PAA复合高吸水性树脂的制备及性能研究[J].精细化工,2010,27(10):947-952.
[9] 凌辉,沈上越,范力仁,等.粉煤灰煅烧除碳对高吸水树脂复合材料的影响[J].矿产综合利用,2006(5):13-16.
[10] 柳明珠,曹丽歆.丙烯酸与海藻酸钠共聚制备耐盐性高吸水树脂[J].应用化学,2002,19(5):455-458.
[11] 张立颖,廖朝东,尹沾合,等.高吸水树脂的吸水机理及吸盐性的改进[J].应用化工,2009,38(2):282-285.
基金资助
河南省高等学校重点科研项目(16B150009);焦作市科技计划项目(20170155)
PDF
(1311KB)