采用静电纺丝法,以聚苯乙烯(PS)和聚丙烯腈(PAN)为溶质,N,N-二甲基甲酰胺(DMF)为溶剂,制备了水接触角为152.5°的具有肩并肩结构的超疏水PS/PAN复合纳米纤维。通过扫描电子显微镜和光学接触角测量仪研究了PS/PAN质量配比、注射速度对复合纳米纤维直径、形貌特征、疏水性及疏水稳定性的影响。结果表明:当PS质量分数占PS/PAN质量分数70%、注射速度为1mL/h时,复合纳米纤维具有较好的疏水稳定性和超疏水性,纤维直径最小,具有明显的肩并肩结构;纤维直径、表面粗糙度和PS含量是影响疏水性的关键因素;PS含量的增加有助于提高复合纳米纤维的疏水稳定性。
The side-by-side superhydrophobic PS/PAN nanofibers with water contact angle of 152.5° were prepared using polystyrene (PS) and polyacrylonitrile (PAN) as solute and N,N-dimethyl formamide (DMF) as solvent by electrostatic spinning.The fiber diameter,morphology characteristics,hydrophobicity and hydrophobic stability were researched by scanning electron microscope (SEM) and optical contact angle measurement under different content ratios and injection speeds.The results showed that the fiber had good hydrophobic stability and hydrophobicity when the mass fraction of PS in PS/PAN was 70% and the injection rate was 1mL/h,the fiber diameter was the smallest,and the fiber had obvious side-by-side structure.It was found that the fiber diameter,surface roughness and PS content were the key factors of hydrophobicity.The increase of PS content was helpful to improve the hydrophobic stability of the composite fiber.
[1] Koch K,Bhushan B,Jung Y C.Self-cleaning efficiency of artificial superhydrophobic surfaces[J].Langmuir,2009,25:3240-3248.
[2] Mchale G,Newton M I,Shirtcliffe N J,et al.Immersed superhydrophobic surfaces:gas exchange,slip and drag reduction properties[J].Soft Matter,2010,6:714-719.
[3] Wang N,Tang L,Cai Y,et al.Scalable superhydrophobic coating with controllable wettability and investigations of its drag reduction[J].Colloids and Surfaces A,2018,555:290-295.
[4] Isimjan T T,Wang T,Rohani S.A novel method to prepare superhydrophobic,UV resistance and anti-corrosion steel surface[J].Chemical Engineering Journal,2012,210:182-187.
[5] Zhang Z,Yang Y,Li C,et al.Porous nanofibrous superhydrophobic membrane with embedded Au nanoparticles for the integration of oil/water separation and catalytic degradation[J].Journal of Membrane Science,2019,582:350-357.
[6] Liu Z,Tang Y,Zhao K,et al.Superhydrophobic SiO2 micro/nanofibrous membranes with porous surface prepared by freeze electrospinning for oil adsorption[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2019,568:356-361.
[7] Sun Q,Liu H,Chen T,et al.Facile fabrication of iron-based superhydrophobic surfaces via electric corrosion without bath[J].Applied Surface Science,2016,369:277-287.
[8] Dong C,Yu G,Zhong M,et al.Fabrication of superhydrophobic Cu surfaces with tunable regular micro and random nano-scale structures by hybrid laser texture and chemical etching[J].Mater Process Technol,2011,211(7):1234-1240.
[9] Mahadik S A,Kavale M S,Mukherjee S K,et al.Transparent superhydrophobic silica coatings on glass by sol-gel method[J].Applied Surface Science,2010,257(2):333-339.
[10] Feng S,Luo W,Wang L,et al.Preparation and property of extremely stable superhydrophobic carbon fibers with core-shell structure[J].Carbon,2019,150:284-291.
[11] Li Y,Li L,Sun J Q.Bioinspired self-healing superhydrophobic coatings[J].Angewandte Chemie International Edition,2010,122(35):6265-6269.
[12] Daewoo H,Steckl A J.Superhydrophobic and oleophobic fibers by coaxial electrospinning[J].Langmuir,2009,25(16):9454-9462.
[13] 孙晶,王瑞,孙红玉,等.聚偏氟乙烯超疏水纳米纤维膜的制备及性能研究[J].化工新型材料,2019,47(4):115-119;124.
[14] Li B,Luo J,Huang X,et al.A highly stretchable,super-hydrophobic strain sensor based on polydopamine and graphene reinforced nanofiber composite for human motion monitoring[J].Composites Part B,2020,181:107580.
[15] Moradi G,Zinadini S,Rajabi L,et al.Full length article fabrication of high flux and antifouling mixed matrix fumarate-alumoxane/PAN membranes via electrospinning for application in membrane bioreactors[J].Applied Surface Science,2018,427:830-842.
[16] Yang S,Lei P,Shan Y,et al.Preparation and characterization of antibacterial electrospun chitosan/poly(vinyl alcohol)/graphene oxide composite nanofibrous membrane[J].Applied Surface Science,2018,435:832-840.
[17] Zhan N,Li Y,Zhang C,et al.A novel multinozzle electrospinning process for preparing superhydrophobic PS films with controllable bead-on-string/microfiber morphology[J].Journal of Colloid and Interface Science,2010,345(2):491-495.
[18] Zhang G,Wang P,Zhang X,et al.The preparation of PCL/MSO/SiO2 hierarchical superhydrophobic mats for oil-water separation by one-step method[J].European Polymer Journal,2019,116:386-393.
[19] Li W,Yu Q,Yao H,et al.Superhydrophobic hierarchical fiber/bead composite membranes for efficient treatment of burns[J].Acta Biomater,2019,92:60-70.
[20] Li W,Wang H,Li Z.Preparation of golf ball-shaped microspheres with fluorinated polycaprolactone via single-solvent electrospraying for superhydrophobic coatings[J].Progress in Organic Coatings,2019,131:276-284.
[21] 李芳,贾坤,李其明,等.静电纺丝制备超疏水/超亲油空心微球状PVDF纳米纤维及其在油水分离中的应用[J].化工新型材料,2016,44(3):223-225.
[22] Su C,Li Y,Cao H,et al.Novel PTFE hollow fiber membrane fabricated by emulsion electrospinning and sintering for membrane distillation[J].Journal of Membrane Science,2019,583:200-208.