采用真空辅助成型工艺制备三维浅交弯联Kevlar/EP装甲材料,分别对6种铺层方式及不同含胶量的装甲材料进行弯曲性能测试,并进一步分析材料的弯曲失效机理。结果表明:铺层方式不同时,三维浅交弯联Kevlar/EP装甲材料的弯曲特性曲线类似;纬纱为材料上、下层承载主体时,其弯曲性能明显好于经纱;含胶量在42%～49%范围内时,Kevlar/EP装甲材料的弯曲强度随着含胶量的增加呈现“先增加后下降”的趋势。
Kevlar/EP armor materials using 3D curved shallow-crossing linking weave were prepared by vacuum assisted forming process.The bending properties of armor materials with six lay-up methods and different contents of adhesive were tested respectively and the bending failure mechanism of the materials was further analyzed.The results showed that,when the lay-up methods were different,the bending characteristic curves of Kevlar/EP armor materials using 3D curved shallow-crossing linking weave were similar.The bending performance of weft yarn was obviously better than that of warp yarn when it was the upper and lower bearing body of material.When the rubber content was in the range of 42%～49%,the bending strength of Kevlar/EP armor material exhibited a trend of first increasing and then decreasing with the increase o f the rubber content.
[1] 牛卉,伍洋,李明.国外高功率微波武器发展情况研究[J].飞航导弹,2021(8):12-16.
[2] 朱孟真,陈霞,刘旭,等.战术激光武器反无人机发展现状和关键技术分析[J].红外与激光工程,2021,50(7):188-200.
[3] Bandaru A K,Chavan V V,Ahmad S,et al.Ballistic impact response of Kevlar® reinforced thermoplastic composite armors[J].International Journal of Impact Engineering,2016,89:1-13.
[4] 李志,方圆.武器工业类科技期刊发展现状及思考[J].采写编,2021(4):140-142.
[5] 刘永才.新形势下武器装备发展思考[J].战术导弹技术,2020(4):1-12.
[6] Cheeseman B A,Bogetti T A.Ballistic impact into fabric and compliant composite laminates[J].Composite Structures,2003,61(1):161-173.
[7] Crouch I G.Body armour-new materials,new systems[J].Defence Technology,2019,15(3):241-253.
[8] 曹贺全,张广明,孙素杰,等.装甲车辆防护技术研究现状与发展[J].兵工学报,2012,33(12):1549-1554.
[9] 高原,姚凯.军用车辆装甲防护材料与技术发展的研究[J].机电产品开发与创新,2015,28(2):10-12.
[10] 赵旭东,高兴勇,刘国庆.装甲防护材料抗侵彻性能研究现状[J].包装工程,2017,38(11):117-122.
[11] 马亚运,高晓平.三维正交机织复合材料拉伸性能研究[J].上海纺织科技,2017,45(2):5-7.
[12] 袁玉华,秦志刚.碳纤维纬编针织复合材料弯曲性能研究[J].上海纺织科技,2017,45(9):7-10.
[13] Jia Xiwen,Sun Baozhong,Gu Bohong.Ballistic penetration of conically cylindrical steel projectile into 3D orthogonal woven composite:a finite element study at microstructure level[J].Journal of Composite Materials,2011,45(9):965-987.
[14] Wei Qingsong,Yang Dan,Gu Bohong,et al.Numerical and experimental investigation on 3D angle interlock woven fabric under ballistic impact[J].Composite Structures,2021,266:113778.
[15] 全国纤维增强塑料标准化技术委员会.GB/T 1449—2005纤维增强塑料弯曲性能试验方法[S].北京:中国标准出版社,2005:371-376.
[16] 冯景鹏,余欢,徐志锋,等.叠层穿刺结构C-f/Al复合材料的弯曲性能及失效分析[J].中国有色金属学报,2020,30(11):2597-2604.
[17] 张涛然,晁晓洁,郭丽红,等.材料力学[M].重庆:重庆大学出版社,2018.
[18] 杨甜甜,王岭,邱海鹏,等.三维机织角联锁SiCf/SiC复合材料弯曲性能及损伤机制[J].纺织学报,2020,41(12):73-80.
基金资助
江苏省高校自然科学研究重大项目(18KJA430011);江苏省大学生创新训练项目(202010304101Y);江苏省先进纺织工程技术中心开放基金重大项目(XJFZ/2018/02)
PDF