蒸发苯亚甲基富勒烯1,2-PhCHC60(1)的间二甲苯(m-C8H10)溶液,制备了微米花状结构的自组装膜。高分辨透射电镜(HRTEM)和选取电子衍射(SAED)结果表明该微米花状结构具有清晰的晶格条纹,晶格间距为0.98nm。结合拉曼光谱测试结果,推测微米花状结构中化合物1分子的C60笼为平行排列。核磁氢谱(1H-NMR)结果表明,该微米花状结构是摩尔比为1∶m-C8H10=1∶0.7的溶剂化物。掺杂的间二甲苯分子具有高结晶性,阻碍了化合物1分子的自由旋转与振动,非辐射跃迁减少,因此该微米花状结构薄膜的光致发光(PL)性能显著提高。
The benzenomethylfullerene 1,2-PhCHC60(1) with flower-like hierarchical microstructure was constructed via facile evaporation compound 1 in m-xylene solution.HRTEM and SAED results revealed well-defined lattices with an interplanar spacing of 0.98nm.Combined with the results of Raman spectroscopy,it was speculated that the C60 cage of compound 1 molecule was in parallel arrangement in micro-flower structure.On the basis of 1H-NMR,the assembly was a solvate with the molar radio of 1∶m-C8H10=1∶0.7.It prevented the free rotation and vibration of the molecule of compound 1,due to the doping solvent and highly crystalline,resulting in remarkable enhancement in photoluminescence (PL) of the flower-like microstructure.
[1] Huang Y,Kramer E J,Heeger A J,et al.Bulk heterojunction solar cells:morphology and performance relationships[J].Chemical Reviews,2014,114(14):7006-7043.
[2] Li F,Yager K G,Dawson N M,et al.Stable and controllable polymer/fullerene composite nanofibers through cooperative noncovalent interactions for organic photovoltaics[J].Chemistry of Materials,2014,26(12):3747-3756.
[3] Park S,Seo D,Ryu T I,et al.Enhancement of organic photovoltaic efficiency via nanomorphology control using conjugated polymers incorporating fullerene compatible side-chains[J].Macromolecules,2015,48(2):337-345.
[4] Shrestha R G,Shrestha L K,Khan A H,et al.Demonstration of ultrarapid interfacial formation of 1D fullerene nanorods with photovoltaic properties[J].ACS Applied Materials & Interfaces,2014,6(17):15597-15603.
[5] Wang L,Liu B,Yu S,et al.Highly enhanced luminescence from single-crystalline C60·1m-xylene nanorods[J].Chemistry of Materials,2006,18(17):4190-4194.
[6] Shin H S,Yoon S M,Tang Q,et al.Highly selective synthesis of C60 disks on graphite substrate by a vapor-solid process[J].Angewandte Chemie Interanational Edition,2008,47(4):693-696.
[7] Jeong J,Cho M,Lim Y T,et al.Synthesis and characterization of a photoluminescent nanoparticle based on fullerene-silica hybridization[J].Angewandte Chemie Interanational Edition,2009,121(29):5400-5403.
[8] Wang B,Gao X,Piao G.Controllable preparation of fullerene nanotubes[J].Materials Letter,2014,115:82-84.
[9] Sathish M,Miyazawa K I,Hill J P,et al.Solvent engineering for shape-shifter pure fullerene (C60)[J].Journal of the American Chemical Society,2009,131(18):6372-6373.
[10] Nakanishi T,Ariga K,Michinobu T,et al.Flower-shaped supramolecular assemblies:hierarchical organization of a fullerene bearing long aliphatic chains[J].Small,2007,3(12):2019-2023.
[11] Nakanishi T,Shen Y,Wang J,et al.Superstructures and superhydrophobic property in hierarchical organized architectures of fullerenes bearing long alkyl tails[J].Journal of Materials Chemistry,2010,20(7):1253-1260.
[12] Wang Y.Photophysical properties of fullerenes and fullerene/N,N-diethylaniline charge-transfer complexes[J].The Journal of Physical Chemistry B,1992,96(2):764-767.
[13] Li F F,Yang W W,He G B,et al.Formation of fullerooxazoles from C61HPh3-:the regioselectivity of heteroatom additions[J].The Journal of Organic Chemistry,2009,74(21):8071-8077.
[14] Kuzmany H,Matus M,Burger B,et al.Raman scattering in C60 fullerenes and fullerides[J].Advanced Materials,1994,6(10):731-745.
[15] Lebedkin S,Gromov A,Giesa S,et al.Raman scattering study of C120,a C60 dimer[J].Chemical Physics Letters,1998,285(3):210-215.
[16] Capozzi V,Trovato T,Berger H,et al.Photoluminescence spectra of C60 thin films deposited on different substrates[J].Carbon,1997,35(6):763-766.