采用硅烷偶联剂,二氧化硅,有机硅憎水剂对不饱和聚酯树脂进行改性。采用红外光谱(FT-IR)对材料进行了表征,考察了改性剂对不饱和聚酯树脂力学性能和耐水性的影响。结果表明:添加二氧化硅综合性能最优,吸水率降低,耐磨性提升最为明显,磨损率降低了30%,拉伸弹性模量144MPa,断裂伸长率7.3%,拉伸应力55.45N,拉伸强度15.5kN。
The unsaturated polyester resin was modified with silane coupling agent,silica and organosilicon hydrophobic agent.FT-IR was used to characterize the materials,and the influence of modifiers on the mechanical properties and water resistance of the unsaturated polyester resin was investigated.The results showed that the addition of silicon yielded the optimal comprehensive performance,with a reduction in water absorption rate,the most obvious increase in wear resistance,a 30% reduction in wear resistance,a tensile elastic modulus of 144MPa,an elongation at break of 7.3%,a tensile stress of 55.45N,and a tensile strength of 15.5kN.
[1] 曹鑫.真空导入工艺用不饱和聚酯树脂的研制[J].纤维复合材料,2009(4):12-13.
[2] 张震乾,吴海银,张志贤.成分比例不同的MEKP固化不饱和聚酯树脂研究[J].热固性树脂,2009,24(1):24-26.
[3] 李相权.我国涂料用不饱和聚酯树脂研究进展[J].上海涂料,2011,49(12):36-39.
[4] 刘方方,邵志轩,可同欢,等.TDI改性原子灰用不饱和聚酯树脂的研究[J].涂料工业,2012,42(3):70-71.
[5] 朱立新,黄凤来,祝亚非,等.高交联度的不饱和聚酯增韧改性的固化特征及动力学分析[J].复合材料,2003,20(3):22-26.
[6] 黄小慧,李海霞.双环戊二烯改性不饱和聚酯树脂的研究[J].精细与专用化学品,2006,14(1):19-22.
[7] 杨凯,朱海斌,胡剑青,等.双环戊二烯改性不饱和聚酯树脂的研究[J].现代涂料与涂装,2007,10(1):4-7.
[8] 雷文,徐菡芳,朱智慧.不同纳米粒子改性不饱和聚酯树脂的对比研究[J].热固性树脂,2008,23(6):35-37.
[9] 齐双春,赵英强,吕海燕.纳米CaCO3粒子对不饱和聚酯树脂性能影响研究[J].玻璃钢/复合材料,2007(4):30-33.
[10] 朱立新,王小萍,贾德民.不饱和聚酯的增韧改性及机理[J].绝缘材料,2004,37(1):52-59.
[11] 瞿金清,陈焕钦.醇酸树脂涂料干燥机理的研究进展[J].合成材料老化与应用,2001(3):24-26,30.
[12] 台会文,武维汀,张留成.不饱和聚酯/聚氨酯互穿网络聚合物基玻璃纤维增强材料的研究[J].高分子材料科学与工程,2000,16(1):140-142.
[13] 程丝,王新波.不饱和聚酯增韧技术进展及机理探讨[J].合成技术及应用,2004,19(1):20-22.
[14] 徐喻琼,游敏,郑小玲,等.二氧化硅对不饱和聚酯树脂浇铸体力学性能的影响[J].弹体,2007,17(1):7-10.
[15] 徐喻琼,游敏,瞿金平,等.二氧化硅增强增韧不饱和聚酯[J].华南理工大学学报,2008,36(4):110-114.
[16] 魏明,黄志杰,左美群,等.纳米SiO2在不饱和聚酯树脂中的应用[J].玻璃钢,1998(8):31-33.
[17] 龚兵,李玲,董凤云.不饱和聚酯树脂改性研究进展[J].绝缘材料,2006,39(4):25-28.
[18] Liu Chengguo,Lei Wen,Cai Zhengchun,et al.Use of tung oil as a reactive toughening agent indicyclopentadiene-terminated unsaturated polyester resins[J].Industrial Crops and Products,2013,49:412-418.
[19] Drocha M J,Riberi B H.Water-reducible unsaturated polymers as binders and clear coatings for UV-curable furniture coatings[J].Journal of Coatings Technology,1992,43(64):808～815.
[20] Patrycja B,Dariusz M,Rafal B,et al.Bio-based polyethylene composites with natural fiber:mechanical,thermal and ageing properties[J].Materials,2020,13(11):2595-2615.
[21] Fang M,Zhang N,Huang M,et al.Effects of hydrothermal aging of carbon fiber reinforced polycarbonate composites on mechanical performance and sand erosion resistance[J].Polymers,2020,12(11):2453.
[22] Shang S W,Williams K J W.Influence of nanosilica particles and research advances of polymer/Silica nanocomposites[J].Journal of Materials Science,1992(27):4949-4956.
[23] 葛曷一,王继辉.纳米材料改性不饱和聚酯树脂的研究[J].玻璃钢/复合材料,1999(3):13-14.
[24] 徐群华,孟卫.纳米二氧化钛增强增韧不饱和聚酯树脂的研究[J].高分子材料科学与工程,2001,17(2):158-160.
[25] 张建华,姜其斌,林金火.有机硅改性不饱和聚酯树脂的制备及应用研究[J].绝缘材料,2007,40(1):3.
[26] 陆昶,燕小然,邹犁野,等.碳酸钙填料对不饱和聚酯树脂体积收缩的影响及其机制[J].复合材料学报,2008,25(5):6.
[27] 伍钦,蔡梅琳,曾朝霞,等.不饱和聚酯树脂的进展[J].化工进展,1999,18(6):3.
[28] 唐君,徐国财,沈娜.松香改性对苯型不饱和聚酯树脂的合成及性能[J].热固性树脂,2009,24(4):3.
基金资助
国家自然科学基金青年科学基金项目(51705414);国家自然科学基金(51641105)
PDF