从分子结构设计出发,以苯硼酸(PBA)与羟基封端的聚二甲基硅氧烷(PDMS-OH)为原料,通过缩聚反应制备了一种新型剪切增稠胶(PPBS)。通过傅里叶变换红外光谱仪和热重分析仪对材料的水解性和热稳定性进行表征,同时利用旋转流变仪对PPBS的线性粘弹区域、能量耗散能力及粘弹性进行研究。结果表明:PPBS具有更为优异的耐水解性和热稳定性,其最快分解温度和完全分解温度分别在466℃和568℃左右;通过Lissajous曲线中应力-应变曲线所包含的面积发现PPBS的能量耗散性能更优异;通过频率扫描发现其储能模量随着外界激励的增加增大5个数量级达到0.64MPa,材料表现出典型的剪切硬化性能,并且具有更为优异的相对剪切增稠效应。
Starting from molecular structure design,a novel shear thickening gel (PPBS) was prepared by polycondensation reaction using phenylboronic acid (PBA) and hydroxyl-terminated polydimethylsiloxane (PDMS-OH) as raw materials.The hydrolysis and thermal stability of the material were characterized by FT-IR and TG.At the same time,a rotational rheometer was used to study the linear viscoelastic region,energy dissipation capacity and viscoelastic properties of PPBS.The results showed that PPBS had better hydrolysis resistance and thermal stability,and its fastest decomposition temperature and complete decomposition temperature were about 466℃ and 568℃,respectively.The energy dissipation performance of PPBS was found to be more excellent by the area contained in the stress-strain curve of the Lissajous curve.The frequency scan revealed that the energy storage modulus increased by 5 orders of magnitude to 0.64MPa with the increase of external excitation,and the material exhibited typical shear hardening performance and a more excellent relative shear thickening effect.
[1] Tang M,Wang W,Xu D,et al.Synthesis of structure-controlled polyborosiloxanes and investigation on their viscoelastic response to molecular mass of polydimethylsiloxane triggered by both chemical and physical interactions[J].Industrial & Engineering Chemistry Research,2016,55(49):12582-12589.
[2] Mitrofanov L A,Sidorovich Y A,Karlin A V,et al.The question of molecular interaction in polyborondimethylsiloxanes (PBDMS)[J].Polymer Science USSR,1969,11(4):882-888.
[3] Seetapan N,Fuongfuchat A,Sirikittikul D,et al.Unimodal and bimodal networks of physically crosslinked polyborodimethylsiloxane:viscoelastic and equibiaxial extension behaviors[J].Journal of Polymer Research,2013,20(7):183-191.
[4] Wang Y,Wang S,Xu C,et al.Dynamic behavior of magnetically responsive shear-stiffening gel under high strain rate[J].Composites Science and Technology,2016,127:169-176.
[5] Wang Y,Wang S,Xu C,et al.Dynamic behavior of magnetically responsive shear-stiffening gel under high strain rate[J].Composites Science and Technology,2016,127:169-176.
[6] He Q,Cao S,Wang Y,et al.Impact resistance of shear thickening fluid/Kevlar composite treated with shear-stiffening gel[J].Composites Part A:Applied Science and Manufacturing,2018,106:82-90.
[7] Wang S,Xuan S,Wang Y,et al.Stretchable polyurethane sponge scaffold strengthened shear stiffening polymer and its enhanced safeguarding performance[J].ACS Applied Materials & Interfaces,2016,8(7):4946-4954.
[8] Liu Z,Picken S J,Besseling N A M.Polyborosiloxanes (PBSs),synthetic kinetics,and characterization[J].Macromolecules,2014,47(14):4531-4537.
[9] 周超,王博,徐昆,等.新型冲击防护微凝胶的合成及应用性能研究[J].功能材料,2013(12):1745-1749.
[10] 邓裕坤,梁学称,裴小鹏,等.柔性主链的支化结构对冲击硬化材料性能的影响[J].应用化学,2019,36(10):1155-1164.
[11] 邓裕坤,秦湘阁,徐昆,等.加入新型扩链剂IPDI的冲击硬化材料合成与性能研究[J].化工新型材料,2016,44(2):126-128.
[12] 王胜.多功能剪切变硬胶复合材料的研制与性能研究[D].合肥:中国科学技术大学,2017.
[13] 徐伟强,蒋年新,周正发,等.耐热羟基聚苯硼硅氧烷的制备及表征[J].弹性体,2019,29(2):18-23.
[14] 展红卫,曹瑾.聚二苯基硅硼氧烷的结构及性质[J].华东理工大学学报,1995,21(6):756-761。
[15] 冯仁军.聚硼硅氧烷的合成及热稳定性分析[D].济南:山东大学,2020.
[16] 吴艳金,吴明军,李美江.聚硼硅氧烷的制备及应用研究进展[J].高分子通报,2012(2):94-98.
[17] Jiang W,Gong X,Wang S,et al.Strain rate-induced phase transitions in an impact-hardening polymer composite[J].Applied Physics Letters,2014,104(12):121915.
[18] Hyun K,Wilhelm M,Klein C O,et al.A review of nonlinear oscillatory shear tests:analysis and application of large amplitude oscillatory shear (LAOS)[J].Progress in Polymer Science,2011,36(12):1697-1753.
[19] Kamkar M,Aliabadian E,Shayesteh Zeraati A,et al.Application of nonlinear rheology to assess the effect of secondary nanofiller on network structure of hybrid polymer nanocomposites[J].AIP Publishing LLC,2018,30(2):23102.
[20] Ewoldt R H,Hosoi A E,Mckinley G H.New measures for characterizing nonlinear viscoelasticity in large amplitude oscillatory shear[J].Journal of Rheology,2008,52(6):1427-1458.
[21] 许阳光.新型磁敏智能软材料(磁流变塑性体)的制备,表征及机理研究[D].合肥:中国科学技术大学,2014.
[22] 袁芳,王胜,桑敏,等.磁性剪切增稠复合材料的制备及其磁力耦合特性研究[J].中国科学:物理学力学天文学,2018,48(9):205-214.
基金资助
镇江市重点研发计划-产业前瞻与共性关键技术(2021009)
PDF