以丁腈橡胶为基体,通过添加芳纶纤维制备了芳纶纤维增强橡胶复合材料(AFRC),研究了纤维长度、纤维质量分数对AFRC横向和纵向拉伸性能的影响。结果表明:随着纤维质量分数的增加,AFRC的横向和纵向抗拉强度呈上升趋势,且纵向抗拉强度普遍高于横向抗拉强度;纤维质量分数为4%、长度为3mm时,AFRC综合性能较优。
With nitrile rubber as the matrix,aramid fiber reinforced rubber composites (AFRC) were prepared by adding aramid fibers,and the effects of fiber length and fiber mass fraction on the transverse and longitudinal tensile properties of AFRC were studied.When the mass fraction increases,the transverse and vertical tensile strength of AFRC is increasing,and the initial tensile strength is generally higher than the transverse tensile strength;when the fiber mass fraction is 4% and the length is 3mm,the comprehensive performance of AFRC is better.
[1] 杜善义.先进复合材料与航空航天[J].复合材料学报,2007,24(1):1-12.
[2] 黄星路,孙开俊,顾伯勤,等.非石棉短纤维增强橡胶基密封复合材料的力学设计[J].中国科技论文在线,2011,6(6):429-433;442.
[3] Zhang Bin,Gu Boqin,Yu Xiaoming.Failure behavior of resorcinol formaldehyde latex coated aramid short fiber reinforced rubber sealing under transverse tension[J].Journal of Applied Polymer Science,2015,132(12):41672.
[4] Gao J,Yang X,Huang L H,et al.Experimental study on mechanical properties of aramid fibres reinforced natural rubber/SBR composite for large deformation-quasi-static mechanical properties[J].Plastics Rubber and Composites,2018,47(9):381-390.
[5] 丁翔,王瑞,徐磊,等.改性芳纶浆粕增强橡胶基复合材料的性能研究[J].化工新型材料,2019,47(1):83-86.
[6] 宋位华,孙云波,鲁学峰,等.芳纶纤维表面处理及其增强天然橡胶复合材料的研究[J].化工新型材料,2018,46(11):104-107.
[7] 王敏,陈晔,顾伯勤.芳纶-玻纤混杂纤维增强橡胶基密封复合材料制备工艺研究[J].润滑与密封,2007,32(3):51-54.
[8] Hintze C,Boldt R,Wiessner S,et al.Influence of processing on morphology in short aramid fiber reinforced elastomer compounds[J].Journal of Applied Polymer Science,2013,130(3):1682-1690.
[9] Zhang Bin,Yu Xiaoming,Gu Boqin.Modeling and experimental validation of interfacial fatigue damage in fiber reinforced rubber composites[J].Polymer Engineering and Science,2018,58(6):920-927.
[10] 李明专,王君,鲁圣军,等.芳纶纤维的研究现状及功能化应用进展[J].高分子通报,2018(1):58-69.