采用可生物降解的聚乳酸(PLA)制备多孔纳米纤维膜用于油水分离,以多孔PLA为壳、聚氨酯(PU)为核借助同轴静电纺丝制备PLA/PU同轴纳米纤维油水分离膜,改善力学性能,提高复用性。通过扫描电镜(SEM)、X射线衍射(XRD)、红外光谱(FT-IR)等手段考察膜材的形貌特征、力学性能和复用性。结果表明:PU的引入提升了纳米纤维膜的力学性能,PLA/PU14%浓度的同轴多孔纳米纤维膜可使油水分离效率达到94.12%;经油水分离后的纯PLA纳米纤维膜的力学性能与分离效率出现下降,而纯PU与PLA/PU纳米纤维膜却有所提高,使用5次后的PLA/PU14%分离效率最好,达到了94.72%。PLA/PU同轴纳米纤维膜有效提高了油水分离的分离效率和膜材的可复用性,具有良好的应用前景。
Biodegradable polylactic acid (PLA) was used to prepare porous nanofiber membrane for oil-water separation.PLA/PU coaxial nanofiber oil-water separation membranes were prepared by coaxial electrospinning with porous PLA as the shell and polyurethane (PU) as the core,improving mechanical properties and reusability.By using SEM,XRD,FT-IR,etc.,the morphological characteristics,mechanical properties,and reusability of the membrane materials were investigated.The results showed that the introduction of PU improved the mechanical properties of the nanofiber membranes,and the coaxial porous nanofiber membrane with PLA/PU14% concentration could make the oil-water separation efficiency reach 94.12%.After conducting oil-water separation experiments,the mechanical properties and separation efficiency of pure PLA nanofiber membranes decreased,while those of pure PU and PLA/PU nanofiber membranes improved.After five uses,the best separation efficiency of PLA/PU 14% was 94.72%.The PLA/PU coaxial nanofiber membrane effectively improved the separation efficiency of oil-water separation and the reusability of the membrane materials,showing promising application prospects.
[1] Cao Y,Liu N,Zhang W,et al.One-step coating toward multifunctional applications:oil/water mixtures and emulsions separation and contaminants adsorption[J].ACS Applied Materials & Interfaces,2016,8(5):3333-3339.
[2] Liu D,He L,Lei W,et al.Multifunctional polymer/porous boron nitride nanosheet membranes for superior trapping emulsified oils and organic molecules[J].Advanced Materials Interfaces,2015,2(12):1500228.
[3] 陈超奇,李兆双,黄钦,等.油水分离膜材料制备及其应用研究进展[J].化工新型材料,2023,51(9):1-7.
[4] Ravanchi M T,Kaghazchi T,Kargari A.Application of membrane separation processes in petrochemical industry:a review[J].Desalination,2009,235(1-3):199-244.
[5] 王长青,张西华,宁朋歌,等.含油废水处理工艺研究进展及展望[J].化工进展,2020,40(1):451-462.
[6] 李璐璐,梁欣宇,森巴特·特尼斯别克,等.油水分离中静电纺纳米纤维膜应用的现状与展望[J].现代化工,2019,39(6):59-64.
[7] Guo J W,Wang C F,Chen S H,et al.Highly efficient self-cleaning of heavy polyelectrolyte coated electrospun polyacrylonitrile nanofibrous membrane for separation of oil/water emulsions with intermittent pressure[J].Separation and Purification Technology,2020,234:116106-116106.
[8] 杨思民,王建强,刘富.油水分离膜研究进展[J].膜科学与技术,2019,39(3):10.
[9] Wen Z,Wang S,Bao Z,et al.Preparation and oil absorption performance of polyacrylonitrile fiber oil absorption material[J].Water,Air,& Soil Pollution,2020,231:1-13.
[10] Wu L,Zhang J,Li B,et al.Mechanical-and oil-durable superhydrophobic polyester materials for selective oil absorption and oil/water separation[J].Journal of Colloid and Interface Science,2014,413:112-117.
[11] Wei Q F,Mather R R,Fotheringham A F,et al.Evaluation of nonwoven polypropylene oil sorbents in marine oil-spill recovery[J].Marine Pollution Bulletin,2003,46(6):780-783.
