聚丙烯腈基(PAN)中空多孔纤维微孔结构丰富,质轻,比表面积大,是碳材料领域的新起之秀。从PAN基中空多孔碳纤维的发展史、制备方法、应用等方面,简要阐述了它的研究现状,并对今后发展提出了几点展望,以期为中空多孔碳纤维的研究工作提供一定的帮助。
Polyacrylonitrile-based hollow-porous carbon fiber which has various macro-porous structure,light weight and large specific surface area arise interest of researcher.Research statue of it was introduced with respect to the history,processing and areas of application.Some directions for future were also prospected.It will helpful for investigation on hollow-porous carbon fiber.
[1] 李光.多孔碳纤维的低成本制备及其作为高效吸波剂的应用研究[J].高科技纤维与应用,2013,38(1):34-39.
[2] Yang M C,Yu D G.Influence of precursor structure on the properties of polyacrylonitrile-based activated carbon hollow fiber[J].Journal of Applied Polymer Science,1996,59(11):1725-1731.
[3] Yang M C,Yu D G.Influence of oxidation conditions on polyacrylonitrile-based activated hollow carbon fibers[J].Textile Research Journal,1996,66(2):115-121.
[4] Yang M C,Yu D G.Influence of activation temperature on the properties of polyacrylonitrile-based activated carbon hollow fiber[J].Journal of Applied Polymer Science,1998,68(8):1331-1336.
[5] 孙俊芬,武利顺,王庆瑞.活化温度对聚丙烯腈基活性中空炭纤维结构和吸附性能的影响[J].合成纤维工业,2004,27(5):7-10.
[6] Sun J F,Wu G X,Wang Q R.The effects of carbonization time on the properties and structure of PAN-based activated carbon hollow fiber[J].Journal of Materials Science,2005,40(3):663-668.
[7] Pam C,Ge L Q,Gu Z Z.Fabrication of multi-walled carbon nanotube reinforced polyelectrolyte hollow nanofibers by electrospinning[J].Composites Science and Technology,2007,67(15-16):3271-3277.
[8] Kozlov M E,Capps R C,Sampson W M,et al.Spinning solid and hollow polymer-free carbon nanotube fibers[J].Advanced Materials,2005,17(5):614-617.
[9] 付正芳,王庆瑞,王曙中.中空活性碳纤维概述[J].高科技纤维与应用,2003,28(5):32-35.
[10] 沈新元,王庆瑞,陈雪英,等.聚丙烯腈中空纤维膜的纺制及其应用[J].合成纤维,1989(6):14-18.
[11] Jia Z,Lu C,Liu Y,et al.Lignin/polyacrylonitrile composite hollow fibers prepared by wet spinning method[J].ACS Sustainable Chemistry & Engineering,2016,4(5):2838-2842.
[12] 胡坚.聚丙烯腈基中空超细碳纤维的制备及形貌研究[D].上海:东华大学,2010.
[13] 黄争鸣,张彦中.共轴复合连续纳/微米纤维及其制备方法:中国,1537981[P].2004-10-20.
[14] 黄争鸣,董国华.制备共轴复合连续纳/微米纤维的多喷头静电纺丝装置:中国,1546753[P].2004-11-17.
[15] 黄争鸣.一种有效包含功能材料的涂装层及其制备方法:中国,1660506[P].2005-08-31.
[16] 陈水挟,陆耘,曾汉民.剑麻基活性炭纤维的制备及其碳化活化动力学[J].合成纤维工业,1998,21(5):12-14.
[17] Molinasabio M,Gonzlez M T,Rodriguezreinoso F,et al.Effect of steam and carbon dioxide activation in the micropore size distribution of activated carbon[J].Carbon,1996,34(4):505-509.
[18] 岳中仁,陆耘,曾汉民.活性碳纤维ZCSACF的制备及其氧化还原吸附性能[J].离子交换与吸附,1995(3):210-215.
[19] 岳中仁,陆耘,曾汉民.KOH活化制备活性碳纤维的研究[J].功能材料,1996,27(4):85-89.
[20] 刘杰,王平华.PAN基ACF的结构表征(Ⅱ)─氮元素与结合态变化的浅析[J].新型炭材料,1999,14(2):29-34.
[21] Kolosov O,Suzuki M,Yamanaka K.Microscale evaluation of the viscoelastic properties of polymer gel for artificial muscles using transmission acoustic microscopy[J].Journal of Applied Physics,1993,74(10):6407-6412.
[22] 付正芳.聚丙烯腈基中空活性炭纤维的制备及储氢性能的研究[D].上海:东华大学,2005.
[23] 谢炜.中空多孔炭纤维轻质吸波材料研究[D].长沙:国防科学技术大学,2008.
PDF
(1161KB)