在空气气氛、吸收剂量分别为60kGy、120kGy、180kGy、240kGy、300kGy条件下,采用电子束对乙烯-四氟乙烯共聚物(ETFE)薄膜进行辐照,研究辐照后ETFE薄膜的结构变化。结果表明:辐照引起ETFE薄膜的表面氧化,在1758cm-1和1850cm-1处出现新的红外特征峰。随吸收剂量的增加,其结晶度发生变化,在120kGy吸收剂量下,ETFE薄膜的最大结晶度为38%。随吸收剂量增加,辐照后ETFE的内部分子链断裂程度增加,其分子链变短,分子量变小。当吸收剂量为300kGy时,ETFE薄膜的长周期和回转半径最小分别为15.41nm和7.55nm。辐照后ETFE薄膜的微观结构变化对于其在离子交换膜和滤膜应用具有重要的学术意义和工程价值。
The ethylene-tetrafluoroethylene copolymer (ETFE) films were irradiated by the electron beam under air atmosphere and absorbed doses of 60kGy,120kGy,180kGy,240kGy and 300kGy,respectively,and the structural changes of ETFE after irradiation were investigated.The results showed that irradiation induced surface oxidation of ETFE films,and new infrared characteristic peaks appeared at 1758cm-1 and 1850cm-1.The crystallinity changed with the absorbed dose increasing,and the maximum crystallinity of the ETFE film was 38% at 120 kGy absorbed dose.With the increase of absorbed dose,the internal molecular chain breakage of ETFE increased,the molecular chain became shorter,and the molecular weight became smaller.When the absorbed dose was 300kGy,the minimum long period and rotation radius of ETFE film were 15.41nm and 7.55nm,respectively.The microstructure changes of ETFE films after irradiation had an important academic significance and engineering value for their application in ion exchange and filter films.
[1] 曹影.乙烯、四氟乙烯多元共聚物的应用与研究[D].济南:济南大学,2019.
[2] Lamnatou C,Moreno A,Chemisana D,et al.Ethylene tetrafluoroethylene(ETFE) material:critical issues and applications with emphasis on buildings[J].Renewable and Sustainable Energy Reviews,2018,82:2186-2201.
[3] Gowa T,Shiotsu T,Urakawa T.Study on depth profile of heavy ion irradiation effects in poly(tetrafluoroethylerie-co-ethylene)[J].Radiation Physics and Chemistry,2011,80(2):264-267.
[4] 闵峻,乔伟男,翟国富,等.辐照过程对交联乙烯-四氟乙烯绝缘线缆的影响[J].机电元件,2021,41(1):22-28.
[5] Biancollii A,Bsoul S,Douglin J,et al.High-performance radiation grafted anion-exchange membranes for fuel cell applications:effects of irradiation conditions on ETFE-based membranes properties[J].Journal of Membrance Science,2022,641:12.
[6] Cui Z,Drioli E,Lee Y.Recent progress in fluoropolymers for membranes[J].Progress in Polymer Science,2014,39(1):164-198.
[7] 孟庆文,王京辉,胡帅捷,等.乙烯-四氟乙烯共聚物的制备、加工及应用进展[J].有机氟工业,2021(1):28-31.
[8] Zen H,Ribeiro G,Geraldes A,et al.Effect of radiation induced crosslinking and degradation of ETFE films[J].Radiation Physics and Chemistry,2013,84:136-139.
[9] Zhang X,Chen F,Su Z,et al.Effect of radiation-induced cross-linking on thermal aging properties of ethylene-tetrafluoroethylene for aircraft cable materials[J].Materials,2021,14(2):257.
[10] 李建喜,单永东,张聪,等.电子束辐照乙烯-四氟乙烯共聚物的化学稳定性[J].辐射研究与辐射工艺学报,2015,33(6):25-30.
[11] Nasef M,Saidi H,Dahlan K.Electron beam irradiation effects on ethylene-tetrafluoroethylene copolymer films[J].Radiation Physics and Chemistry,2003,68(5):875-883.
[12] Nasef M,Saidi H,Dahlan K.Electron irradiation effects on partially fluorinated polymer films:structure-property relationships[J].Nuclear Instruments and Methods in Physics Research,2003,201(4):604-614.
[13] Zhang Y,Ma H,Zhang X,et al.Irradiation,thermal and mechanical properties of ethylene-tetrafluoroethylene copolymer for use in wings of unmanned aerial vehicle[J].Iranian Polymer Journal,2021,30:393-399.
[14] 张强,季珎琰,张帆,等.三种市售医用一次性防护服的γ射线辐照后效应[J].辐射研究与辐射工艺学报,2021,39(5):44-51.
[15] 宋敏彦,陈嘉言,沈青,等.悬浮改性PTFE原料及其制品的热分析[J].有机氟工业,2021(4):6-12.
[16] 陈晓勇.乙烯-四氟乙烯共聚物的辐照交联及辐照敏化剂研究[J].化学推进剂与高分子材料,2011,9(3):19-24.
[17] Kuzuya M,Niwa J,Noguchi T.Electron spin resonance study on plasma-induced surface radicals of ethylene-tetrafluoroethylene copolymer[J].Polymer Journal,1995,27(3):251-255.
[18] Ignatieva L,Mashchenko V,Zverev G,et al.Study of the manufactured copolymers of ethylene with tetrafluoroethylene[J].Journal of Fluorine Chemistry,2020,231:109460.
[19] 杨春明,洪春霞,周平,等.同步辐射小角X射线散射及其在材料研究中的应用[J].中国材料进展,2021,40(2):112-119.
[20] Liu Y,MA J Y,Liu W H,et al.Free radical decay and micro-structure evolution of PVDF membranes in situ irradiated by synchrotron radiation X-ray[J].Polymer Testing,2022,108:107507.
[21] Zhang X,Schneider K,Liu G,et al.Deformation-mediated superstructures and cavitation of poly(l-lactide):in-situ small-angle X-ray scattering study[J].Polymer,2012,53(2):648-656.
[22] Hyunjung C,Sik J K,Jaegeun L,et al.Estimation of degree of polymerization of poly-acrylonitrile-grafted carbon nanotubes using guinier plot of small angle X-ray scattering[J].Nanotechnology,2018,29(27):275708.
基金资助
国防科技173计划技术领域基金项目(2021-JCJQ-JJ-0128);广西科技大学大学生创新创业训练计划项目(S202110594013)
PDF