以3-氨丙基三乙氧基硅烷(APTES)为硅源前驱体制备了含氨有机硅膜,并与1,2-双(三乙氧基硅基)乙烷(BTESE)制备的有机硅膜进行对比,研究了湿度对两种有机硅膜进行CO2分离性能的影响。结果表明:APTES膜随湿度的增加CO2渗透率降低幅度不明显,而BTESE膜由于水蒸汽在膜孔中发生毛细凝聚现象,从而造成CO2渗透率降低幅度较大;相比于APTES膜,BTESE膜的CO2/N2选择性仅增加了0.43倍,APTES膜的CO2/N2选择性增加了0.91倍。这是由于APTES支链上的氨基基团在水的存在下能促进CO2的传输,说明含氨有机硅膜在湿气条件下对CO2的分离具有良好的应用前景。
Amino-containing organosilicon membranes were prepared with 3-aminopropyltriethoxysilane (APTES) as the silicon precursors,and compared with the organosilicon membranes prepared from 1,2-bis(triethoxysilyl) ethane (BTESE).The effect of humidity on the CO2 separation performance of the two organosilicon membranes was investigated.The results showed that the CO2 permeability of APTES membrane was a slight decrease with the increase of humidity,while the CO2 permeability of BTESE membrane decreased significantly with the increase of humidity due to the capillary condensation of water vapor in the membrane pores.The CO2/N2 selectivity of BTESE membrane only increased by 0.43 times of that under dry conditions,whereas APTES membrane increased by 0.91 times.This was due to the fact that the amino group on the APTES branched chain could promote CO2 transport in the presence of water,indicating that amino-containing organosilicon membranes had a good application prospect for CO2 separation under humid condition.
[1] Ren X,Tsuru T.Organosilica-based membranes in gas and liquid-phase separation[J].Membranes-Basel,2019,9(9):107.
[2] Vatanpour V,Pasaoglu M E,Barzegar H,et al.Cellulose acetate in fabrication of polymeric membranes:a review[J].Chemosphere,2022,295:133914.
[3] Kanehashi S,Scholes C A.Perspective of mixed matrix membranes for carbon capture[J].Frontiers of Chemical Science and Engineering,2020,14(3):460-469.
[4] Casado-Coterillo C,Garea A,Irabien Á.Effect of water and organic pollutant in CO2/CH4 separation using hydrophilic and hydrophobic composite membranes[J].Membranes,2020,10(12):103390.
[5] Moriyama N,Nagasawa H,Kanezashi M,et al.Bis(triethoxysilyl)ethane (BTESE)-derived silica membranes:pore formation mechanism and gas permeation properties[J].Journal of Sol-Gel Science and Technology,2018,86(1):63-72.
[6] Castricum H L,Qureshi H F,Nijmeijer A,et al.Hybrid silica membranes with enhanced hydrogen and CO2 separation properties[J].Journal of Membrane Science,2015,488:121-128.
[7] Ren X,Nishimoto K,Kanezashi M,et al.CO2 permeation through hybrid organosilica membranes in the presence of water vapor[J].Industrial & Engineering Chemistry Research,2014,53(14):6113-6120.
[8] Fuoco A,Satilmis B,Uyar T,et al.Comparison of pure and mixed gas permeation of the highly fluorinated polymer of intrinsic microporosity PIM-2 under dry and humid conditions:experiment and modelling[J].Journal of Membrane Science,2020,594:117460.
[9] 罗居杰,张萌,郭瑞乾,等.氨基功能化聚醚砜气体分离膜对CO2/N2、CO2/CH4分离性能研究[J].化工新型材料,2016,44(3):95-107.
[10] Yu L,Kanezashi M,Nagasawa H,et al.Role of amine type in CO2 separation performance within amine functionalized silica/organosilica membranes:a review[J].Applied Sciences,2018,8(7):1032.
[11] Araki S,Kiyohara Y,Imasaka S,et al.Preparation and pervaporation properties of silica-zirconia membranes[J].Desalination,2011,266(1):46-50.
[12] Chai S,Du H,Zhao Y,et al.Fabrication of highly selective organosilica membrane for gas separation by mixing bis(triethoxysilyl)ethane with methyltriethoxysilane[J].Separation and Purification Technology,2019,222:162-167.
[13] Nakahiro K,Yu L,Nagasawa H,et al.Pore structure controllability and CO2 permeation properties of silica-derived membranes with a dual-network structure[J].Industrial & Engineering Chemistry Research,2021,60(23):8527-8537.
[14] Yang J,Fan W,Bell C M.Effect of calcination atmosphere on microstructure and H2/CO2 separation of palladium-doped silica membranes[J].Separation and Purification Technology,2019,210:659-69.
[15] Meng L,Kanezashi M,Wang J,et al.Permeation properties of BTESE-TEOS organosilica membranes and application to O2/SO2 gas separation[J].Journal of Membrane Science,2015,496:211-218.
[16] Miyamoto M,Takayama A,Uemiya S,et al.Gas permeation properties of amine loaded mesoporous silica membranes for CO2 separation[J].Desalination and Water Treatment,2011,34:266-271.
[17] Song H,Wei Y,Wang C,et al.Tuning sol size to optimize organosilica membranes for gas separation[J].Chinese Journal of Chemical Engineering,2018,26(1):53-59.
[18] Anggarini U,Yu L,Nagasawa H,et al.Metal-induced aminosilica rigidity improves highly permeable microporous membranes via different types of pendant Precursors[J].ACS Applied Materials Interfaces,2022,14(37):42692-42704.
[19] Anggarini U,Yu L,Nagasawa H,et al.Structural transformation of the nickel coordination-induced subnanoporosity of aminosilica membranes for methanol-selective,high-flux pervaporation[J].Journal of Membrane Science,2022,656:120613.
[20] Kanezashi M,Yoneda Y,Nagasawa H,et al.Gas permeation properties for organosilica membranes with different Si/C ratios and evaluation of microporous structures[J].AIChE Journal,2017,63(10):4491-4498.
[21] Yu L,Kanezashi M,Nagasawa H,et al.Fabrication and CO2 permeation properties of amine-silica membranes using a variety of amine types[J].Journal of Membrane Science,2017,541:447-456.
[22] Mietner B J,Fröba M,Valiullin R.Water transport in periodic mesoporous organosilica materials[J].The Journal of Physical Chemistry C,2018,122(24):12673-12680.
[23] 马益平,严浩军,王琼京,等.混合配体法合成氨基MIL-101(Cr)及其二氧化碳吸附和除湿性能[J].南京大学学报(自然科学),2019,55(5):840-849.
[24] Ito F,Nishiyama Y,Duan S,et al.Examination of selection and combination of water-absorbing agent to blend with polyvinyl alcohol (PVA) in preparing CO2-separation membrane with high-performance[J].Macromolecular Research,2020,28(4):365-372.
[25] 张中正,汤娇娣,苏伟,等.水对胺改性吸附剂吸附分离CO2的影响[J].化学工程,2013,41(2):23-28.
基金资助
江苏省自然科学基金项目(BK20200982);常州市科技计划项目(CZ20220033)
PDF