摘要
以天然丝瓜络为原料,经过高温碳化和棕榈蜡改性,得到改性丝瓜络,利用扫描电子显微镜、傅里叶变换红外光谱仪对改性丝瓜络的结构和形貌进行表征,通过吸油/吸水倍率评价了改性丝瓜络的疏水亲油性能。结果表明:在碳化温度为800℃、碳化时间为1h、棕榈蜡乳液质量浓度为2.5g/L、浸渍时间为10s时制备的改性丝瓜络纤维呈长圆筒形、由多层丝状纤维交织形成网状结构,且具有良好的疏水性和油吸附稳定性。改性丝瓜络作为一种环境友好且性能优良的吸油材料,有望在废水处理和油水分离等领域得到广泛应用。
Abstract
Using natural loofah sponge as raw material,the modified loofah sponge was prepared by combining high temperature carbonization and palm wax modification.The structure and morphology of the modified loofah sponge were characterized by scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR).The hydrophobicity and lipophilicity were evaluated by oil/water absorption rate.When the carbonization temperature,time,palm wax concentration and the impregnation time were 800℃,1h,2.5g/L and 10s,respectively,the obtained loofah sponge fiber was long cylindrical with the network structure formed by interweaving of multi-layer filamentous fibers,and had good hydrophobicity and oil adsorption stability.The modified loofah sponge was an environmentally friendly and excellent oil absorption material,which was expected to be widely used in wastewater treatment and oil-water separation.
关键词
丝瓜络
/
高温碳化
/
棕榈蜡改性
/
吸油性能
Key words
loofah sponge
/
high temperature carbonization
/
palm wax modification
/
oil absorption property
丝瓜络纤维的功能改性及其吸油性能研究[J].
化工新型材料, 2023, 51(1): 285-289 DOI:10.19817/j.cnki.issn1006-3536.2023.01.055
[1] 王耀华.海上溢油的归宿和形态研究[D].大连:大连海事大学,2010.
[2] 孙晓燕,俞莉红,王鑫,等.海面无机吸油材料的研究进展[J].中国陶瓷工业,2020,27(4):24-29.
[3] 杨锟.植物纤维原料改性制备吸油材料的研究[D].南京:南京林业大学,2007.
[4] 王天杰,苏丹,李雪,等.丝瓜络改性方法及其对水中痕量多环芳烃的吸附特征[J].应用化工,2020,49(5):1082-1087.
[5] 李健鹏.源于丝瓜络的巨孔碳及其复合材料的制备与电化学性能[D].哈尔滨:哈尔滨工业大学,2015.
[6] 杨期鑫,俞璐军,董余兵,等.磁功能化多孔生物质炭复合材料的制备及吸波性能[J].新型炭材料,2019,34(5):455-463.
[7] Diwakar S,Rajkumar K.Preparation of super hydrophobic loofah sponge for fast and efficient separation of oil from seawater[J].Materials Today:Proceedings,2018,5(6):14367-14374.
[8] Lin Y L,Yi P,Yu M G,et al.Fabrication and performance of a novel 3D superhydrophobic material based on a loofah sponge from plant[J].Materials Letters,2018,230:219-223.
[9] 毛金浩,刘引烽,杨红,等.丝瓜络的化学改性及其对金属离子的吸附[J].水处理技术,2008,34(7):46-50.
[10] 董姗姗.丝瓜络吸油测试及组成结构分析[J].山东工业技术,2017(5):293-294.
[11] Zhang C F,Yuan B H,Liang Y,et al.Carbon nanofibers enhanced solar steam generation device based on loofah biomass for water purification[J].Materials Chemistry and Physics,2021,258:123998.
[12] Liu L Y,Yang S,Hu H Y,et al.Lightweight and efficient microwave-absorbing materials based on loofah-sponge-derived hierarchically porous carbons[J].ACS Sustainable Chemistry & Engineering,2019,7:1228-1238.
基金资助
江苏省大学生创新创业训练计划项目(2021045Z);中央高校基本科研业务费专项资金(JUSRP41910)