通过在聚乙烯醇(PVA)网络中引入动态亚胺键,成功制备了具有pH响应性能的形状记忆水凝胶,并对其微观形貌、力学性能和形状记忆性能进行了研究。结果表明,浸泡pH=10的NaOH溶液后,水凝胶内部交联度提高,网络更加致密,其最高拉伸强度和最大断裂伸长率分别可达(68±0.5)kPa和200%,这表明在碱性条件下,可在聚合物网络中成功引入可逆的动态亚胺键。此外,水凝胶具有形状记忆性能,并且随着壳聚糖季铵盐(HACC)与氧化硫酸软骨素(OCS)质量比的降低,水凝胶的形状固定率与形状恢复率都呈上升趋势,且最优形状固定率和形状恢复率均在80%以上。该pH响应型形状记忆水凝胶,凭借高含水率、良好的生物相容性和独特的刺激响应性等特点,在信息储存与解密、航空航天等领域具有良好的应用前景。
Shape memory hydrogel materials with pH-responsive properties were successfully prepared by introducing dynamic imine bonds into the polyvinyl alcohol (PVA) networks,and their microscopic morphology,mechanical properties and shape memory properties were investigated.The results showed that after immersing in sodium hydroxide solution with pH=10,the internal cross-linking degree increased,the network was more dense,and its maximum tensile strength and maximum elongation at break could reach 68 (±0.5)kPa and 200%,respectively,which indicated that dynamic reversible imine bonds were successfully introduced into the polymer network under alkaline conditions.In addition,the hydrogel had shape memory properties,and the shape fixation rate and shape recovery rate tended to increase with the decrease of the mass ratio of chitosan quaternary ammonium salt (HACC) to oxidized chondroitin sulfate (OCS).The optimal shape fixation rate and shape recovery rate were all above 80%.This pH-responsive shape memory hydrogel,with its high water content,good biocompatibility and unique stimulus responsiveness,has promising applications in the fields of information storage and decryption,and aerospace engineering.
[1] Vazquez-Gonzalez M,Willner I.Stimuli-responsive biomolecule-based hydrogels and their applications[J].Angewandte Chemie International Edition,2020,59(36):15342-15377.
[2] Shintake J,Cacucciolo V,Floreano D,et al.Soft robotic grippers[J].Advanced materials,2018,30(29):1707035.
[3] Li T Q,Li Y,Wang X H,et al.Thermally and near-infrared light-induced shape memory polymers capable of healing mechanical damage and fatigued shape memory function[J].ACS Appl Mater Interfaces,2019,11(9):9470-9477.
[4] Shang J J,Le X X,Zhang J W,et al.Trends in polymeric shape memory hydrogels and hydrogel actuators[J].Polymer Chemistry,2019,10(9):1036-1055.
[5] Hua L Q,Zhao C Z,Guan X,et al.Cold-induced shape memory hydrogels for strong and programmable artificial muscles[J].Science China Materials,2022,65(8):2274-2280.
[6] Kolesov I,Dolynchuk O,Jehnichen D,et al.Changes of crystal structure and morphology during two-way shape-memory cycles in cross-linked linear and short-chain branched polyethylenes[J].Macromolecules,2015,48(13):4438-4450.
[7] Hu Q Q,Zhang Y C,Wang T,et al.pH responsive strong polyion complex shape memory hydrogel with spontaneous shape changing and information encryption[J].Macromolecular Rapid Communications,2021,42(9):2000747.
[8] Lu L X,Tian T,Wu S S,et al.A pH-induced self-healable shape memory hydrogel with metal-coordination cross-links[J].Polymer Chemistry,2019,10(15):1920-1929.
[9] Liu Y J,Lv H B,Lan X,et al.Review of electro-active shape-memory polymer composite[J].Composites Science and Technology,2009,69(13):2064-2068.
[10] Zeng C J,Liu L W,Bian W F,et al.4D printed electro-induced continuous carbon fiber reinforced shape memory polymer composites with excellent bending resistance[J].Composites Part B:Engineering,2020,194:108034.
[11] Zhao Q,Qi H J,Xie T.Recent progress in shape memory polymer:new behavior,enabling materials,and mechanistic understanding[J].Progress in Polymer Science,2015,49:79-120.
[12] Lu W,Le X X,Zhang J W,et al.Supramolecular shape memory hydrogels:a new bridge between stimuli-responsive polymers and supramolecular chemistry[J].Chemical Society Reviews,2017,46(5):1284-1294.
[13] Xia D Y,Wang P,Ji X F,et al.Functional supramolecular polymeric networks:the marriage of covalent polymers and macrocycle-based host-guest interactions[J].Chemical Reviews,2020,120(13):6070-6123.
[14] Belowich M E,Stoddart J F.Dynamic imine chemistry[J].Chemical Society Reviews,2012,41(6):2003-2024.
[15] Chan B Q,Low Z W,Heng S J,et al.Recent advances in shape memory soft materials for biomedical applications[J].ACS Appl Mater Interfaces,2016,8(16):10070-10087.
[16] Korde J M,Kandasubramanian B.Naturally biomimicked smart shape memory hydrogels for biomedical functions[J].Chemical Engineering Journal,2020,379:122430.
[17] Chen Y W,Dai S P,Zhu H,et al.Self-healing hydrogel sensors with multiple shape memory properties for human motion monitoring[J].New Journal of Chemistry,2021,45(1):314-320.
[18] Xiao H,Lu W,Le X X,et al.A multi-responsive hydrogel with a triple shape memory effect based on reversible switches[J].Chemical Communications,2016,52(90):13292-13295.
[19] Miao J T,Ge M Y,Peng S Q,et al.Dynamic Imine bond-based shape memory polymers with permanent shape reconfigurability for 4D printing[J].ACS Appl Mater Interfaces,2019,11(43):40642-40651.
[20] Li T,Song X B,Weng C M,et al.Self-crosslinking and injectable chondroitin sulfate/pullulan hydrogel for cartilage tissue engineering[J].Applied Materials Today,2018,10:173-183.
[21] Dawlee S,Sugandhi A,Balakrishnan B,et al.Oxidized chondroitin sulfate-cross-linked Gelatin matrixes:a new class of hydrogels[J].Biomacromolecules,2005,6(4):2040-2048.
[22] Zhou L,Fan L,Zhang F M,et al.Hybrid gelatin/oxidized chondroitin sulfate hydrogels incorporating bioactive glass nanoparticles with enhanced mechanical properties,mineralization,and osteogenic differentiation[J].Bioactive Materials,2021,6(3):890-904.
[23] Andreica B I,Cheng X J,Marin L.Quaternary ammonium salts of chitosan.A critical overview on the synthesis and properties generated by quaternization[J].European Polymer Journal,2020,139:110016.
基金资助
山西省自然科学基金(2021-0302123158);山西浙大新材料与化工研究院(2022SX-TD023)
PDF