PDF (1302K)
摘要
以甲基乙烯基硅橡胶为基体,加入表面改性后的气相法白炭黑及其他助剂制得发泡硅橡胶。采用红外光谱(FT-IR)和活性指数对白炭黑改性效果进行评价;探索了加入改性白炭黑后发泡硅橡胶的力学性能;通过热分析对其耐热性能进行测试。结果表明,白炭黑用偶联剂KH560改性后活性指数由82.3%提高到93.1%,添加改性白炭黑40%(wt,质量分数)时发泡硅橡胶综合性能最优,其抗撕强度为4.8823N/mm、拉伸强度为0.697MPa、断裂伸长率为498.63%、表观密度为0.553g/cm3、邵氏硬度为18.26HA,落球回弹率为31.70%,热稳定性也较好。
Abstract
Base on the methyl vinyl silicone rubber,added the surface-modified fumed silica and the other additives,silicone rubber was prepared.The modifying effect of foam by modified silica was evaluated by activity index and fourier transform infrared spectroscopy (FT-IR).It was also explored that the mechanical properties of foamed silicone rubber with modified silica.In addition,it was also tested that its heat resistance by thermal analysis.The results showed that the activity index of silica modified by KH560 increased from 82.3% to 93.1%.When added 40wt% modified silica,the comprehensive performance of foamed silicone rubber was optimal and its tear strength was 4.8823N/mm,the tensile strength was 0.697MPa.Besides,the fracture elongation and apparent density were 498.63% and 0.553g/cm3 respectively.Moreover the shaw hardness was 18.26HA,the falling ball bounce rate was 31.70% and had good thermal stability.
关键词
甲基乙烯基硅橡胶
/
KH560
/
气相法白炭黑
/
发泡硅橡胶
/
力学性能
Key words
methyl vinyl silicone rubber
/
KH560
/
fumed silica
/
foam silicone rubber
/
mechanical property
气相法白炭黑表面改性及对发泡硅橡胶的性能影响[J].
化工新型材料, 2018, 46(2): 238-241 DOI:
[1] 周宁琳.有机硅聚合物导论[M].北京:科学出版社,2000,89-170.
[2] 李彬.新型硅橡胶泡沫材料的制备与性能研究[D].广州:华南理工大学,2011.
[3] 李智敏,吴友平.高抗撕裂硅橡胶复合材料的制备[J].合成橡胶工业,2015,38(2):141-144.
[4] 王香爱,张洪利.硅橡胶的研究进展[J].中国胶粘剂,2012,21(9):44-48.
[5] 戚云霞,赵士贵,姜伟峰,等.加成型室温硫化硅橡胶的研究进展[J].有机硅材料,2006,20(1):34-37.
[6] 胡义.泡沫硅橡胶用白炭黑的改性[J].有机硅材料,2000,14(6):32-34.
[7] Frohlich J,Luginsland H D.RPA-studies into the silica/silicane system[J].Rubber World,2001,16(4):28-35.
[8] Gerspacher M,Nikiel L,Yang H H,et al.Flocculation in carbon black filled rubber compounds[J].Kautschuk Gummi Kunststoffe,2002,55(11):596-597.
[9] 雷海军,王进文.热硫化型硅橡胶海绵发泡机理浅析[J].弹性体,2002,12(1):24-30.
[10] Guido Raos.Application of the Christensen-Lo model to the reinforcement of elastomers by fractal fillers[J].Macromolacular Theory and Simulations,2003,12(1):17-23.
[11] 刘杰胜,张宗旺,郑雄贞,等.有机硅偶联剂改性SiO2作用机理研究[J].胶体与聚合物,2013,31(1):23-25.
[12] 魏仕涛,夏志伟,周远建.液体室温硫化硅橡胶在泡沫材料领域的研究进展[J].化工新型材料,2015,43(4):18-26.
[13] 扈广法,黄捷.提高低硬度硅橡胶撕裂强度的配方设计[J].合成橡胶工业,2002,25(3):248-250.