以氟代烷氧基聚磷腈(TOAPF)/三元乙丙橡胶(EPDM)作为并用基础胶,通过复配、硫化制备出TOAPF改性EPDM包覆层,并研究了包覆层的硫化特性、力学性能、热失重特性、耐烧蚀性能及抗硝化甘油迁移性能。硫化特性分析结果表明,随着EPDM包覆层配方中TOAPF用量的增大,焦烧时间与正硫化时间基本保持不变,最低转矩、最高转矩以及转矩差逐渐降低;力学性能研究结果表明,随着EPDM包覆层配方中TOAPF用量的增大,包覆层的拉伸强度逐渐降低,延伸率逐渐提高;热失重特性和耐烧蚀性能研究结果表明,通过TOAPF/EPDM并用的途径可以提高EPDM包覆层的耐热性和耐烧蚀性。由于TOAPF具有优良的耐化学腐蚀和耐油性,在EPDM包覆层中引入TOAPF可以提高包覆层的抗硝化甘油迁移能力。
Poly(fluoroalkoxyphosphazenes)(TOAPF) modified EPDM coating layer was prepared by compounding and vulcanization using TOAPF/EPDM as matrix materials.The vulcanization characteristics,mechanical properties,thermogravimetric characteristics,ablation resistance and nitroglycerin migration resistance of the coating layer were studied.The results of vulcanization characteristic analysis showed that with the increase of TOAPF content in EPDM coating layer formulation,the scorch time and optimum cure time remained basically unchanged,whereas the minimum torque,maximum torque and torque difference decreased gradually.The results of mechanical analysis indicated that with the increase of TOAPF content in EPDM coating layer formulation,the tensile strength gradually decreased and the elongation gradually increased.The results of thermogravimetric characteristics and ablation resistance demonstrated that the heat-resistance and ablation resistance of EPDM coating layer could be improved by the combination of TOAPF/EPDM.Because TOAPF had excellent chemical corrosion resistance and oil resistance,the introduction of TOAPF into EPDM coating layer improved the anti nitroglycerin migration abilities of the EPDM coating layer.
[1] 张以河,孙维钧,孙隆丞,等.高分子材料在固体火箭包覆层中的应用[J].工程塑料应用,1994,22(5):37-41.
[2] 侯林法,张春森,周学刚,等.复合固体推进剂[M].北京:宇航出版社,1994.
[3] 路向辉,杨士山,刘晨,等.填料对三元乙丙橡胶包覆层性能影响研究[J].化工新型材料,2013,41(10):131-132.
[4] 李鹏,李军强,刘晨,等.三元乙丙包覆层流变硫化性能及注射成型工艺研究[J].化工新型材料,2020,48(1):232-236.
[5] 李冬,陈竚,任黎,等.三元乙丙基固体推进剂包覆层拉伸性能影响因素研究[J].化工新型材料,2011,39(9):98-99.
[6] Gordon S.Solid propellant with inhibitor layer in rocket motor:US,3991565[P].1976-11-16.
[7] Wasserman B.Powder barrier bonding technique:US,4009231[P].1977-02-22.
[8] 陈宝喜,李建军,苗彩琴.丁腈橡胶对三元乙丙橡胶包覆剂抗硝化甘油迁移性能的影响[J].火炸药学报,2004,27(1):56-58.
[9] 贡长生.聚磷腈的合成化学[J].弹性体,1989(3):57-63.
[10] 金日光,张腾,蔡晴.无机功能高分子聚磷腈的研究现状及展望[R].中国(青岛)材料科技周(中国机械工程学会),2004:218-229.
[11] 李冬,王吉贵.聚磷腈材料及其在固体火箭发动机绝热层中的应用探讨[J].化学推进剂与高分子材料,2008,6(2):20-23.
[12] 王建中,王志锋,曹继平,等.芳氧基聚磷腈绝热包覆材料的性能表征[J].固体火箭技术,2015,38(2):278-280.
[13] Chang S C,Rouge B.Rocket motor insulation using phophonitrilic elastomeric compositions:US,5024860[P].1991-06-18.
[14] Kyker G S,Antkowiak T A,Halasa A F.Process for conversion of elastomeric phosphazene:US,3970533[P].1976-07-20.
[15] Cheng T C.Phosphonitrilic polymers with curability by sulfur accelerated cures or radiation cures:US,4116785[P].1978-09-26.
[16] Zhang Teng,Cai Qing,Wu Dezhen,et al.Phosphazene cyclo-matrix network polymers:some aspects of synthesis,characterization and flame-retardant mechanism of polymers[J].Journal of Applied Polymer Science,2005,95(4):880-889.
[17] Harry Allcock R,Gayann McDonnel S,Geoffrey Riding H,et al.Influence of different organic side groups on the thermal behavior of polyphazenes:random chain cleavage,depolyme-rization,and pyrolytic cross-linking[J].Chem Mater,1990,2(4):425-432.
[18] Bowmer T N,Haddon R C,Hicks,et al.Effect of substituents on the thermal transitions and degradation behavior of poly[bis(R-phenoxy)phosphazenes][J].Macromolecules,1991,24(17):4827-4833.
PDF