采用多元醇法制备镁-镍合金纳米粉末,并以此为催化剂制备纳米碳管,利用比表面和孔径分布测定仪、X射线衍射仪和透射电镜,研究镁-镍合金催化剂的性能和纳米碳管的生长模式。结果表明:Mg∶Ni值对镁-镍合金催化剂特性影响较大,其中Mg∶Ni为1的催化剂颗粒比表面积较大且平均粒径较小;聚乙烯吡咯烷酮(PVP)用量增大,有利于提高催化剂颗粒的比表面积、减小平均粒径,但用量过大不利于Mg2Ni合成。在以镁-镍合金为催化剂制备碳纳米管的过程中,首先在催化剂表面形成碳膜,随后形成的碳膜将前期形成的碳膜及催化剂颗粒向外推挤,催化剂颗粒移动后遗留下中空隧道,最终形成碳管,由于纳米碳管尖端的催化剂颗粒反应后失去催化活性,碳管的生长动力主要来自碳管根部。
Mg-Ni alloy nano-powder was prepared by polyol method and used as catalyst to prepare carbon nanotubes(CNTs).The performance of Mg-Ni alloy catalyst was studied by measurement of specific surface area and pore size distribution and XRD.The growth process of CNTs was studied by TEM.The results shown that the change of Mg∶Ni value greatly affected the performances of Mg-Ni alloy catalysts,and the catalyst particles with Mg∶Ni value of 1 had larger specific surface area and smaller average particle size.The increase of the amount of PVP was beneficial to increase the specific surface area of the catalyst particles and reduced the average particle size,but the excessive amount was not conducive to the synthesis of Mg2Ni.In the process of preparing CNTs by using Mg-Ni alloy as catalyst,a carbon film was first formed on the surface of the catalyst,and then the formed carbon film pushed the carbon film and catalyst particles formed in the early stage outward,and the hollow tunnel was left after the catalyst particles move.Finally,a carbon tube was formed.Since the catalyst particles at the tip of CNTs losed catalytic activity after reaction,the growth dynamics of CNTs mainly came from the roots of the carbon tubes.
[1] Henglein A.Small-particle research:physicochemical properties of extremely small colloidal metal and semiconductor particles[J].Cheminform,1990,21(17):1861-1873.
[2] Dagani R.Gallium ‘triple bonds’ under fire[J].Chem Eng News,1998,76(11):31-35.
[3] Gates B C.Supported metal clusters:synthesis,structure,and catalysis[J].Chemical Reviews,1995,26(37):511-522.
[4] Trunschke A,Dang L H,Lieske H.In situ FT-IR studies of high-temperature adsorption of hydrogen on zirconia[J].Journal of the Chemical Society Faraday Transactions,1995,91(24):4441-4444.
[5] Lee A F,Baddeley C J,Hardacre C,et al.Structural and catalytic properties of novel Au/Pd bimetallic colloid particles:EXAFS,XRD,and acetylene coupling[J].Chemin Form,1995,26(34):6096-6102.
[6] Li Y D,Li L Q,Liao H W,et al.Preparation of pure nickel,cobalt,nickel-cobalt and nickel-copper alloys by hydrothermal reduction[J].Journal of Materials Chemistry,1999,9(10):2675-2677.
[7] Aymard L,Dumont B,Viau G.Production of Co,Ni alloys by mechanical-alloying[J].Journal of Alloys & Compounds,1996,242(1-2):108-113.
[8] Imamoto T,Mita T,Yokoyama M.Reduction of organic compounds with rare-earth intermetallics containing absorbed hydrogen[J].Cheminform,1988,19(21):5695-5699.
[9] 王利,闫慧忠,吴建民.稀土储氢合金研究及发展现状[J].稀土信息,2018(3):8-11.
[10] Ma J,Jiang X,Jiang L,et al.Hydrogen evolution reaction on composite-coated electrodes of ball milling-formed nanocrystalline Ni-Mo alloy[J].Acta Physico-chimica Sinica,1996,12(1):22-28.
[11] Toshima N,Lu P.Synthesis and catalysis of colloidal dispersions of Pd/Ni bimetallic clusters[J].Chemistry Letters,1996,1996(9):729-730.
[12] Zeng H C,Lin J,Teo W K,et al.Monoclinic ZrO2 and its supported materials Co/Ni/ZrO2 for N2O decomposition[J].Journal of Materials Research,1995,10(3):545-552.
[13] 余建平,甘金朝,林燕,等.氟离子选择电极法测定稀土-镁金属间化合物中的氟[J].稀土,2012,33(3):82-85.
[14] Wu Z,Wu J,Zhang L,et al.Effect of volume fraction on the coarsening of Pb nanophase in Al-Pb nanocomposite alloys prepared by high energy ball milling[J].Rare Metal Materials and Engineering,2018,47(7):1993-1998.
[15] 刘腾蛟,冉广,黄金华,等.高能球磨制备中子吸收体Fe-Dy2O3纳米晶粉末的研究[J].材料热处理学报,2016,37(12):7-11.
[16] Zheng M D,He X J,Yi T F,et al.Synthesis of carbon nanotubes at different pressure by arc discharge and its characterization[J].Journal of Functional Materials & Devices,2008,124(15):3759-3762.
[17] 李启厚,毕丹丹,刘志宏,等.多元醇法制备超微粉体材料的特点及应用[J].粉末冶金材料科学与工程,2008,13(2):79-83.
基金资助
陕西省教育厅专项科研计划项目(15JK2186);国家科技重大专项项目(2017ZX04011010)
PDF
(2369KB)