采用硅烷偶联剂KH550对气相SiO2进行表面改性,制备肥料缓释用改性SiO2/PU复合包衣涂层。探究了改性SiO2含量对树脂性能及肥料缓释性能的影响。结果表明,与添加改性SiO2之前相比,多元醇、多异氰酸酯和改性SiO2混合料黏度增大,复合涂层耐水性提高、拉伸强度增大、断裂伸长率降低,肥料缓释期延长。而且,随着改性SiO2含量的增多,混合料黏度不断增大,涂层吸水率不断减小,断裂伸长率、水接触角基本不变,拉伸强度增大,肥料缓释期先增大后降低。当改性SiO2含量为2%(wt,质量分数)时,制备的包衣肥料缓释期最长,可达59d,与添加改性SiO2之前相比延长了32%。
Gas phase silica(SiO2) was modified using the silanecoupling agent KH550 to prepare the modified SiO2/polyurethane(PU) composite coating for controlled-release fertilizer.The effect of modified SiO2 content on the properties of the resin and the controlled-release fertilizer was investigated.The results showed that compared with before adding modified SiO2,the mixture viscosity of polyol and polyisocyanate with modified SiO2 increased.The composite coating showed an increased water resistance and tensile strength,while an decreased elongation at break.And fertilizer showed an longer controlled-release period.Moreover,with the increase of modified SiO2 content,the viscosity of the mixture increased continuously.The water absorption rate of the coating decreased.The elongation at break and the water contact angle basically remained unchanged.The tensile strength increased.Andthe fertilizer release period first increased and then decreased.When the modified SiO2 content in the coating film layer was 2%,the prepared coated fertilizer had the longest controlled-release period that reached up to 59 days.And this period extended 32% compared with that of fertilizer containing no modified SiO2.
[1] 李汾.改性聚氨酯包膜剂的合成与性能研究[J].山西化工, 2016, 36(5):24-27.
[2] Zhang S G, Yang Y C, Gao B, et al.Superhydrophobic controlled-released fertilizer coated with bio-based polymer with organosilicone and nano-silica modifications[J].Journal of Materials Chemistry A, 2017, 5(37).
[3] Li Q, Wu S, Ru T, et al.Synthesis and performance of polyurethane coated urea as slow/controlled release fertilizer[J].Journal of Wuhan University of Technology Materials Science Edition, 2012, 27(1):126-129.
[4] Trinh T H, Kushaari K Z, Basit A, et al.Use of multi-diffusion model to study the release of urea from urea fertilizer coated with polyurethane-like coating (PULC)[J].Apcbee Procedia, 2014, 8:146-150.
[5] 宫涛, 杨树竹.聚氨酯包膜缓释肥的制备及性能的研究[J].聚氨酯工业, 2014(2):33-36.
[6] 王宇旋, 李桂妃, 任绍志.硅烷偶联剂改性二氧化硅用于制备单组分聚氨酯密封胶[J].化学与粘合, 2010, 32(4):65-67.
[7] Wu W L.SBR/BR blend reinforced by modified silica with KH-550[J].China Elastomerics, 2009.
[8] Zheng W Z, He C P, Zhen Y C, et al.The ultrasonic wave-assisted preparation and modification by KH-550 of SiO2 aerogels[J].Advanced Materials Research, 2012, 554-556:580-583.
[9] 高艳飞.纳米二氧化硅改性纸/塑复合用聚氨酯胶粘剂的研究[J].中国胶粘剂, 2015, 24(2):41-44.
[10] 陈静, 刘爱学, 杨军, 等.KH-550改性纳米SiO2和纳米TiO2对PET/PBT聚酯合金熔融过程中的性能影响[J].塑料工业, 2013, 41(10):5-8.
[11] 朱建君, 翟秋阁, 李晓玲, 等.KH550改性纳米SiO2的制备及其界面相互作用研究[J].化学研究与应用, 2014(7):988-992.
[12] 章芬成, 杨建军, 吴庆云, 等.纳米SiO2改性醇溶性蓖麻油-聚氨酯树脂的制备与表征[J].精细化工, 2012, 29(10):90-94.
[13] 王宇婷, 文卓琼, 文祝友, 等.尿素控释包衣剂的制备及理化性质研究[J].化肥工业, 2015(5):13-17.
[14] Lei S, Yu T, Meng Y G, et al.Influences of medium and temperature on the shear thickening behavior of nano fumed silica colloids[J].物理学报, 2015, 64(6):68301-068301.
[15] 杨树竹.聚氨酯包膜材料耐水性的研究[J].当代化工研究, 2014(8):31-35.
[16] 葛震, 周闪闪, 罗运军.纳米SiO2/有机硅改性水性聚氨酯复合材料的制备及性能[J].复合材料学报, 2014, 31(4):909-915.
[17] Xie J Z, Yang Y C, Gao B, et al.Biomimetic superhydrophobic biobased polyurethane-coated fertilizer with atmosphere “outerwear”[J].ACS Applied Materials & Interfaces, 2017, 9(18):15868-15879.
[18] 刘丹, 袁永朝, 曹红宝.红外光谱法研究聚氨酯脲氢键[J].化学推进剂与高分子材料, 2009, 7(6):60-63.