Influence of modified expanded graphite on the performance of anticorrosive antistatic coating

Expand
  • 1. College of Chemistry and Chemical Engineering,Qingdao University,Qingdao 266071;
    2. Weihai Innovation Research Institute of Qingdao University,Weihai 264200;
    3. College of Chemistry and Environment Engineering,Baise University,Baise 533000

Received date: 2020-08-04

  Revised date: 2020-10-15

  Online published: 2021-01-27

摘要

环氧树脂水性防腐抗静电涂料已广泛应用于储油罐、输油管道等许多领域。将改性膨胀石墨加入环氧树脂水性防腐抗静电涂料中,制备了高性能防腐抗静电涂料。结果表明:当改性膨胀石墨在涂层中的添加质量为0.5%时,涂层的力学性能没有受到影响,同时涂层的电阻率降至1×108Ω,达到抗静电国家标准要求;涂层的耐腐蚀性能增强,耐3% NaCl溶液浸泡实验显示耐盐腐蚀达到5d;耐10% NaOH溶液达到21d;耐酸性能提高显著。

本文引用格式

赵杰, 刘正堂, 谷正, 李培耀, 李慧, 王宁宋俐凝, 李振旭, 杨丽娜 . 改性膨胀石墨对防腐抗静电涂料性能的影响[J]. 化工新型材料, 2021 , 49(1) : 139 -142 . DOI: 10.19817/j.cnki.issn 1006-3536.2021.01.031

Abstract

Epoxy resin waterborne anticorrosive and antistatic coatings have been widely used in many fields such as oil storage tanks and oil pipelines.The modified expanded graphite was added into epoxy resin waterborne antistatic coating to prepare high performance antistatic coating.The results proved that:when the modification of expanded graphite content in the coating was 0.5%,the mechanics properties of the coating was not affected.At the same time,coating resistivity was lowered to 1×108Ω,met the requirements of antistatic national standards.The corrosion resistance of the coating was enhanced,and its resistance to 3% NaCl solution immersion shown salt resistance extended to 5d.Coating resistance to 10% NaOH solution extended to 21d,acid resistance was improved significantly.

参考文献

[1] 王龙龙,刘竞,夏继军.化工生产中静电产生的原因及危害[J].科技创新导报,2020,17(7):87-88.
[2] 何桂兰,马兴,韩青.浅色油罐内壁导静电防腐涂料的研制[J].中国涂料,2014,29(12):35-38.
[3] 耿艳文.静电在石油产品储运过程中的危害及应对措施[J].化工管理,2019(34):111-112.
[4] 侯波,孙红娟,彭同江,等.低温加热快速制备膨胀石墨(英文)[J].新型炭材料,2020,35(3):262-268.
[5] 陈文亮,滕东晓,马元,那平.膨胀石墨材料的研究进展及其应用综述[J].科技创新导报,2019,16(6):111-114.
[6] 郑宾国,王荣红,刘群,等.膨胀石墨及其复合材料在水处理领域的应用研究[J].化工新型材料,2017,45(6):239-241.
Options
文章导航

/