矿物阻燃填料是传统防火涂料的重要组成部分。基于中国知网数据库、Web of Science数据库和国家知识产权局数据库,检索了1990年至2022年有机防火涂料中矿物阻燃填料研究的文献,介绍了矿物阻燃填料的研究应用情况。文献检索及专利分析表明:进入21世纪以后,国内外对矿物阻燃填料在有机防火涂料中的应用研究关注度呈增长趋势,研究热点主要集中在钢结构防火涂料、阻燃机理、表面改性、热稳定性等方面,矿物阻燃填料研究种类从以氢氧化铝、氢氧化镁为主逐渐转为以氢氧化铝、氢氧化镁、可膨胀石墨和黏土矿物为主,种类多样化、成分多样化和结构复杂化是近年来有机防火涂料中矿物阻燃填料的研究趋势,矿物阻燃填料的纳米化、协同阻燃以及表面改性等技术将不断得到发展。
Mineral flame retardant fillers are important components of traditional fireproof coatings.Based on the databases of CNKI,Web of Science and China National Intellectual Property Administration,this paper retrieved the research literatures on mineral flame retardant fillers in organic fireproof coatings from 1990 to 2022,and introduced the research application of mineral flame retardant fillers.The analysis showed that,after entering the 21st century,domestic and foreign attention to the application of mineral flame retardant fillers in organic fireproof coatings was increasing,and the research hotspots mainly focused on steel structure fireproof coatings,flame retardant mechanism,surface modification and thermal stability.The types of mineral flame retardant fillers had gradually shifted from aluminum hydroxide and magnesium hydroxide to aluminum hydroxide,magnesium hydroxide,expandable graphite and clays.Diversification and structural complexity were the research trends of mineral flame retardant fillers in organic fireproof coatings in recent years,and technologies such as nanometer,synergistic flame retardant and surface modification of mineral flame retardant fillers would continue to be developed.
[1] 赵文君.不同防火涂料的应用探究[J].冶金与材料,2022,42(4):187-189.
[2] 李博,卢明超.防火涂料阻燃/抑烟技术的研究现状及进展[J].化工新型材料,2018,46(4):227-229.
[3] Yasir M,Ahmad F,Yusoff P S M M,et al.Latest trends for structural steel protection by using intumescent fire protective coatings:a review[J].Surface Engineering,2019(2):1-30.
[4] 王强.橡塑填料市场分析[J].化工管理,2017(14):135-136;139.
[5] 路林,赵正任,付丽,等.钢结构水性膨胀型防火涂料性能优化方法[J].涂料工业,2022,52(9):70-76.
[6] Abulyazied D E,Ene A.An investigative study on the progress of nanoclay-reinforced polymers:preparation,properties,and applications:a review[J].Polymers,2021,13(24):4401.
[7] 王飞跃,刘辉,颜龙.钨尾矿填料在膨胀型防火涂料中的协效作用[J].中国安全科学学报,2021,31(10):46-53.
[8] 于全蕾,李旭光,周莲洁,等.水性超薄膨胀型防火涂料的制备与性能研究[J].涂料工业,2021,51(4):30-35.
[9] Bourbigot S,Duquesne S.Fire retardant polymers:recent developments and opportunities[J].Journal of Materials Che-mistry,2007,17(22):2283.
[10] Pilarska A A,Klapiszewski L,Jesionowski T,et al.Recent development in the synthesis,modification and application of Mg(OH)2 and MgO:a review[J].Powder Technology,2017,319:373-407.
[11] Liu P.Polymer modified clay minerals:a review[J].Applied Clay Science,2007,38(1/2):64-76.
[12] Wu Q,Deng H,Bai H,et al.Facile and eco-friendly functiona-lization of basalt fiber with polyelectrolyte complex toward excellent interfacial adhesion of epoxy composites[J].Composites Part A:Applied Science and Manufacturing,2022,156:106889.
[13] 王余莲,印万忠,李闯,等.碱式碳酸镁的表面有机改性及性能表征[J].硅酸盐学报,2020,48(1):120-127.
[14] Zielecka M,Rabajczyk A,Cygańczuk K,et al.Silicone resin-based intumescent paints[J].Materials,2020,13(21):4785.
[15] Uddin M,Alabbad M,Li L,et al.Novel micronized mica mo-dified casein-aluminum hydroxide as fire retardant coatings for wood products[J].Coatings,2022,12(5):673.
[16] Xu W,Fan L,Qin Z,et al. Silica-coated metal-organic framework-β-FeOOH hybrid for improving the flame retardant and smoke suppressive properties of epoxy resin[J]. Plastics Rubber and Composites,2021,50:1-10.
[17] Ozyhar T,Tschannen C,Hilty F,et al.Mineral-based composition with deliquescent salt as flame retardant for melamine-urea-formaldehyde (MUF)-bonded wood composites[J].Wood Science and Technology,2021,55(5):1529-1530.
[18] Zhang G,Li S L,Zhang X Y,et al.Synthesis and properties of a fire-retardant coating based on intercalated expandable graphite-modified cellulose for steel structures[J].Journal of Building Engineering,2022,51:104270.
[19] Chen X X,Liu J H,Kurniawan A,et al.Inclusion of organic species in exfoliated montmorillonite nanolayers towards hierarchical functional inorganic-organic nanostructures[J].Soft Matter,2021,17(43):9819-9841.
[20] Xu Z,Xie X,Yan L,et al.Fabrication of organophosphate-grafted kaolinite and its effect on the fire-resistant and anti-ageing properties of amino transparent fire-retardant coatings[J].Polymer Degradation and Stability,2021,188:109589.
[21] Li S,Wang J,Wen S,et al.Synergistic effect of aluminum diethylphosphinate/sodium stearate modified vermiculite on flame retardant and smoke suppression properties of amino coatings[J].RSC Adv,2021,11(54):34059-34070.
[22] 王清海,王秀娟,方健君,等.颜填料在水性膨胀型防火涂料中的应用研究[J].涂层与防护,2021,42(11):29-32;37.
[23] Xu Z,Liu D,Yan L,et al.Synergistic effect of sepiolite and polyphosphate ester on the fire protection and smoke suppression properties of an amino transparent fire-retardant coating[J].Progress in Organic Coatings,2020,141:105572.
[24] Mazela B,Batis Ta A,Grzekowiak W.Expandable graphite as a fire retardant for cellulosic materials—a review[J].Forests,2020,11(7):755.
[25] Ng Y H,Dasari A,Qian L J,et al.Intumescent fire-retardant acrylic coatings:effects of additive loading ratio and scale of testing[J].Progress in Organic Coatings,2021,150:105985.
基金资助
国家国际科技合作专项(2014DFA52900)
PDF