分别采用等离子体和紫外固化法对玉米秸秆纤维素-腐植酸基吸水树脂(CS-HA-PAA)进行改性,通过傅里叶变换红外光谱仪和扫描电子显微镜对改性吸水树脂的结构和形貌进行表征,考察了改性吸水树脂的耐盐性、耐酸碱性、保水性、反复吸液性等性能。结果表明:改性后CS-HA-PAA亲水基团增多,表面粗糙且产生孔洞结构,有利于提高吸水性能;采用最佳工艺条件制备的等离子体改性CS-HA-PAA和紫外固化改性CS-HA-PAA的吸水率分别可达1053.2g/g、869.44g/g,NaCl质量浓度为9g/L时最高吸盐水率分别为181.03g/g、151.49g/g,等离子体改性CS-HA-PAA的吸水、耐盐性能优于紫外固化法改性CS-HA-PAA。
Corn straw cellulose-humic acid-based water-absorbent resin (CS-HA-PAA) was modified by plasma and ultraviolet curing methods,respectively.The structure and morphology of the modified water-absorbent resin were characterized by Fourier transform infrared spectrometry (FT-IR) and scanning electron microscopy (SEM).The properties of the modified water-absorbent resin,such as salt resistance,acid and alkali resistance,water retention,and repetitive liquid absorption,were investigated.The results showed that the modified CS-HA-PAA had more hydrophilic groups,rough surface and pore structure,which was conducive to the improvement of the water absorption performance.The water absorption rates of the plasma-modified CS-HA-PAA and the ultraviolet-cured modified CS-HA-PAA prepared under the optimal process conditions were up to 1053.2g/g and 869.44g/g,respectively,and the highest salt water absorption rates were 181.03g/g and 151.49g/g,respectively,at the mass concentration of NaCl of 9g/L.The results indicated that the water absorption and salt resistance of the plasma-modified CS-HA-PAA were better than those of the ultraviolet-cured CS-HA-PAA.
[1] 尹洪清,赵梅梅,刘峰,等.高吸水性树脂合成方法研究进展[J].胶体与聚合物,2021,39(4):190-193.
[2] 邬一凡.高吸水性树脂研究进展及发展趋势[J].化工新型材料,2019,47(5):23-26;31.
[3] Zhang M,Yang P,Lan G H,et al.High crosslinked sodium carboxyl methylstarch-g-poly (acrylic acid-co-acrylamide) resin for heavy metal adsorption:its characteristics and mechanisms[J].Environmental Science and Pollution Research,2020,27(31):38617-38630.
[4] Zhang W X,Chen J,Tao J H,et al.Effects of super absorbent polymers and gibberellin on germination and growth of alfalfa[J].Legume Research,2020,43(6):800-804.
[5] Fan J,Chen Q,Li J,et al.Preparation and dewatering property of two sludge conditioners chitosan/AM/AA and chitosan/AM/AA/DMDAAC[J].Journal of Polymers and the Environment,2019,27(2):275-285.
[6] 邵江涛,范振忠,刘庆旺,等.高分子吸水剂的合成及其在油田中的应用研究进展[J].石油化工,2022,51(5):601-607.
[7] Hai J J,Bai B,Ding C X,et al.Removal of oil from water surface by novel composite NSM-g-P(MMA-co-BA) super oil-absorption resin[J].Polymer Composites,2018,39(4):1051-1063.
[8] 林立.耐盐抗压高吸水性树脂的制备及其应用[D].福州:福州大学,2018.
[9] 张燕,来水利,穆冰硕,等.CMC/NC复合高吸水性树脂的制备及其性能[J].陕西科技大学学报,2021,39(6):90-96.
[10] 惠璠,高乐,郭战英,等.添加风化煤腐植酸对丙烯酸吸水树脂性能的影响[J].功能材料,2020,51(2):2144-2149.
[11] 潘滋涵.天然纤维素基高吸水性树脂研究进展[J].山东化工,2019,48(12):52-53.
[12] 王晨,师晓鹏,魏浩钦,等.玉米秸秆基高吸水性树脂的试验研究[J].河南农业大学学报,2020,54(1):81-86.
[13] 穆林聪,郭雅妮,卢亚楠,等.一种改性腐植酸基吸附树脂的制备及表征[J].西安工程大学学报,2019,33(4):413-419;432.
[14] 姜洁,郭雅妮,徐斗均,等.腐植酸基高吸水性树脂的制备及其性能[J].西安工程大学学报,2019,33(1):51-56;94.
[15] 杨雪,刘瑞松,于丽华,等.腐殖酸改性聚丙烯酸高吸水性树脂制备及性能研究[J].安徽化工,2021,47(5):33-36.
[16] Zhou H,Su Y,Chen X G,et al.Plasma modification of substrate with poly (methylhydrosiloxane) for enhancing the interfacial stability of PDMS/PAN composite membrane[J].Journal of Membrane Science,2016,520(12):779-789.
[17] 贾景霞,刘建平,薛俊杰.紫外光固化树脂的研究进展[J].辽宁化工,2018,47(5):434-436.
[18] 朱宁,孙明明,张斌,等.一种紫外光固化树脂的合成及性能表征[J].化学与黏合,2018,40(5):339-342.
[19] 王浩宇,郭雅妮,梁兰兰,等.农矿业废弃物复合制备玉米秸秆-腐植酸基吸水树脂[J].化工新型材料,2022,50(12):209-214.
[20] 袁金玲,梁家仪,陈丽娟,等.辐射聚合法制备高吸水树脂研究进展[J].化工新型材料,2020,48(S1):28-31.
基金资助
陕西省科技厅重点研发计划(2024GX-YBXM-334);西安市碑林区应用技术研发储备工程项目(GX2308)
PDF