金属硒化物具有优良的电催化活性,近年来一直受到广泛关注,采用水热法,以Ni(NO3)2·6H2O和硒粉为原料,在不同的循环次数条件下,合成了在碳布上生长的棒状NiSe2,即NiSe2-CC复合材料。通过XRD、SEM、EDS表征对样品的结构、样品的形貌和元素分布进行分析,通过电化学工作站对其电解水析氢性能研究。结果表明,该NiSe2-CC复合材料拥有良好的电解水析氢性能,其中,循环6次的NiSe2-CC-6复合材料的电分解水析氢的性能最好,在1mA/cm2的电流密度下,过电势为121mV;在10mA/cm2的电流密度下,过电势为223mV,塔菲尔斜率为151mV/dec,Cdl为29.7mF/cm2。
Due to the excellent electrocatalytic activity of metal selenide,it has been widely concerned by researchers in recent years.The rod-shaped NiSe2 grown on carbon cloth,namely NiSe2-CC composite,was synthesized using Ni(NO3)2·6H2O,selenium powder as raw materials by hydrothermal method.The structure,morphology and element distribution of the sample were analyzed by XRD,SEM and EDS.The hydrogen evolution performance of the electrolyzed water was studied by electrochemical workstation.The results shown that the composite material had good electrolysis hydrogen evolution performance.Among them,the NiSe2-CC-6 composite material with 6 cycles had the best performance in electrolysis of water.The overpotential at a current density of 1mA/cm2 was 121mV,the overpotential at a current density of 10mA/cm2 was 223mV,the Tafel slope was 151mV/dec and the Cdl was 29.7mF/cm2.
[1] Turner J A.Sustainable hydrogen production[J].Science, 2004(305):972-974.
[2] Luo J, Im J H, Mayer M T, et al.Water photolysis at 12.3% efficiency via perovskite photovoltaics and Earth-abundant catalysts[J].Science, 2014(345):1593-1596.
[3] Montoya J H, Seitz L C, Chakthranont P, et al.Materials for solar fuels and chemicals[J].Nat Mater, 2017(16):70-81.
[4] Bates M K, Jia Q, Ramaswamy N, et al.Composite Ni/NiO-Cr2O3 catalyst for alkaline hydrogen evolution reaction[J].Phys Chem C, 2015(119):5467-5477.
[5] Chinnappan A, Ji D, Jayathilaka W A D M, et al.Facile synthesis of electrospun C@NiO/Ni nanofibers as an electrocatalyst for hydrogen evolution reaction[J].Int J Hydrogen Energy, 2018(43):15217-15224.
[6] Chinnappan A, Chung W J, Kim H.Hypercross-linked microporous polymeric ionic liquid membranes:synthesis, properties and their application in H2 generation[J].Mater Chem, 2015(3):22960-22968.
[7] Chinnappan A, Puguan J M C, Chung W J, et al.Hydrogen generation from the hydrolysis of sodium borohydride using chemically modified multiwalled carbon nanotubes with pyridinium based ionic liquid and decorated with highly dispersed Mn nanoparticles[J].Power Sources, 2015(293):429-436.
[8] Chinnappan A, Kim H, Baskar C, et al.Hydrogen generation from the hydrolysis of sodium borohydride with new pyridinium dicationic salts containing transition metal complexes[J].Int J Hydrogen Energy, 2012(37):10240-10248.
[9] Danilovic N, Subbaraman R, Strmcnik D, et al.Enhancing the alkaline hydrogen evolution reaction activity through the bifunctionality of Ni(OH)2/Metal catalysts[J].Angew Chem, 2012(124):12663-12666.
[10] Kemppainen E, Bodin A, Sebok B, et al.Scalability and feasibility of photoelectrochemical H2 evolution:the ultimate limit of Pt nanoparticle as an HER catalyst[J].Energy Environ Sci, 2015(8):2991-2999.
[11] Yildiz Y, Kuzu S, Sen B, et al.Different ligand based monodispersed Pt nanoparticles decorated with rGO as highly active and reusable catalysts for the methanol oxidation[J].Int J Hydrogen Energy, 2017(42):13061-13069.
[12] Sen B, Kuzu S, Demir E, et al.Polymer-graphene hybride decorated nanoparticles as highly efficient and reusable catalyst for the dehydrogenation of dimethylamineborane at room temperature[J].Int J Hydrogen Ene, 2017(42):23284-23291.
[13] Sen B, Savk A, Sen F.Highly efficient monodisperse Pt nanoparticles confined in the carbon black hybrid material for hydrogen liberation[J].Colloid Interface Sci, 2018, 520:112-118.
[14] Sen B, Kuzu S, Demir E, et al.Hydrogen liberation from the dehydrocoupling of dimethylamine-borane at room temperature by using novel and highly monodispersed RuPtNi nanocatalysts decorated with graphene oxide[J].Int Hydrogen Energy, 2017(42):23299-232306.
[15] Wang F, Li Y, Shifa T A, et al.Selenium-enriched nickel selenide nanosheets as a robust electrocatalyst for hydrogen generation[J].Angew Chem Int, 2016(55):6919-6924.
[16] Swesi A T, Masud J, Liyanage W P R, et al.Textured NiSe2 film:bifunctional electrocatalyst for full water splitting at remarkably low overpotential with high energy efficiency[J].Scientific Reports, 2017, 7(1):2401.
[17] Liu C, Chen Q, Hao Q, et al.Ni(OH)2/NiSe2 hybrid nanosheet arrays for enhanced alkaline hydrogen evolution reaction[J].International Journal of Hydrogen Energy, 2019, 44(10):4832-4838.
[18] Sun X H, Shao Q, Pi Y C, et al.A general approach to synthesise ultrathin NiM (M=Fe, Co, Mn) hydroxide nanosheets as high-performance low-cos electrocatalysts for overall water splitting[J].Mater Chem A, 2017, 5(17):7769-7775.