采用静电纺丝技术制备聚偏氟乙烯(PVDF)/聚丙烯腈(PAN)纤维膜,通过控制多巴胺(DA)浓度自聚合形成聚多巴胺(PDA)纳米簇,并将其沉积在PVDF/PAN纤维膜表面,得到PDA@PVDF/PAN纤维膜。通过扫描电子显微镜、傅里叶变换红外光谱仪、接触角分析仪等对PDA@PVDF/PAN纤维膜进行表征并测试了其油水分离性能。结果表明,PDA负载到PVDF/PAN纤维膜表面,与未改性纤维膜相比,PDA@PVDF/PAN纤维膜接触角减小了102.8°,对菜籽油/水混合物的分离效率均在97%以上,经过6次循环后,分离效率未发生显著变化,对石油醚/水乳液的过滤效率高达96.6%,表现出优异的过滤效率和耐久性能。
Polyvinylidene fluoride (PVDF)/polyacrylonitrile (PAN) fiber membrane was prepared by electrospinning technology.Polydopamine (PDA) nanoclusters were formed by self-polymerization under the control of dopamine concentration,and deposited on the PVDF/PAN fiber membrane surface to prepare PDA@PVDF/PAN fiber membrane.The PDA@PVDF/PAN fiber membrane was characterized by scanning electron microscope,Fourier transform infrared spectrometer and contact angle analyzer,and its oil-water separation performance was tested.The results showed that PDA was loaded on the PVDF/PAN fiber membrane surface.Compared with the unmodified fiber membrane,the contact angle of PDA@PVDF/PAN fiber membrane was reduced by 102.8°,and the separation efficiency of rapeseed oil/water mixture was above 97%.After 6 cycles,the separation efficiency did not change significantly,and the filtration efficiency of petroleum ether/water emulsion was as high as 96.6%,showing excellent filtration efficiency and durability.
[1] Cheng H A,Wei Y,Jiang Q Z,et al.Superhydrophilic graphene oxide@electrospun cellulose nanofiber hybrid membrane for high-efficiency oil/water separation[J].Carbohydrate Polymers,2017,175:216-222.
[2] Xiao L L,De X S,Sheng C,et al.Freely switchable super-hydrophobicity and super-hydrophilicity of sponge-like poly(vinylidene fluoride)porous fibers for highly efficient oil/water separation[J].Journal of Hazardous Materials,2021,416:125926.
[3] Zheng F W,Yi W,Liang L D,et al.PDA controllably-modified Janus membranes with high-permeability for oil/water separation[J].Composites Communications,2023,40:101574.
[4] Rosalam S.An overview of recent progress in nanofiber membranes for oily wastewater treatment[J].Nanomaterials,2022,12:2919.
[5] 赵晓燕,黄晨,刘远.水过滤用膜材料的制备及其性能研究进展[J].应用化工,2020,49(3):781-787;791.
[6] Chun X D,Ze H W,Gao Y L,et al.One-step electrospinning PVDF/PVP-TiO2 hydrophilic nanofiber membrane with strong oil-water separation and anti-fouling property[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2021,624:126790.
[7] Dong W,Jun J Z,Qing X W,et al.Hierarchical composite membrane with multiscale roughness structures for water-in-oil emulsion separation[J].Applied Surface Science,2021,566:150666.
[8] Haitao M,Tong X,Ming Y G,et al.An oil-contamination-resistant PVP/PAN electrospinning membrane for high-efficient oil-water mixture and emulsion separation[J].Journal of Applied Polymer Science,2020,138:50043.
[9] Hui Z,Dong Z,Lan Y J.PAN/PVA composite nanofibrous membranes for separating oil-in-water emulsion[J].Journal of Polymer Research,2022,29:108.
[10] Da C Z,Xiao Y W,Jing J W.Green electrospun poly(vinyl alcohol)/silicon dioxide nanofibrous membrane coated with polydopamine in the presence of strong oxidant for effective separation of surfactant-stabilized oil-in-water emulsion[J].Surface and Coatings Technology,2023,460:129421.
[11] Hao D Z,Ya L H,Yan B Z,et al.Mussel-inspired fabrication of PDA@PAN electrospun nanofibrous membrane for oil-in-water emulsion separation[J].Nanomaterials,2021,11:3434.
[12] Ji Q L,Mei L C,Xiu W H,et al.Electrospun hierarchically channeled polyacrylonitrile nanofibrous membrane for wastewater recovery[J].Journal of Cleaner Production,2022,361:132167.
[13] Lu W,Shan S D,Xue W L,et al.A ternary system oleophilic-hydrophobic membrane prepared by electrospinning for efficient gravity-driven oil-water separation[J].Sn Applied Sciences,2019,1:797.
[14] 张娇娇,左晓飞,覃小红,等.聚多巴胺涂覆改性聚丙烯腈纳米纤维膜及其油水分离性能[J].东华大学学报(自然科学版),2018,44(1):10-17;32.
[15] Diego W,Adriano D S,Cristiane C.Modification of PVDF hydrophobic microfiltration membrane with a layer of electrospun fibers of PVP-co-PMMA:increased fouling resistance[J].Chemical Engineering Research and Design,2021,171:268-276.
[16] Chong D L,Qing X L.Oxidant-induced high-efficient mussel-inspired modification on PVDF membrane with superhydrophilicity and underwater superoleophobicity charac-teristics for oil/water separation[J].ACS Applied Materials & Interfaces,2017,9:1-11.
[17] Qi X,Hao C,Qiong T,et al.Waste PET derived Janus fibrous membrane for efficient oil/water emulsions separation[J].Journal of Environmental Chemical Engineering,2022,10:108459.
[18] Meng H T,Liang H O,Xu T,et al.Crosslinked electrospinning membranes with contamination resistant properties for highly efficient oil-water separation[J].Journal of Polymer Research,2021,28:347.
[19] Ahmadi A,Qanati O,Dorraji M S,et al.Investigation of antifouling performance a novel nanofibrous S-PVDF/PVDF and S-PVDF/PVDF/GO membranes against negatively charged oily foulants[J].Journal of Membrane Science,2017,536:86-97.
[20] Jing W,Li A H,Kang K Y,et al.Polydopamine nanocluster decorated electrospun nanofibrous membrane for separation of oil/water emulsions[J].Journal of Membrane Science,2018,547:156-162.
基金资助
2019年自治区创新环境(人才、基地)建设专项(自然科学基金)联合基金(2019D01C077)
PDF