以环氧树脂为胶粘剂,以聚酰胺为固化剂,采用化学浸渍法在AZ91镁合金表面制备了环氧有机涂层,在制备过程中添加不同含量的蓖麻油,采用扫描电子显微镜(SEM)、X射线衍射仪(XRD)和红外光谱(FT-IR)等手段表征了复合有机涂层的组成及微观结构,并用电化学极化曲线及电化学阻抗谱考察了蓖麻油的添加对环氧有机涂层防腐性能的影响。结果表明:环氧有机涂层具有一定的抗腐蚀性能,在制备有机涂层前,对镁合金基底进行磷酸盐转化,可以提高有机涂层与基底的结合力;适量蓖麻油的添加可大大提高复合涂层的防腐能力,当蓖麻油加入量为3%时,得到的复合涂层防腐性能最佳,其腐蚀电位可以达到-0.823V,比未添加时提升了374mV。
The epoxy organic coating was prepared by chemical immersion method on the surface of AZ91 magnesium alloy with the epoxy resin as adhesive and polyamide as curing agent.And the different concentration castor oil was added in the preparation process.The microstructure and composition of complex organic coating were characterized using scanning electron microscopy (SEM),X-ray diffraction (XRD) and infrared spectroscopy (FT-IR),and the influence of castor oil on the performance of coating was investigated by the electrochemical polarization curve and the electrochemical impedance spectroscopy.The results showed that the coating had the corrosion resistance and the conversion of phosphate before the preparation of organic coating can improve the adhesion of coating and the magnesium alloy substrate.A certain amount of castor oil can greatly improve the corrosion resistance of coating and the best corrosion resistance appeared when the amount of castor oil was 3%,the corrosion potential can reach -0.823V,the increasing was 374mV more than that without castor oil.
[1] Veys-Renaux D,Rocca E,Henrion G.Micro-arc oxidation of AZ91 mg alloy:an in-situ electrochemical study[J].Electrochemistry Communications,2013,31:42-45.
[2] Zhang S F,Zhang R F,Li W K,et al.Effects of tannic acid on properties of anodic coatings obtained by micro arc oxidation on AZ91 magnesium alloy[J].Surface and Coatings Technology,2012,207(8):170-176.
[3] 赵旭辉,张晓丰,唐聿明,等.AZ31镁合金的微弧氧化处理及其对粘接性能的影响[J].材料导报B:研究篇,2012,26(1):76-79.
[4] Zhang X,Xiao G Y,Jiao Y,et al.Facile preparation of hopeite coating on stainless steel by chemical conversion method[J].Surface and Coatings Technology,2014,240(2):361-364.
[5] Zeng R C,Lan Z D,Kong L H,et al.Characterization of calcium-modified zinc phosphate conversion coatings and their influences on corrosion resistance of AZ31 alloy[J].Surface and Coatings Technology,2011,205(2):3347-3355.
[6] Phuong N V,Lee K H,Chang D,et al.Effects of Zn2+ concentration and pH on the zinc phosphate conversion coatings on AZ31 magnesium alloy[J].Corrosion Science,2013,74(9):314-322.
[7] Phuong N V,Moon S.Comparative corrosion study of zinc phosphate and magnesium phosphate conversion coatings on AZ31 Mg alloy[J].Materials Letters,2014,122(5):341-344.
[8] 明杜,舒武炳,秦卫.防腐环氧树脂粘接涂层的研究进展[J].中国胶粘剂,2011,20(7):53-57.
[9] She Z X,Wang Z W,Tan C,et al.Highly anticorrosion,self-cleaning superhydrophobic Ni-Co surface fabricated on AZ91D magnesium alloy[J].Surface and Coatings Technology,2014,251:7-14.
[10] Palraj S,Selvaraj M,Maruthan K,et al.Corrosion and wear resistance behavior of nano-silica epoxycomposite coatings[J].Progress in Organic Coatings,2015,81:132-139.
[11] Mülazim Y,Çakmakçi E,Kahraman M V.Preparation of photo curable highly hydrophobic coatings using a modified castor oil derivative as a sol-gel component[J].Progress in Organic Coatings,2011,72(9):394-401.
[12] 李学良,孙炜.蓖麻油改性的水性聚氨酯涂料的制备及其防蚀性能[J].广东化工,2010,37(5):3-5.
[13] 于伟岸,李青山,洪伟,等.蓖麻油改性封端型水性聚氨酯的制备及性能研究[J].聚氨酯工业,2011,26(6):35-38.
[14] 吕建平,李彬,张磊,等.蓖麻油硅氧烷双重交联改善水性聚氨酯的耐水性[J].聚氨酯工业,2011,26(3):37-39.
[15] 尚东升.单组分蓖麻油聚氨酯粘合剂初粘性的改进[J].聚氨酯工业,2005,20(5):32-34.
[16] 胡飞燕.水性聚氨酯涂膜耐水性影响因素研究[J].广东化工,2007,34(11):34-36.
[17] 高焕方,张胜涛,赵波,等.植酸浓度对AZ31B镁合金植酸转化膜防腐性能的影响[J].材料工程,2010(9):45-49.
[18] Alam M,Akram D,Sharmin E,et al.Vegetable oil based eco-friendly coating materials:a review article[J].Arabian Journal of Chemistry,2014,7(4):469-479.
基金资助
国家自然科学基金(21463017和21003070);内蒙古自然科学基金(BMYJ2010005);内蒙古自治区蓖麻育种重点实验室开放基金项目(2012MS0208、BMYJ2015-03和MDK2016002);内蒙古自治区通辽市和内蒙古民族大学合作项目(SXYB2012053)
PDF
(3292KB)