[12] Zhou Z,Liu L,Yuan W.A superhydrophobic poly (lactic acid) electrospun nanofibrous membrane surface-functionalized with TiO2 nanoparticles and methyltrichlorosilane for oil/water separation and dye adsorption[J].New Journal of Chemistry,2019,43(39):15823-15831.
[13] Kang Y L,Zhang J,Wu G,et al.Full-biobased nanofiber membranes toward decontamination of wastewater containing multiple pollutants[J].ACS Sustainable Chemistry & Engineering,2018,6(9):11783-11792.
[14] 李亮,裴斐斐,刘淑萍,等.聚乳酸纳米纤维基载药敷料的制备与表征[J].纺织学报,2022,43(11):1-8.
[15] 李亮,刘淑萍,裴斐斐,等.载中药聚乳酸多孔纳米纤维医用敷料[J].材料导报,2024,38(10):1-14.
[16] 刘强飞,黎璠,杨吉震,等.多孔聚乳酸纳米纤维膜的吸油性能研究[J].棉纺织技术,2021,49(10):4.
[17] Guo J,Wang T,Yan Z,et al.Preparation and evaluation of dual drug-loaded nanofiber membranes based on coaxial electrostatic spinning technology[J].International Journal of Pharmaceutics,2022,629:122410.
[18] Chen K,Hu H,Zeng Y,et al.Recent advances in electrospun nanofibers for wound dressing[J].European Polymer Journal,2022,178:111490.
[19] Wang L,Deng N,Ju J,et al.A novel core-shell structured poly-m-phenyleneisophthalamide @polyvinylidene fluoride nanofiber membrane for lithium ion batteries with high-safety and stable electrochemical performance[J].Electrochimica Acta,2019,300:263-273.
[20] Wang C,Yan K W,Lin Y D,et al.Biodegradable core/shell fibers by coaxial electrospinning:processing,fiber characterization,and its application in sustained drug release[J].Macromolecules,2010,43(15):6389-6397.
[21] Radhamani A V,Shareef K M,Rao M S R.ZnO@ MnO2 core-shell nanofiber cathodes for high performance asymmetric supercapacitors[J].ACS Applied Materials & Interfaces,2016,8(44):30531-30542.
[22] Shao W,He J,Sang F,et al.Coaxial electrospun aligned tussah silk fibroin nanostructured fiber scaffolds embedded with hydroxyapatite-tussah silk fibroin nanoparticles for bone tissue engineering[J].Materials Science and Engineering:C,2016,58:342-351.
[23] Wang Y,Zhou G,Yan Y,et al.Construction of natural loofah/poly (vinylidene fluoride) core-shell electrospun nanofibers via a controllable Janus nozzle for switchable oil-water separation[J].ACS Applied Materials & Interfaces,2020,12(46):51917-51926.
[24] Yang X,Pu Y,Zhang Y,et al.Multifunctional composite membrane based on BaTiO3@PU/PSA nanofibers for high-efficiency PM2.5 removal[J].Journal of Hazardous Materials,2020,391:122254.
[25] Liu B,Ying X,Zhang Y,et al.Polyurethane nanofiber membranes immobilized with Bacillus altitudinis LS-1 for bioremediation of diesel-contaminated wastewater[J].Process Safety and Environmental Protection,2023,180:883-892.
[26] Xia S,Pang Y,Yu Z,et al.Superhydrophobic DTES-SEP/SiO2@PDMS coated sponge and stainless steel mesh for efficient oil and water separation[J].Journal of Environmental Chemical Engineering,2023,11(5):110605.
[27] 张成成,刘让同,李淑静,等.聚左旋乳酸非溶剂挥发诱导成孔机制与纳米多孔纤维膜制备[J].纺织学报,2023,44(10):16-23.
[28] Kumar M,Ulbricht M.Novel ultrafiltration membranes with adjustable charge density based on sulfonated poly (arylene ether sulfone) block copolymers and their tunable protein separation performance[J].Polymer,2014,55(1):354-365.
基金资助
国家重点研发计划资助项目(2017YFB0309100)
PDF