摘要
在小试确定的最佳工艺条件下,采用中试工艺制备微-纳米碳酸钙(CaCO3)复合粉体,利用pH计、温度计和电导率仪测量了反应体系的酸度、温度和电导率,并分析了其变化规律。研究结果表明,反应体系的起始pH约12,在较长一段时间里保持相对平稳、缓慢下降和迅速下降阶段,反应结束时pH约为7;500目、1250目、5000目、7000目反应体系pH出现拐点的反应时间分别约70、90、100和80min;反应体温度出现拐点的反应时间分别约100、90、100和100min;反应结束后温度上升分别约8、8、6和2℃;电导率出现拐点的反应时间分别约90、90、100和80min。可以根据酸度、温度和电导率值出现拐点,尤其是电导率的拐点,来判断反应结束,研究结果对工业化生产具有指导作用。
Abstract
The spilot-scale process was used to prepare the micro-nano calcium carbonate composite powder under the experimental conditions determined by the small scale process.The acidity,temperature and conductivity of reaction system were measured by pH meter,thermometer and conductivity meter (TDS),and their change laws were analyzed.The results showed that the initial value of pH was about 12,and relatively remained stable and declined very slowly for a long time during the reaction,then declined fast,at last declined slowly,the pH was about 7 at the end of the reaction.The pH inflection points of 500,1250,5000 and 7000 mesh reaction systems were about 70,90,100,80min,respectively.The temperature inflection points were about 100,90,100,100min,respectively.The conductivity inflection points were 90,90,100,80min,respectively.The inflection points of curves of acidity,temperature and conductivity of reaction system,especially the curve of conductivity could be used to judge the reaction end point.The investigating results were very important guidance roles for industrial production.
关键词
碳酸钙
/
复合粉体
/
反应机理
/
动力学
Key words
calcium carbonate
/
composite powder
/
reaction mechanism
/
dynamics
中试工艺制备微-纳米碳酸钙复合粉体的动力学及其反应终点判定研究[J].
化工新型材料, 2018, 46(2): 143-146 DOI:
[1] 郑水林.重质碳酸钙生产技术现状与趋势[J].无机盐工业,2015,47(5):1-4.
[2] 吴成宝,盖国胜,任晓玲,等.不同品种重质碳酸钙粉在外墙涂料中的应用[J].中国粉体技术,2011,17(2):16-19.
[3] 段好,王燕民,潘志东.采用混合改性剂改性超细碳酸钙塑料填料[J].中国粉体技术,2011,17(4):45-50.
[4] 邹燕,纪彬彬,温变英.滑石粉、碳酸钙填充聚丙烯复合材料等温结晶行为的研究[J].中国塑料,2010,24(2):26-29.
[5] 孙强.聚丙烯/无机粉体/异形纤维复合材料的制备[J].中国塑料,2012,26(4):54-60.
[6] 张周达,陈雪梅,董源,等.纳米碳酸钙-粉末橡胶复合粒子增强增韧聚氯乙烯[J].复合材料学报,2012,29(6):19-25.
[7] 周朋朋,栾英豪,马新胜.纳米碳酸钙表面改性剂的合成及其应用于PVC的研究[J].塑料工业,2013,41(9):39-43.
[8] 郎萌萌,焦运红,谢吉星,等.仿生合成碳酸钙的制备及其在PVC中的应用[J].塑料科技,2010,38(10):77-80.
[9] Abd A.Studying the mechanical and electrical properties of epoxy with PVC and calcium carbonate filler[J].International Journal of Engineering and Technology,2014,3(4):545-553.
[10] Jiao Y H,Peng F,Xu J Z,et al.Biomimetic synthesis of zinc hydroxystannate-coated calcium carbonate and its application in PVC[J].Chemical Engineer,201,25(5):5-8.
[11] 蔡楚江,吴芸,沈志刚.重质碳酸钙颗粒气流粉碎与表面改性的一体化处理[J].中国粉体技术,2012,18(1):18-21.
[12] 盖国胜.微纳米颗粒复合与功能化设计[M].北京:清华大学出版社,2008:156-161.
[13] 刘银,吴燕.纳米包覆重质碳酸钙用作造纸填料的研究[J].中国造纸,2013,32(2):16-21.
[14] 崔爱莉,王亭杰,金涌,等.二氧化钛表面包覆氧化硅纳米膜的热力学研究[J].高等学校化学学报,2001,22(9):1543-1545.
[15] 吴德海,任家烈,陈森灿.近代材料加工原理[M].北京:清华大学出版社,1997,24-89.
[16] 潘金生.材料学基础[M].北京:清华大学出版社,1998,12-128.
基金资助
国家自然科学基金项目(50974079)