NiCo2O4/泡沫镍复合电极材料的制备及其超级电容器性能研究

展开
  • 1.黔南民族师范学院化学化工学院,都匀558000;
    2.中山大学化学学院,广州510275
柏任流(1969-),男,硕士,副教授,主要从事储能材料与器件的研究,E-mail:xiangyi481230@126.com。

网络出版日期: 2020-10-20

基金资助

贵州省科技厅联合基金(黔科合KY字[2015]7718);贵州省普通高等学校工程研究中心项目(黔教合KY字[2015]342和黔教合KY字[2018]010);黔南民族师范学院校级项目(qnsy2015);黔南民族师范学院大学创新创业项目(201510670003)

Study on fabrication and performance of NiCo2O4/NF electrode material as supercapacitor

Expand
  • 1.School of Chemistry and Chemical Engineering,Qiannan Normal University for Nationalities, Duyun 558000;
    2.School of Chemistry,Sun Yat-sen University,Guangzhou 510275

Online published: 2020-10-20

摘要

通过水热法和焙烧法在泡沫镍(NF)上制备了具有纳米片状的钴酸镍(NiCo2O4/NF),采用X射线衍射(XRD)、扫描电子显微镜(SEM)、N2等温吸附/脱附测试和电化学测试等手段,对NiCo2O4/NF样品的组成、形貌和电化学性能等进行表征。结果表明:具有纳米片状的NiCo2O4均匀地生长在NF表面。当NiCo2O4/NF作为一种不使用胶黏剂的电极材料时,表现出良好的电化学性能,其在电流密度为1A/g时比电容可高达1102F/g,在电流密度10A/g条件下循环测试5000次后,比电容损失量约为11.3%。此外,以NiCo2O4/NF为正极,活性炭(AC)为负极组装了非对称超级电容器(NiCo2O4/NF//AC-ASC),发现其具有高能量密度及良好的循环稳定性。

本文引用格式

柏任流, 甄德帅, 吴大旺, 张悦红, 文志刚, 张杰, 邹洪涛, 童叶翔 . NiCo2O4/泡沫镍复合电极材料的制备及其超级电容器性能研究[J]. 化工新型材料, 2020 , 48(10) : 73 -77 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.10.016

Abstract

The NiCo2O4 nanosheets uniformly grown on the Ni foam (CF)(NiCo2O4/NF) were successfully fabricated by a hydrothermal method,followed by the calcination process.The compositions,morphologies and electrochemical performance of NiCo2O4/NF were demonstrated by XRD,SEM,N2 adsorption/desorption measurements,and electrochemical measurements.The results suggested that the NiCo2O4 nanosheets uniformly grown on the NF,and NiCo2O4 nanosheets had the good electrochemical performance.For example,the specific capacitance value of NiCo2O4/NF was up to 1102F/g and the after a 4000-cycle test at a current density of 10A/g,the retention capacitance value was about 88.7%.In addition,an ASC was assembled using NiCo2O4/NF as the positive electrode and activated carbon (AC) as the negative electrode,which shown a high energy density and remarkable cycling performance.

参考文献

[1] Yu X Y, Yao X Z.T, Facile synthesis of urchin-like NiCo2O4 hollow microspheres with enhanced electrochemical properties in energy and environmentally relate application[J].ACS Applied Materials & Interfaces, 2014, 6:268995-269036.
[2] Zhang C Q, Lou X W.General solution growth of mesoporous NiCo2O4 nanosheets on various conductive substrates as high performance electrodes for supercapacitors[J].Advanced Materials, 2013, 25:976-979.
[3] Gang J D, Zhou H M.Ultrathin porous NiCo2O4 Nanosheets arrays on flxible carbon fabric for high performances supercapacitors[J].ACS Applied Materials & Interfaces, 2013, 5:7405-7409.
[4] Liu X Y, Shi S J, Xing Q Q.Hierarchial NiC2O4@NiCo2O4 core/shell nanoflake arrays as high performances supercapacitor materials[J].ACS Applied Materials & Interfaces, 2013, 5:8790-8795.
[5] Zhang C, Shen X Q.Preparation of spinel NiFe2O4 fibres by organicgel-thermal decompostion process[J].Journal of Sol-Gel Science and Technology, 2007, 42:95-100.
[6] Li C, Balamurugan J, Kim N H, et al.Hierarchical Zn-Co-S nanowires as advanced electrodes for all solid state asymmetric supercapacitors[J].Advanced Energy Materials, 2018, 8(8):1702014.
[7] Moosavifard S E, Fani S, Rahmanian M.Hierarchical CuCo2S4 hollow nanoneedle arrays as novel binder-freeelectrodes for high-performance asymmetric supercapacitors[J].Chemical Communications, 2016, 52(24):4517-4520.
Options
文章导航

/