通过简便、经济的方法合成了MWCNTs/ZIF-67复合材料,并运用SEM、TEM、XRD、XPS等技术手段对该复合材料进行了表征。为了评估MWCNTs/ZIF-67催化剂的催化活性,在NaBH4存在下进行了对硝基苯酚(4-NP)的还原实验。结果表明,MWCNTs/ZIF-67催化剂具有很好的催化性能,在6min内对4-NP的催化效率高达99.82%,表观速率系数达到0.4973min-1。此外,该材料可以通过磁铁从水溶液中收集,便于回收和再利用。且经过5次循环后,复合材料的催化活性仍很高,表明该复合材料有较好的稳定性,可以作为去除环境污染物的新型催化材料。
In this paper,MWCNTs/ZIF-67 composite material was synthesized by a simple and economical method,and characterized by SEM,TEM、XRD,XPS and other technical means.In order to evaluate the catalytic activity of the MWCNTs/ZIF-67 catalyst,the reduction experiment of p-nitrophenol (4-NP) was carried out in the presence of NaBH4.The results showed that the MWCNTs/ZIF-67 catalyst had good catalytic performance with a catalytic efficiency of 99.82% for 4-NP within 6min and an apparent rate coefficient of 0.4973min-1.In addition,the material could be collected from aqueous solution by magnets,which was convenient for recycling and reuse.Moreover,after 5 cycles,the catalytic activity of the composite material was still very high,indicating that the composite material had good stability and could be used as a new type of catalytic material for the removal of environmental pollutants.
[1] Yan Q,Wang X Y,Feng J,et al.Simple fabrication of bimetallic platinum-rhodium alloyed nano-multipods:a highly effective and recyclable catalyst for reduction of 4-nitrophenol and rhodamine B[J].Journal of Colloid and Interface Science,2021,582(PB):701-710.
[2] Maslamani N,Khan S B,Danish E Y,et al.Carboxymethyl cellulose nanocomposite beads as super-efficient catalyst for the reduction of organic and inorganic pollutants[J].International Journal of Biological Macromolecules,2021,167:101-116.
[3] Min Z,Xintai S,Lida M,et al.Promotion effects of halloysite nanotubes on catalytic activity of Co3O4 nanoparticles toward reduction of 4-nitrophenol and organic dyes[J].Journal of Hazardous Materials,2021,403:123870-123870.
[4] Jiangyong L,Jinxing L,Panming J,et al.Intriguing hierarchical Co@NC microflowers in situ assembled by nanoneedles:towards enhanced reduction of nitroaromatic compounds via interfacial synergistic catalysis[J].Journal of Hazardous Materials,2021,403:123987.
[5] 薛梅.钴(镍)基催化剂的前驱体路线制备及催化对硝基苯酚还原性能[D].哈尔滨:东北林业大学,2020.
[6] 孟羽茜.双金属基纳米材料的设计合成及其催化性能的研究[D].黑龙江:哈尔滨师范大学,2020.
[7] 李晓柠.钴基纳米复合材料的制备及其催化还原4-硝基苯酚性能研究[D].马鞍山:安徽工业大学,2019.
[8] 倪美君,赵鹏程,谢轶羲.基于MOF-199/多壁碳纳米管纳米复合材料的对乙酰氨基苯酚电化学传感器[J].分析科学学报,2021(4):515-521.
[9] Gökhan P,Emre C I,Aytekin U,et al.Effect of milling time,MWCNT content,and annealing temperature on microstructure and hardness of Fe/MWCNT nanocomposites synthesized by high-energy ball milling[J].Advanced Powder Technology,2021,32(8):3107-3116.
[10] 孙小惠.弱磁性Co0.85Se纳米片负载碳纳米管作为电催化析氢催化剂[J].催化学报,2021,42(1):235-245.
[11] Guo D J,Cui S K.A composite strategy to prepare high active Pt-WO3/MWCNT catalysts for methanol electro-oxidation[J].Journal of Physics and Chemistry of Solids,2021,159:110293.
[12] Zhao H Y,Wang Y,Zhao L.Magnetic nanocomposites derived from hollow ZIF-67 and core-shell ZIF-67@ZIF-8:synthesis,properties,and adsorption of rhodamine B[J].European Journal of Inorganic Chemistry,2017,2017(35):4110-4116.
[13] Yi A L K,Der L W.Self-assembled magnetic graphene supported ZIF-67 as a recoverable and efficient adsorbent for benzotriazole[J].Chemical Engineering Journal,2016,284:1017-1027.
[14] Li Y,Zhou K,He M,et al.Synthesis of ZIF-8 and ZIF-67 using mixed-base and their dye adsorption[J].Microporous and Mesoporous Materials,2016,234:287-292.
[15] Wang Y,Gao P,Wei Y Y,et al.Silver nanoparticles decorated magnetic polymer composites (Fe3O4@PS@Ag) as highly efficient reusable catalyst for the degradation of 4-nitrophenol and organic dyes[J].Journal of Environmental Management,2021,278(P1):111473.
[16] Gao F,Feng G,Jin Z,et al.Prussian blue-carboxylated MWCNTs/ZIF-67 composite:a new electrochemical sensing platform for paracetamol detection with high sensitivity[J].Nanotechnology,2021,32(8):085501.
[17] Tu N T T,Sy P C,Thien T V,et al.Microwave-assisted synthesis and simultaneous electrochemical determination of dopamine and paracetamol using ZIF-67-modified electrode[J].Journal of Materials Science,2020,67(7):1219-1229.
[18] Zhang D,Cheng K,Shi N,et al.Nickel particles supported on multi-walled carbon nanotubes modified sponge for sodium borohydride electrooxidation[J].Electrochemistry Communications,2013,35:128-130.
[19] Luo S,Sun W,Ke J,et al.A 3D conductive network of porous carbon nanoparticles interconnected with carbon nanotubes as the sulfur host for long cycle life lithium-sulfur batteries[J].Nanoscale,2018,10(47):22601-22611.
[20] Li Y,Xie M,Zhang X,et al.Co-MOF nanosheet array:a high-performance electrochemical sensor for non-enzymatic glucose detection[J].Sensors & Actuators:B Chemical,2019,278:126-132.
[21] Li X,Zeng C,Jiang J,et al.Magnetic cobalt nanoparticles embedded in hierarchically porous nitrogen-doped carbon frameworks for highly efficient and well-recyclable catalysis[J].Journal of Materials Chemistry A,2016,4(19):7476-7482.
[22] Xie Y,Liu B,Li Y,et al.Cu/Cu2O/rGO nanocomposites:solid-state self-reduction synthesis and catalytic activity for p-nitrophenol reduction[J].New Journal of Chemistry,2019,43(30):12118-12125.
[23] Liu Y,Fang Z,Kuai L,et al.One-pot facile synthesis of reusable tremella-like M1@ M2@ M1(OH)2(M1=Co,Ni,M2=Pt/Pd,Pt,Pd and Au) three layers core-shell nanostructures as highly efficient catalysts[J].Nanoscale,2014,6(16):9791-9797.
基金资助
西北民族大学中央高校基本科研业务费专项资金(31920180003,31920190017,31920190018);西北民族大学中央高校基本科研业务费专项资金资助研究生项目(Yxm2019136,Yxm2020119)
PDF