为了改善改性双基推进剂的力学性能,并提高推进剂的能量,用纤维素甘油醚硝酸酯(NGEC)替代硝化纤维素,采用吸收-压延法制备推进剂样品并进行了研究。对NGEC的基本理化性能进行了测试;采用靶线法测试了推进剂的燃速,并计算了压力指数,发现随着NGEC的加入,推进剂燃速与原配方样品均有所增加;高低温力学性能实验结果显示,含NGEC配方样品抗拉强度及延伸率均有不同程度的改善,尤其在高能高固推进剂配方中,低温条件下抗拉强度增幅达到43.2%,延伸率增幅达66.7%,充分证明NGEC能够改善双基推进剂低温脆的缺点;爆热测试结果显示NGEC的加入能够小幅提高爆热。
In order to improve the mechanical property of the modified double-base propellant and improved the energy of the propellant,cellulose glyceryl ether nitrate (NGEC) was used instead of nitrocellulose,and propellant samples were prepared by an absorption-extrusion method.The basic physical and chemical properties of NGEC were tested.The burning rate of the propellant was measured by the target line method,and the pressure index was calculated.It was found that with the addition of NGEC,the burning rate of each formula propellant increased.The results of high and low-temperature mechanical properties test shown that the tensile strength and elongation of NGEC-containing formulation were improved,especially in the high-energy and high-solid propellant formulation,the tensile strength increased by 43.2% under low-temperature condition,and the elongation rate increases by 66.7%.It fully proved that NGEC can improve the shortcoming of low-temperature brittleness of double-base propellant.The results of the thermal test showed that the addition of NGEC could slightly increase the explosive heat.
[1] 邵自强,杨雯霏,王文俊,等.新一代纤维素基高性能黏合剂的研究和发展[J].火炸药学报,2006,29(2):55-57.
[2] 邵自强.硝化纤维素生产工艺及设备[M].北京:北京理工大学出版社,2002,4-12.
[3] 王飞俊,杨雯霏,王江宁,等.NGEC基改性双基推进剂的制备及性能[J].火炸药学报,2006,29(6):51-53.
[4] 潘葆,刘所恩,张有德,等.纤维素甘油醚硝酸酯(NGEC)在高能低特征信号推进剂配方中应用研究[C].贵阳:火炸药学术研讨会论文集,2008.
[5] 汪渊,刘蓉,宁斌科,等.硝化棉的热分解机理[J].含能材料,1998,6(4):157-168.
[6] Pourmortazavi S M,Hosseini S G,Rahimi-Nasrabadi M.Effect of nitrate content on thermal decomposition of nitrocellulose[J].Journal of Hazardous Materials,2009,162:1141-1144.
[7] 张有德,邵自强,李博,等.NGEC的热行为和热分解机理[J].含能材料,2010,18(5):568-573.
[8] Pourmortazavi S M,Kohsari I,Teimouri M B,et al.Thermal behavior kinetic study of dihydroglyoxime and dichloroxime[J].Materials Letters,2007,61:4670-4673.
[9] Zhang Tonglai,Hu Rongzu,Xie Yi,et al.The estimation of critical temperatures of thermal explosion for energetic materials using non-isothermal DSC[J].Thermochim Acta,1994,244:171-176.
[10] 王国强,马晓燕,卢先明,等.热塑性弹性体复合推进剂研究[J].火炸药学报,1999,22(3):68-70.
[11] 王飞俊,杨斐霏,王江宁,等.NGEC基改性双基推进剂的制备及性能[J].火炸药学报,2006,29(6):51-53.
[12] 邵自强,王飞俊,杨斐霏,等.二羟丙基纤维素硝酸酯的合成及性能表征[J].含能材料,2004,12(3):138-142.
[13] 张有德,邵自强,周晋红,等.纤维素甘油醚硝酸酯粘合剂及其推进剂的力学性能[J].推进技术,2010,31(3):345-350.
PDF
(1265KB)