以多官能环氧树脂TDE-85、E-51环氧树脂、活性稀释剂和固化剂为主要原材料,制备了一种中高温固化的环氧树脂。采用非等温差示扫描量热(DSC)法研究树脂固化行为,利用Kissinger和Crane方程求得该树脂的固化反应动力学参数,并使用T-β外推法得到该树脂的最佳固化温度,从而建立了该环氧树脂体系的固化动力学模型。在此基础上,以该树脂为基体,T800碳纤维为增强相,采用缠绕模压工艺制得复合材料单向板及NOL环。利用扫描电镜(SEM)观察复合材料的微观形貌,通过动态机械热分析仪发现T800碳纤维/EP复合材料的储能模量随温度的升高而降低,损耗因子峰值对应的玻璃化转变温度为137℃。复合材料单向板在室温下的拉伸强度为2784MPa,NOL环在350℃下的拉伸强度为1349MPa,其拉伸强度随温度的增加而减小。
Using multifunctional epoxy resin TDE-85,E-51 epoxy resin,reactive diluent and curing agent as the main raw materials,a medium-high temperature curing epoxy resin was prepared.The curing behavior of the resin was studied by non-isothermal differential scanning calorimetry (DSC) method,the kinetic parameters of the curing reaction of the resin were obtained by the Kissinger and Crane equations,and the optimal curing temperature of the resin was obtained by T-β extrapolation.Thus,the curing kinetic model of the epoxy resin system was established.On this basis,using the resin as the matrix and T800 carbon fiber as the reinforcing phase,the composite material unidirectional plate and the NOL ring were prepared by the winding molding process.The microscopic morphology of the composite was observed by SEM.The dynamic mechanical thermal analysis revealed that the storage modulus of the T800 carbon fiber/EP composite decreased with the increase of temperature,and the glass transition temperature corresponding to the peak loss factor was 137℃.The tensile strength of the composite unidirectional plate at room temperature was 2748MPa,and the tensile strength of the NOL ring at 350℃ was 1349MPa,and its tensile strength decreased with the increase of temperature.
[1] Yetgin H,Veziroglu S,Aktas O C,et al.Enhancing thermal conductivity of epoxy with a binary filler system of h-BN platelets and Al2O3 nanoparticles[J].International Journal of Adhesion and Adhesives,2019,98:102540.
[2] 白云起,薛丽梅,刘云夫.环氧树脂的改性研究进展[J].化学与粘合,2007,29(4):289-292.
[3] 熊佳,黄英,王琦洁,等.环氧树脂增韧研究进展[J].塑料,2004,33(3):58-61.
[4] Qing Y,Zhou W,Jia S,et al.Effect of heat treatment on the microwave electromagnetic properties of carbonyl iron/epoxy-silicone resin coatings[J].Journal of Materials Science and Technology:English Edition,2010,26(11):1011-1015.
[5] 吴晓青,李嘉禄,康庄,等.TDE-85环氧树脂固化动力学的DSC和DMA研究[J].固体火箭技术,2007,30(3):264-268.
[6] 宁保江,宁荣昌,马小琴,等.E-51环氧/TA-70体系固化反应动力学研究[J].粘接,2008,29(2):22-24.
[7] He S J,Shi K Y,Wo H,et al.Studies on the properties of epoxy resins modified with chain-extended ureas[J].Polymeric Materials Science & Engineering,2003,17(1):69-72.
[8] Cai P Z,Zhang H,Zhao D L,et al.Effect of diluent on mechanical properties of DDM/E-51 epoxy resin system[J].Polymer Materials Science & Engineering,2010,26(11):75-77,82.
[9] Li Z H,Lu J T,Chou J N.Curing mechanism of TDE-85/E-51 resin modified by polyurethane[J].Polymeric Materials Science and Engineering,2009,25(11):30-32.
[10] 郭建君,孙晋良,任慕苏,等.TDE-85/AG-80环氧树脂基复合材料微观形貌与力学性能分析[J].玻璃钢/复合材料,2010,7(1):49-52.
[11] 段国晨,赵景丽,赵伟超.E51环氧树脂基碳纤维复合材料力学性能研究[J].粘接,2018,39(8):42-44.
[12] 王芬,刘亮,刘府,等.T800级碳纤维及复合材料性能对比研究[J].高科技纤维与应用,2020,45(5):8-14.
[13] 李伟东,张金栋,刘刚,等.国产T800碳纤维/双马来酰亚胺复合材料的界面及力学性能[J].复合材料学报,2016,33(7):1484-1491.
[14] 欧秋仁,嵇培军,肖军,等.T800碳纤维/9518氰酸酯复合材料的性能[J].复合材料学报,2018,47(8):125-131.
PDF