甘蔗渣是甘蔗经榨糖后的残渣物,是一种良好的生物质残渣原料,为使甘蔗渣利用价值最大化,探索生物质液化新方法至关重要。本研究通过用正辛醇、聚乙二醇等试剂液化甘蔗渣,利用红外(FT-IR)、凝胶渗透色谱(GPC)、羟基值测定等分析方法研究其液化产物特性。研究发现,在液比为4∶1,催化剂用量9%,液化温度180℃,液化时间150min时,得到的正辛醇液化残渣率最低仅为9%,优于传统多元醇液化。通过正交试验发现,液化过程中各因素对性能的影响顺序为:液化时间>液比>液化温度>催化剂用量。加入聚乙二醇混合液化后,在液化试剂比为5∶5时残渣率达到11.2%,优于传统混合多元醇液化;FT-IR分析发现,混合液化产物可作为一种聚醚多元醇使用;GPC分析发现,液化产物是一种高分子量产物;羟基值测定发现,聚乙二醇的加入大大提高了液化产物羟基值,为聚氨酯的合成原料提供了一种新的来源。
Bagasse is the residue of sugarcane after sugar extraction.It is a versatile biomass residue material.In order to maximize the utilization value of bagasse,it is very important to explore new methods of biomass liquefaction.In this study,n-octanol and polyethylene glycol as well as other reagents were used to liquefy bagasse,and the performances of the liquefied products were characterized by using of FT-IR,GPC and hydroxyl value measurement.It was found that when the liquid ratio was 4∶1,the amount of catalyst was 9%,the liquefaction temperature was 180℃ and the liquefaction time was 150min,the n-octanol liquefaction residue rate obtained was as low as only 9%,which was better than the conventional polyol liquefaction.Through the orthogonal experiment,it was found that the order of the factors affecting the performance in the liquefaction process was:liquefaction time>liquid ratio>liquefaction temperature>catalyst dosage.The polyethylene glycol was used to reinforce the liquefaction process and results,and when the ratio of n-octanol and polyethylene glycol was set at 5∶5,the residue rate reached 11.2%,which was better than the conventional hybrid polyol liquefaction.FT-IR analysis demonstrated that the hybrid liquefaction product could be used as a potential polyether polyol for commercial application.In addition,GPC analysis confirmed that the liquefied product was a high molecular weight product.Hydroxyl value measurements revealed that the hydroxyl value of the liquefied product was significantly increased with the addition of polyethylene glycol,which provided a new route for the synthesis of polyurethane.
[1] 崔丽虹,魏晓奕,常刚,等.甘蔗渣的材料化研究进展[J].热带农业科学,2017,37(9):83-87.
[2] 刘洋,洪亚楠,姚艳丽,等.中国甘蔗渣综合利用现状分析[J].热带农业科学,2017,37(2):91-95.
[3] Shaikh T.全球聚氨酯市场[J].中国涂料,2020,35(4):74-75.
[4] Demirbas M F,Balat M.Recent advances on the production and utilization trends of bio-fuels:A global perspective[J].Energy Conversion and Management,2006,47(15-16):2371-2381.
[5] 王允圃,李积华,刘玉环,等.甘蔗渣综合利用技术的最新进展[J].中国农学通报,2010,26(16):370-375.
[6] Yu F,Le Z,Chen P,et al.Atmospheric pressure liquefaction of dried distillers grains (DDG) and making polyurethane foams from liquefied DDG[J].Appl Biochem Biotechnol,2008,148(1-3):235-243.
[7] Zhang B,Huang H J,Ramaswamy S.Reaction kinetics of the hydrothermal treatment of lignin[J].Appl Biochem Biotechnol,2008,147(1-3):119-131.
[8] Chen H,Zhang Y,Xie S.Selective liquefaction of wheat straw in phenol and its fractionation[J].Appl Biochem Biotechnol,2012,167(2):250-258.
[9] 文旭,彭思瑶,蒋文伟,等.关于蔗渣纤维素提取方法的比较研究[J].化工新型材料,2017,45(9):250-252.
[10] Zhang T,Zhou Y,Liu D,et al.Qualitative analysis of products formed during the acid catalyzed liquefaction of bagasse in ethylene glycol[J].Bioresour Technol,2007,98(7):1454-1459.
[11] Zhang H,Luo J,Li Y,et al.Acid-catalyzed liquefaction of bagasse in the presence of polyhydric alcohol[J].Appl Biochem Biotechnol,2013,170(7):1780-1791.
[12] 程发,王东华,魏玉萍,等.苯甲基化木材溶液代替聚醚多元醇使用的研究[J].高分子学报,2002(3):349-353.
[13] Zhang H,Pang H,Shi J,et al.Investigation of liquefied wood residues based on cellulose,hemicellulose,and lignin[J].Journal of Applied Polymer Science,2012,123(2):850-856.
[14] Zhang H,Ding F,Luo C,et al.Liquefaction and characterization of acid hydrolysis residue of corncob in polyhydric alcohols[J].Industrial Crops and Products,2012,39:47-51.
[15] 秦颖,王强强.聚氨酯材料的发展现状[J].中国建材科技,2017,26(1):39-41.
[16] Yan Y,Pang H,Yang X,et al.Preparation and characterization of water-blown polyurethane foams from liquefied cornstalk polyol[J].Journal of Applied Polymer Science,2008,110(2):1099-1111.
[17] Shin H J,Kim C J,Kim S B.Kinetic study of recycled newspaper liquefaction in polyol solvent[J].Biotechnology and Bioprocess Engineering,2009,14(3):349-353.
[18] Jasiukaitytė E,Kunaver M,Strlič M.Cellulose liquefaction in acidified ethylene glycol[J].Cellulose,2009,16(3):393-405.
[19] 崔晓晓,何林韩,安珍,等.沙柳多元醇液化产物流变性能的研究[J].林业工程学报,2020,5(2):90-96.
[20] 钟强,李绪宾,陈爽,等.稻壳液化产物用于聚氨酯胶黏剂的制备与性能[J].化工进展,2016,35(3):780-786.
[21] 卢婷婷,房桂干,沈葵忠,等.竹材废料多元醇液化的工艺研究[J].化工新型材料,2014,v.42;No.505(10):97-101.
[22] 张婷,周玉杰,张建安,等.木质纤维原料各组分温和液化行为[J].清华大学学报(自然科学版),2006(12):2011-2014.
[23] 庞浩,柳雨生,廖兵,等.甘蔗渣多元醇制备聚氨酯硬泡的研究[J].林产化学与工业,2006(2):57-60.
[24] 邹献武,杨智,秦特夫.木材正辛醇液化产物的红外光谱分析[J].光谱学与光谱分析,2009,29(6):1545-1548.
[25] 魏超.甘蔗渣催化液化制备聚醚多元醇及其应用[D].长春:长春工业大学,2021.
[26] 戈进杰,吴睿,邓葆力,等.基于甘蔗渣的生物降解材料研究(Ⅰ)甘蔗渣的液化反应和聚醚酯多元醇的制备[J].高分子材料科学与工程,2003(2):194-198.
[27] Kobayashi M,Asano T,Kajiyama M,et al.Analysis on residue formation during wood liquefaction with polyhydric alcohol[J].Journal of Wood Science,2004,50(5):407-414.
基金资助
云南省基础研究计划项目(202101AS070008);云南省“兴滇英才支持计划”——青年人才,高等学校学科创新引智计划资助(D21027)
PDF