采用微波溶剂热法、溶剂热法和共沉淀法三种方法合成碘氧化铋(BiOI)光催化剂,并对其进行了性能表征;以罗丹明B(RhB)为目标污染物,进行可见光光降解性能测试。研究结果表明,共沉淀法合成的BiOI结晶性最好,但溶剂热法合成的材料比表面积最大,降解性能最好,可见光照射60min后,对40mg/L的RhB溶液的降解率达96%。
Bismuth iodide (BiOI) photocatalyst was synthesized by microwave solvothermal method,solvothermal method and coprecipitation method,and characterized.Methyl orange was used as the target pollutant to test the photodegradation performance under visible light.The results shown that the BiOI synthesized by coprecipitation method had the best crystallinity,but the material synthesized by solvent method had the largest specific surface area and the best degradability.After visible light irradiation on 60min,the degradation rate of BiOI to rhodamine b solution of 40mg/L can reach 96%.
[1] Reddy P,Reddy P,Kwon E,et al.Recent advances in photocatalytic treatment of pollutants in aqueous media[J].Environment International,2016,91:94-103.
[2] Cheng H F,Huang B B,Dai Y.Engineering BiOX(X=Cl,Br,I) nanostructures for highly efficient photocatalytic applications[J].Nanoscale,2014,6:2009-2026.
[3] He R A,Cao S W,Zhou P,et al.Recent advances in visible light Bi-based photocatalysts[J].Chinese Journal of Catalysis,2014,35(7):989-1007.
[4] 张进,徐丹,冒彩云.碘氧化铋的制备及可见光催化性能研究[J].化工新型材料,2018,46(5):192-194.
[5] Jia M K,Hu X L,Wang S L,et al.Photocatalytic properties of hierarchical BiOXs obtained via an ethanol-assisted solvothermal process[J].Journal of Environmental Sciences,2015,35(9):172-180.
[6] 连辉,李刚.水解法制备BiOI及其可见光光催化性能的研究[J].化学工程师,2017(5):10-13.
[7] Yan C X,Zhang Z L,Wang W J,et al.Synthesis and characterization of polyaniline-modified BiOI:a visiblelight-response photocatalyst[J].Journal of Materials Science:Materials in Electronics,2018,29:18343-18351.
[8] Ma M G,Zhu Y J,Cheng G F,et al.Microwave synthesis and characterization of ZnO with various morphologies[J].Materials Letters,2008,62(3):507-510.
[9] 王鹏.环境微波化学技术[M].北京:化学工业出版社,2003.
[10] Wan Q,Wang T H,Zhao J C.Enhanced photocatalytic activity of ZnO nanotetrapods[J].Applied Physics Letters,2005,87(7):0831051-0831053.
[11] Sugraez R,Alvarez J I,Cruz-Yusta M,et al.Enhanced photocatalytic degradation of NOx gases by regulating the microstructure of mortar cement modified with titanium dioxide[J].Building & Environment,2013,69(11):55-63.
[12] Xu H,Yan J,Xu Y G,et al.Novel visible-light-driven Ag X/graphite-like C3N4(X=Br,I)hybrid materials with synergistic photocatalytic activity[J].Applied Catalysis B:Environmental,2013,129(17):182-193.