通过高锰酸钾和浓硫酸氧化石墨边缘,加入双氧水与氨水混合溶液进行剥层,得到边缘氧化石墨烯(EGO)。使用乙二胺对EGO进行氨基化改性,得到氨基改性的边缘氧化石墨烯(NEGO)。将NEGO与聚3,4-二氧乙烯噻吩∶聚苯乙烯磺酸(PEDOT∶PSS)水分散液混合,在聚对苯二甲酸乙二醇酯(PET)基膜上涂膜,制备NEGO/PEDOT∶PSS透明热电薄膜。通过傅里叶变换红外光谱仪、显微拉曼成像光谱仪、X射线衍射仪,自制塞贝克系数测试装置、四探针测试仪等对样品进行表征。结果表明制备的NEGO能在PEDOT∶PSS酸性分散液中稳定分散,与PEDOT∶PSS有着强烈的π-π共轭作用,NEGO掺杂量为3%(质量分数)时,热电薄膜的热电效率最高,功率因子达到0.99μW/(m·K2),薄膜透光度大于80%。
The graphite edges were oxidized by potassium permanganate and concentrated sulfuric acid,and then exfoliated by adding a mixed solution of hydrogen peroxide and ammonia to prepare edge graphene oxide (EGO).Next,EGO was modified by ethylenediamine to obtain amino-modified marginal graphene oxide(NEGO).After that,NEGO was mixed with poly 3,4-dioxyethylene thiophene:polystyrene sulfonic acid (PEDOT∶PSS) aqueous dispersion,and coated on a polyethylene terephthalate (PET) base film to prepare NEGO/PEDOT∶PSS composite thermoelectric film.The samples were characterized by Fourier transform infrared spectrometer,Raman spectrometer,X-ray diffractometer,self-made Seebeck coefficient tester and four-probe tester etc.The results showed that the prepared NEGO could be stably dispersed in the PEDOT∶PSS acid dispersion and had a strong π-π conjugation effect with PEDOT∶ PSS.When the NEGO doping amount was 3wt%,the obtained film had the highest thermoelectric efficiency,its power factor reached 0.99μW/(m·K2),and the transmittance of the film was higher than 80%.
[1] Zhang Q,Sun Y,Xu W,et al.Organic thermoelectric materials:emerging green energy materials converting heat to electricity directly and efficiently[J].Adv Mater,2014,26(40):6829-6851.
[2] Dong G H,Zhu Y J.One-step microwave-solvothermal rapid synthesis of Sb doped PbTe/Ag2Te core/shell composite nanocubes[J].Chemical Engineering Journal,2012,193-194:227-233.
[3] Hongzhi W,Yaogang L I,Qinghong Z,et al.Preparation and thermoelectric performance of tellurium nanowires-based thin-film materials[J].Journal of Inorganic Materials,2020,35(9):1034-1040.
[4] He M,Ge J,Lin Z,et al.Thermopower enhancement in conducting polymer nanocomposites via carrier energy scattering at the organic-inorganic semiconductor interface[J].Energy & Environmental Science,2012,5(8):8351.
[5] Jiang F,Liu C,Xu J.The evolution of organic thermoelectric material based on conducting poly(3,4-ethylenedioxythiophene)[J].Chinese Science Bulletin,2017,62(19):2063-2076.
[6] Choongho Yu,Kim S Y,Kim D,et al.Thermoelectric behavior of segregated-network polymer nanocomposites[J].Nano Letters,2008,8(12):4428-4432.
[7] Kim N,Kee S,Lee S H,et al.Highly conductive PEDOT∶ PSS nanofibrils induced by solution-processed crystallization[J].Adv Mater,2014,26(14):2268-2272;2109.
[8] Xiong J,Jiang F,Shi H,et al.Liquid exfoliated graphene as dopant for improving the thermoelectric power factor of conductive PEDOT∶PSS nanofilm with hydrazine treatment[J].ACS Appl Mater Interfaces,2015,7(27):14917-14925.
[9] Wei L,Wu F,Shi D,et al.Spontaneous intercalation of long-chain alkyl ammonium into edge-selectively oxidized graphite to efficiently produce high-quality graphene[J].Sci Rep,2013,3:2636.
[10] Tian S,Sun J,Yang S,et al.Controllable edge oxidation and bubbling exfoliation enable the fabrication of high quality water dispersible graphene[J].Sci Rep,2016,6:34127.
[11] Ramanathan T,Fisher F T,Ruoff R S,et al.Amino-functionalized carbon nanotubes for binding to polymers and biological systems[J].Chem Mater,2005,17:1290-1295.
[12] Ouyang J,Xu Q,Chu C W,et al.On the mechanism of conductivity enhancement in poly(3,4-ethylenedioxythiophene)∶poly(styrene sulfonate) film through solvent treatment[J].Polymer,2004,45(25):8443-8450.
[13] Yoo D,Kim J,Kim J H.Direct synthesis of highly conductive poly(3,4-ethylenedioxythiophene)∶poly(4-styrenesulfonate)(PEDOT∶PSS)/graphene composites and their applications in energy harvesting systems[J].Nano Research,2014,7(5):717-730.
[14] Lee C P,Lai K Y,Lin C A,et al.A paper-based electrode using a graphene dot/PEDOT∶PSS composite for flexible solar cells[J].Nano Energy,2017,36:260-267.
[15] Du F P,Cao N N,Zhang Y F,et al.PEDOT∶PSS/graphene quantum dots films with enhanced thermoelectric properties via strong interfacial interaction and phase separation[J].Sci Rep,2018,8:6441.
PDF