表面活性剂对TiO₂纳米粒子形貌和结晶性的影响

作者信息 +

Effect of surfactant on morphology and crystallinity of TiO₂ nanoparticles

Yang Zhisheng¹, Ke Weifang², Yu Zenan¹, Chen Yan¹, Zhu Hua³

Author information +

文章历史 +

Received		Published
2021-10-18		2023-02-20
Issue Date	Revised Date
2023-03-01	2021-10-18

PDF

摘要

二氧化钛(TiO₂)半导体材料因优异的光电性能在太阳能电池、发光二极管和紫外探测器等光电器件领域得到广泛应用,引入表面活性剂制备的TiO₂纳米粒子具有更好的光电性能。采用低成本的油酸作为表面活性剂,通过溶剂热法在较低的反应温度下得到了具有高结晶性和窄尺寸分布的TiO₂纳米粒子,其粒径分布在10～11nm之间且纳米粒子的形状均一,具有优异的分散性能。热重分析表明500℃时油酸已完全分离,有利于TiO₂纳米粒子在光电器件中的应用。

Abstract

Titanium dioxide (TiO₂) semiconductor materials have been widely applied in the field of optoelectronic devices such as solar cells,light-emitting diodes and UV detectors because of their excellent photoelectric properties.The TiO₂ nanoparticles with surfactant possess better photoelectric properties.Using low-cost oleic acid as surfactant,TiO₂ nanoparticles with high crystallinity and narrow size distribution were prepared by solvothermal method at lower reaction temperature.The particle size distribution was between 10～11nm,the shape of nanoparticles was uniform and the dispersion performance was excellent.The TGA curve showed that oleic acid had been completely separated at 500℃,which was beneficial to the application of TiO₂ nanoparticles in optoelectronic devices.

关键词

TiO₂ / 表面活性剂 / 制备 / 油酸

Key words

TiO₂ / surfactant / preparation / oleic acid

引用本文

引用格式 ▾

表面活性剂对TiO₂纳米粒子形貌和结晶性的影响[J]. 化工新型材料, 2023, 51(2): 184-186 DOI:10.19817/j.cnki.issn1006-3536.2023.02.037

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Ma X C,Dai Y,Yu L,et al.New basic insights into the low hot electron injection efficiency of gold-nanoparticle-photosensitized titanium dioxide[J].ACS Applied Materials & Interfaces,2014,6(15):12388-12394.
[2] Mellott N P,Durucan C,Pantano C G,et al.Commercial and laboratory prepared titanium dioxide thin films for self-cleaning glasses:photocatalytic performance and chemical durability[J].Thin Solid Films,2005,502(1):112-120.
[3] 王传坤,吴正雪,唐颖.钙钛矿太阳能电池中TiO₂材料制备及应用进展[J].化工新型材料,2020,48(1):41-44.
[4] Lewkowicz A,Bogdanowicz R,Bojarski P,et al.The luminescence of 1,8-diazafluoren-9-one/titanium dioxide composite thin films for optical application[J].Materials,2020,13(13):3014.
[5] Skiba M,Vorobyova V,Pasenko O.Surface modification of titanium dioxide with silver nanoparticles for application in photocatalysis[J].Applied Nanoscience,2022,12:1175-1182.
[6] Irwan I,Muzakkar M Z,Umar A A,et al.Effect of hexamethylenetetramine surfactant in morphology and optical properties of TiO₂ nanoparticle for dye-sensitized solar cells[J].Journal of Physics:Conference Series,2021,1899(1):12045.
[7] Alphas Jebasingh J,Stanley R,Manisha Vidyavathy S.Sol-gel preparation of surfactants assisted titania for solar photocata-lysis[J].Materials Letters,2020,279:128460.
[8] Kubiak A,Bielan Z,Bartkowiak A,et al.Synthesis of titanium dioxide via surfactant-assisted microwave method for photocatalytic and dye-sensitized solar cells applications[J].Catalysts,2020,10(5):586-609.
[9] Liu R R,Ji Z J,Wang J,et al.Mesocrystalline TiO₂/sepiolite composites for the effective degradation of methyl orange and methylene blue[J].Frontiers of Materials Science,2018,12:292-303.
[10] Raimondo G,Marzia B,Simona F,et al.Influence of surfactants in improving degradation of polluting dyes photocatalyzed by TiO₂ in aqueous dispersion[J].Journal of Photochemistry and Photobiology A:Chemistry,2021,418:113342.
[11] Gunes S,Marjanovic N,Nedeljkovic J M,et al.Photovoltaic characterization of hybrid solar cells using surface modified TiO₂ nanoparticles and poly(3-hexyl)thiophene[J].Nanotechnology,2008,19:424009.
[12] Boucle J,Chyla S,Shaffer M S P,et al.Hybrid solar cells from a blend of poly(3-hexylthiophene) and ligand-capped TiO₂ nanorods[J].Advanced Functional Materials,2008,18(4):622-633.
[13] Li X L,Peng Q,Yi J X,et al.Near monodisperse TiO₂ nano-particles and nanorods[J].Chemistry-A European Journal,2006,12(8):2383-2391.
[14] Jun Y W,Casula M F,Sim J H,et al.Surfactant-assisted eli-mination of a high energy facet as a means of controlling the shapes of TiO₂ nanocrystals[J].J Am Chem Soc,2003,125:15981-15985.