采用传统高温固相法在较低温度下制备Sm3+离子掺杂Sr3MgSi2O8橙红色荧光粉,研究了Sr3-xMgSi2O8:x% Sm3+的晶体结构和发光性能。激发和发射光谱表明,样品可被近紫外350~420nm波段激发,最强激发峰位于402nm处,发射光谱呈现出Sm3+的特征橙红色,谱带峰值分别在563nm、601nm、644nm,对应于 4G5/2→6H5/2、4G5/2→6H7/2和 4G5/2→6H9/2特征跃迁。最强发射对应的掺杂浓度为5%(摩尔分数,下同),浓度猝灭的发生主要是因为非辐射荧光粉中Sm3+离子之间的能量转移。浓度为5%的CIE坐标为(0.5548,0.4366)最接近橙红色,获得极佳的演色性。样品Sr3-xMgSi2O8:x% Sm3+荧光粉是一种具有应用潜力的近紫外激发三基色白光LED用橙红色荧光粉。
The Sm3+ ion-doped Sr3MgSi2O8 orange-red phosphor was prepared at a lower temperature by conventional high-temperature solid-phase method.The crystal structure and luminescence properties of Sr3-xMgSi2O8:x% Sm3+ were studied.The excitation and emission spectra shown that the sample can be excited by the near-ultraviolet 350~420nm band,and the strongest excitation peak was located at 402nm.The emission spectrum exhibited characteristic orange-red emission of Sm3+,and the peak positions of the bands were at 563nm,601nm and 644nm.Corresponding to 4G5/2→6H5/2,4G5/2→6H7/2 and 4G5/2→6H9/2 characteristic transitions,respectively.The results shown that the doping concentration corresponding to the strongest emission was 5%,and the CIE coordinate was (0.5548,0.4366),which was closest to orange-red color,and obtained a lower color temperature and excellent color rendering.The sample Sr3-xMgSi2O8:x% Sm3+ phosphor was an orange-red phosphor for near-ultraviolet excitation trichromatic white LED with potential application.
[1] Shi M L,Zhu C F,Wei M Z,et al.Dy3+,Tb3+,and Eu3+ activated NaCa4(BO3)3 phosphors for lighting based on near ultraviolet light emitting diodes[J].Vacuum,2018,149:343-349.
[2] Zhou Y,Zhu C F,Zhang M M,et al.Optical properties of Eu and Dy doped calcium aluminoborosilicate glasses for LED applications[J].Journal of Alloys and Compounds,2016,688:715-720.
[3] Zhao C,Wu Y H,Wang D H,et al.A near-ultraviolet (NUV) converting blue-violet Mg2SiO4:Ce3+ phosphor for white light-emitting-diodes (w-LEDs)[J].Journal of Luminescence,2019,207:241-245.
[4] Zhang Z W,Wang L J,Han L,et al.High-brightness Eu3+-doped La0.67Mg0.5W0.5O3 red phosphor for NUV light-emitting diodes application[J].Materials Letters,2015,160:302-304.
[5] 张方圆,谢建军,汪暾,等.Bi4Si3O12:Sm3+荧光粉的制备及发光性能的研究[J].人工晶体学报,2017,46(8):1493-1497.
[6] 海热古·吐逊,吐沙姑·阿不都吾甫,美合日古丽·麦麦提,等.Sm3+掺杂天然钠长石(NaAlSi3O8)荧光粉的发光性质研究[J].人工晶体学报,2017,46(9):1697-1702,1708.
[7] 王邦卿,宁青菊,王秀峰.白光LED用稀土Eu掺杂氯硅酸盐荧光粉的研究进展[J].化工新型材料,2011,39(11):9-10,131.
[8] 宋俊,陆启飞,孙亮,等.用于红蓝光LED的(Ba,Sr)3MgSi2O8:Eu2+,Mn2+荧光材料的热光衰性能[J].光学学报,2013,33(10):216-220.
[9] Wang L C,Lu Q F,Li J,et al.Microwave firing-incubation of cage-like (Ba,Sr)3MgSi2O8:0.06Eu2+,0.1Mn2+ sphere from sprayed template-free xerogel particles[J].Journal of Rare Earths,2013,31(6):541-545.
[10] 武秀兰,张晋春,朱建锋,等.LED用红色荧光粉NaGdTiO4:Sm3+的合成与发光性能[J].人工晶体学报,2015,44(4):972-975.
[11] 王萍,杨定明,王刚.白光LED用K2ZnSiO4:Sm3+橙红色荧光粉的制备及发光性能[J].硅酸盐学报,2015,43(12):1772-1776.
[12] Li J G,Yan H F,Yan F M.A novel orange-red emitting borate based phosphor for NUV pumped LEDs[J].Optik,2016,127(15):5984-5989.
[13] 贺香红.LED用红色荧光粉SrZnO2:Sm3+,Li+的合成与发光性能[J].稀有金属材料与工程,2007,36(9):1574-1577.
[14] Ren Y,Liu Y,Yang R.A series of color tunable yellow-orange-red-emitting SrWO4:RE (Sm3+,Eu3+-Sm3+) phosphor for near ultraviolet and blue light-based warm white light emitting diodes[J].Superlattices and Microstructures,2016,91:138-147.
[15] Zhao J,Huang S X,Zhao D,et al.Sm3+,doped K3Gd3B4O12:an orange-emitting phosphor for white light-emitting diodes[J].Optik,2018,159:115-122.
[16] Chen C T,Lin T J,Molokeev M S,et al.Synthesis,luminescent properties and theoretical calculations of novel orange-red-emitting Ca2Y8(SiO4)6O2:Sm3+,phosphors for white light-emitting diodes[J].Dyes and Pigments,2018,150:121-129.
[17] Man Y,Liu G H,Wen J H,et al.Blue-light-excited Eu3+/Sm3+ co-doped NaLa(MoO4)2 phosphors:synthesis,characterizations and red emission enhancement for WLEDs[J].Materials,2018,11(7):1090-1101.
[18] Wu J X,Li M,Wang M T,et al.Preparation and luminescence properties of NaLa(WO4)2:Sm3+,orange-red phosphor[J].Journal of Luminescence,2018,197:219-227.
[19] Zhang X G,Chen M Y,Zhang J L,et al.Photoluminescence studies of high-efficient red-emitting K2Y(WO4)(PO4):Eu3+,phosphor for NUV LED[J].Materials Research Bulletin,2016,73:219-225.
[20] 吴锦绣,李梅,崔松松,等.SrMoO4:Sm3+,Na+红色荧光粉的形貌调控和发光性能[J].无机化学学报,2017,33(2):219-226.
[21] 温慧霞,樊彬,王伟岸,等.白光LED用Ca2-x-ySiO3Cl2:xDy3+,yEu3+单一基质荧光粉的制备及发光性能研究[J].内蒙古科技大学学报,2018,37(4):307-310,348.