以蔗渣纤维为原料,采用机械活化法合成丁二酸蔗渣纤维素酯。通过扫描电子显微镜、傅里叶变换红外光谱仪、示差扫描量热仪、热重分析仪观察改性前后材料的微观形貌、分子基团、热学性能的变化,通过测定结合酸含量描述反应进行的程度。结果表明:蔗渣纤维在机械活化作用下,细化成细小颗粒,机械力能削弱纤维素分子内或分子间的氢键作用,强化蔗渣纤维与丁二酸酐发生酯化反应;反应后材料的亲水性增强,且更易脱水与解聚;接入的羧基含量随反应时间与催化剂用量的增加先提高后减小,提高温度或增加酯化剂用量有利于反应的进行,当反应时间为2.0h、催化剂用量为4%时,羧基含量高达5.21mmol/g。与传统酯化改性相比,机械活化固相酯化反应条件更加温和,且不需要使用有机溶剂,避免了二次污染。
Succinate bagasse cellulose ester(SABC) was synthesized by mechanical activation(MA) method with bagasse cellulose(BC) as raw material.Scanning electron microscope,fourier transform infrared spectrometer,differential scanning calorimeter and thermogravimetric analyzer were used to observe the changes of micromorphology,molecular groups and thermal properties of the materials before and after modification,and described the degree of reaction by measuring the content of combined acid.Results showed that BC was refined into fine particles under MA,and esterified with SA.Besides,carboxyl group was introduced.The mechanical force could weaken the hydrogen bond within or between the molecules of cellulose and strengthened the reaction.The interaction between the product and the bound water was strengthened,and the side chain connected enhanced the dehydration or depolymerization.When the reaction time or the amount of catalyst was increased,the content of the introduced carboxyl group increased initially and then decreased.While raising temperature or increasing the amount of esterification agent was conducive to the reaction.When the reaction time was 2.0h and the amount of catalyst was 4%,the content of carboxyl group was as high as 5.21mmol/g.Compared with traditional esterification method,the MA solid reaction had more mild conditions without using organic solvents,which can avoid the secondary pollution.
[1] Wang S,Lu A,Zhang L.Recent advances in regenerated cellulose materials[J].Progress in Polymer Science,2016,53:169-206.
[2] Liu C,Tan Z,Li H M,et al.Research progress in cellulose extraction,modification and application[J].Materials Science Forum,2016,852:1194-1200.
[3] 韩宁宁,王训遒,陈琦,等.植物纤维改性方法及其增强复合材料研究进展[J].化工新型材料,2020,48(3):9-13.
[4] 周金平,甘蔚萍,张俐娜.均相体系中纤维素化学改性研究概述[J].中国科学:化学,2012,42(5):591-605.
[5] 姚一军,王鸿儒.纤维素化学改性的研究进展[J].材料导报,2018,32(19):3478-3488.
[6] Suhas,Gupta V K,Carrott P J,et al.Cellulose:a review as natural,modified and activated carbon adsorbent[J].Bioresource Technology,2016,216:1066-1076.
[7] Fan S L,Zhou J R,Zhang Y J,et al.Preparation of sugarcane bagasse succinate/alginate porous gel beads via a self-assembly strategy:improving the structural stability and adsorption efficiency for heavy metal ions[J].Bioresource Technology:2020,306:1-8.
[8] Bendaoud A,Kehrbusch R,Baranov A,et al.Nanostructured cellulose-xyloglucan blends via ionic liquid /water processing[J].Carbohydrate Polymers,2017,168:163-172.
[9] 樊翠珍,霍美霞.纤维素在染料废水处理中的应用[J].化工新型材料,2020,48(S1):150-153.
[10] Gan T,Zhang Y J,Yang M,et al.Synthesis,characterization,and application of a multifunctional cellulose derivative as an environmentally friendly corrosion and scale inhibitor in simulated cooling water systems[J].Industrial & Engineering Chemistry Research,2018,57:10786-10797.
[11] Baláž P,Dutková E.Fine milling in applied mechanochemistry[J].Minerals Engineering,2009,22(7-8):681-694.
[12] 刘洋,洪亚楠,姚艳丽,等.中国甘蔗渣综合利用现状分析[J].热带农业科学,2017,37(2):91-94.
[13] 沈华艳,谢东,刘海露,等.甘蔗渣生物质资源在复合材料领域的研究进展[J].现代化工,2019,39(7):52-55.
[14] Xue J L,Zhao S,Liang R M,et al.A biotechnological process efficiently co-produces two high value-added products,glucose and xylooligosaccharides,from sugarcane bagasse[J].Bioresource Technology,2016,204:130-138.
[15] Yu H,You Y,Lei F,et al.Comparative study of alkaline hydrogen peroxide and organosolv pretreatments of sugarcane bagasse to improve the overall sugar yield[J].Bioresource Technology,2015,187:161-166.
[16] Gan T,Zhang Y J,Su Y,et al.Esterification of bagasse cellulose with metal salts as efficient catalyst in mechanical activation-assisted solid phase reaction system[J].Cellulose,2017,24:5371-5387.
[17] 方桂珍.多元羧酸与纤维素酯化反应中NaH2PO2的催化作用[J].林产化学与工业,2004,24(2):44-47.
[18] Abeer A M,Wahab Z H A,Ibrahim A A,et al.Characterization of microcrystalline cellulose prepared from lignocellulosic materials.part Ⅰ.acid catalyzed hydrolysis[J].Bioresource Technology,2010,101(12):4446-4455.
[19] Dawy M,Shabaka A A,Nada A M A.Molecular structure and dielectric properties of some treated lingnins[J].Polymer Degradation and Stability,1998,62(3):455-462.
[20] Dong C,Qian L Y,Zhao G L,et al.Preparation of antimicrobial cellulose fibers by grafting β-cyclodextrin and inclusion with antibiotics[J].Materials Letters,2014,124(124):181-183.
[21] Garcia P S,Grossmann M V E,Shirai M A,et al.Improving action of citric acid as compatibiliser in starch/polyester blown films[J].Industrial Crops and Products,2014,52(1):305-312.
[22] Shafizadeh F.Introduction to pyrolysis of biomass[J].Journal of Analytical and Applied Pyrolysis,1982,3(4):283-305.
基金资助
国家自然科学基金(201666005和51463003);广西自然科学基金项目(2019GXNSFDA245020);广西环境控制理论与技术重点实验室主任基金项目(桂科能1701K004)
PDF