以二苯基甲烷二异氰酸酯(MDI)、聚四氢呋喃醚二醇(PTMG)、1,4-丁二醇(BDO)为原料,无催化剂条件下制备了热塑性聚氨酯,通过红外光谱(FT-IR)、核磁共振谱(NMR)、凝胶渗透色谱(GPC)等方法表征了其结构。通过变温红外光谱研究了温度对聚氨酯中氨基甲酸酯及氢键的影响,结果发现,当温度升高时氢键开始解离,而温度降低时氢键又发生重组;当温度升高到130℃及以上时,氨基甲酸酯有极少量解离,温度降低时又重新形成氨基甲酸酯。热重分析结果表明,热塑性聚氨酯样品热稳定性较好。
Thermoplastic polyurethanes were prepared with diphenylmethane diisocyanate (MDI),polytetramethylene ether glycol (PTMG) and 1,4-butanediol (BDO) without catalysts.Their structures were characterized by fourier transform infrared spectroscopy(FT-IR),nuclear magnetic resonance spectroscopy (NMR) and gel permeation chromatography (GPC).The effect of temperature on the urethane and hydrogen bonding in polyurethane was studied by variable-temperature infrared spectroscopy.It was found that hydrogen bonding begins to dissociate with increasing temperature,while the new hydrogen bonding reformed with decreasing temperature,and carbamate dissociates very little with temperature rising to 130℃ and above,while carbamate reformed with decreasing temperature.Thermogravimetric analysis results showed that the thermoplastic polyurethane samples had good thermal stability.
[1] Kim S M,Jeon H,Shin S H,et al.Superior toughness and fast self-healing at room temperature engineered by transparent elastomers[J].Advanced Materials,2018,30(1):1705145.
[2] Zheng N,Hou J,Xu Y,et al.Catalyst-free thermoset polyurethane with permanent shape reconfigurability and highly tunable triple-shape memory performance[J].ACS Macro Letters,2017,6(4):326-330.
[3] Matsukizono H,Endo T.Re-workable polyhydroxyurethane films with reversible acetal networks obtained from multi-functional six-membered cyclic carbonates[J].Journal of the American Chemical Society,2018,140(3):884-887.
[4] Y1lgör E,Y1lgör I,Yurtsever E.Hydrogen bonding and polyurethane morphology.Ⅰ.Quantum mechanical calculations of hydrogen bond energies and vibrational spectroscopy of model compounds[J].Polymer,2002,43(24):6551-6559.
[5] Yilgör E,Yurtsever E,Yilgör .Hydrogen bonding and polyurethane morphology.Ⅱ.Spectroscopic,thermal and crystallization behavior of polyether blends with 1,3-dimethylurea and a model urethane compound[J].Polymer,2002,43(24):6561-6568.
[6] Senich G A,MacKnight W J.Fourier transform infrared thermal analysis of a segmented polyurethane[J].Macromolecules,1980,13(1):106-110.
[7] Tao H J,Meuse C W,Yang X,et al.A spectroscopic analysis of phase separation behavior of polyurethane in restricted geometry:chain rigidity effects[J].Macromolecules,1994,27(24):7146-7151.
[8] Meuse C W,Yang X,Yang D,et al.Spectroscopic analysis of ordering and phase-separation behavior of model polyurethanes in a restricted geometry[J].Macromolecules,1992,25(2):925-932.
[9] Lin C K,Kuo J F,Chen C Y,et al.Investigation of bifurcated hydrogen bonds within the thermotropic liquid crystalline polyurethanes[J].Polymer,2012,53(1):254-258.
[10] Zheng N,Fang Z,Zou W,et al.Thermoset shape-memory polyurethane with intrinsic plasticity enabled by transcarbamoylation[J].Angewandte Chemie International Edition,2016,55(38):11421-11425.
[11] Ferrillo R G,Arendt V D,Granzow A H.DSC study of the polyurethane formation from poly(ethylene adipate) and toluene diisocyanate[J].Journal of Applied Polymer Science,1983,28(7):2281-2289.
[12] Teo L S,Chen C Y,Kuo J F.Fourier transform infrared spectroscopy study on effects of temperature on hydrogen bonding in amine-containing polyurethanes and poly(urethane-urea)s[J].Macromolecules,1997,30(6):1793-1799.
基金资助
污染物分析与资源化技术湖北省重点实验室(湖北师范大学)资助项目(PA20170103)
PDF
(1939KB)