Using titanium-containing furnace slag as the raw material,a submicron sheet-like silicon-based titanium dioxide photocatalyst was synthesized by hydrothermal-acidification-calcination process.The effects of acid hydrolysis reaction concentration,acid hydrolysis reaction time,photocatalyst dosage,and light conditions on the catalytic performance were studied.The results showed that when the acid hydrolysis concentration was 1.2mol/L,the acid hydrolysis reaction time was 5h,and the amount of photocatalyst was 20mg,the methylene blue degradation rate was up to 97.28% after 60min under UV irradiation,and the methylene blue removal rate was up to 77.85% after 120min under visible light irradiation.
[1] Que Z,Li Y,Yu H,et al.Controllable synthesis of nanorod/nanodisk TiO2 from titanium-containing electric furnace molten slag[J].Rare Metals,2015,34(4):267-275.
[2] Cai Y,Song N,Yang Y,et al.Recent progress of efficient utilization of titanium-bearing blast furnace slag[J].International Journal of Minerals Metallurgy and Materials,2022,29(1):22-31.
[3] Qiu G,Guo Y.Current situation and development trend of titanium metal industry in China[J].International Journal of Minerals,Metallurgy and Materials,2022,29(4):599-610.
[4] Fan G,Wang M,Dang J,et al.A novel recycling approach for efficient extraction of titanium from high-titanium-bearing blast furnace slag[J].Waste Manage,2020,120:626-634.
[5] Zhu S,Hu J,Zhang C,et al.Process optimization and kinetics of titanium leaching from mechanically activated titanium-bearing blast furnace slag[J].Journal of Sustainable Metallurgy,2022,9(1):230-239.
[6] Wang L,Chen L,Liu W,et al.Recovery of titanium,aluminum,magnesium and separating silicon from titanium-bearing blast furnace slag by sulfuric acid curing-leaching[J].International Journal of Minerals,Metallurgy and Materials,2022,29(9):1705-1714.
[7] 阙再青,李克非,刘洋,等.水热法从含钛电炉熔分渣中制备纳米片状结构二氧化钛光催化剂[J].北京科技大学学报,2012,34(8):931-938.
[8] 张小雪.赤铁矿非均相类Fenton反应降解亚甲基蓝的研究[D].西安:西安科技大学,2013.
[9] Kuo W S,Ho P H.Solar photocatalytic decolorization of methylene blue in water[J].Chemosphere,2001,45(1):77-83.
[10] Davis R J,Gainer J L,O'Neal G,et al.Photocatalytic decolorization of wastewater dyes[J].Water Environment Research,1994,66(1):50-53.
[11] Mahadik M A,An G W,David S,et al.Fabrication of A/R-TiO2 composite for enhanced photoelectrochemical perfor-mance:solar hydrogen generation and dye degradation[J].Applied Surface Science,2017,426:833-843.
基金资助
国家自然科学基金(21666015)
PDF