通过扫描电子显微镜分析和树脂冲击性能测试,研究了聚醚砜(PES)对高温环氧树脂5284性能的影响及增韧机理,并基于“离位”增韧技术制备了具有增韧功能的ES-U3160织物。以ES-U3160织物作为增强体,采用树脂转移模塑成型(RTM)工艺制备了ES-U3160/5284复合材料,并对复合材料的韧性性能进行研究。结果表明:随着PES含量的增加,环氧树脂5284的冲击韧性大幅度提高;PES与5284树脂形成了双连续相结构,有效地阻止了裂纹的扩展,起到了增韧的作用。与未增韧复合材料相比,“离位”增韧ES-U3160/5284复合材料的I型层间断裂韧性(GⅠC)、Ⅱ型层间断裂韧性(GⅡC)及冲击后压缩强度(CAI)都有较大的提高。
Abstract
The effect of PES on the properties of 5284 resin and the toughening mechanism were investigated by SEM and mechanical properties tests of resin.ES-U3160 fabrics with toughening function were prepared according to ex-situ toughening technology.ES-U3160/5284 composites were prepared by RTM process taking ES-U3160 fabrics as reinforcement,and the properties of toughness of composites were studied.The results showed that with the increase of PES content,the impact toughness of 5284 resin was greatly improved.PES and 5284 resin formed a double continuous phase structure,which effectively prevented the crack propagation and played a role in toughening.GⅠC value,GⅡC value and CAI value of ES-U3160/5284 were greatly improved,compared with that of un-toughened composite.
关键词
ES-U3160织物
/
“离位”增韧
/
复合材料
/
冲击后压缩强度
/
层间断裂韧性
Key words
ES-U3160 fabrics
/
ex-situ toughening
/
composite
/
CAI
/
interlaminar fracture toughness
“离位”增韧ES-U3160/5284复合材料的制备及性能研究[J].
化工新型材料, 2019, 47(4): 167-170 DOI:
[1] Yee A F.Modifying matrix materials for tougher composites[C].ASTM Toughened Composite Symposium.Houston:1985.
[2] Joshi S P,Sun C T.Impact induced fracture in a laminated composite[J].Journal of Composites Materials,1985,19(1):51-66.
[3] Hull D,Shi Y B.Damage mechanism characterization in composite damage tolerance investigations[J].Composites Structure,1993,23(2):99-120.
[4] 益小苏,安学锋,唐邦铭,等.一种提高层状复合材料韧性的方法:中国,01100981.0[P].2001-03-26.
[5] 益小苏.先进树脂转移模塑树脂基复合材料技术研究进展[C].第十五届全国复合材料学术会议论文集.哈尔滨:2008.
[6] 刘志真,李宏运,邢军.RTM聚酰亚胺复合材料“离位”增韧技术研究[J].航空材料学报,2008,28(6):72-77.
[7] 闫丽,安学锋.RTM用ES-Fabric增强织物的制备及其复合材料性能研究[J].化工新型材料,2016,44(4):94-96.
[8] 张朋,刘刚,胡晓兰.结构化增韧层增韧RTM复合材料性能[J].复合材料学报,2012,29(4):1-9.
[9] Long W,Xu Y H,Yi X S.Preliminary study on resin transfer molding of highly toughened graphite laminate by ex-situ method[J].Journal of Materials Science,2004,39(6):2263-266.
[10] Cheng Q F,Fang Z P,Xu Y H,et al.Morphological and spatial effects on toughness and impact damage resistance of PAEK-toughened BMI and graphite fiber composite laminates[J].Chinese Journal of Aeronautics,2009,22(1):87-96.
[11] 益小苏,安学锋,张明,等.一种液态成型复合材料用预制织物及其制备方法:中国,200810000135.2[P].2008-01-04.
[12] Inoue,Akashi.Reaction-induced phase decomposition in polymer blends[J].Progress in Polymer Science,1995,20(1):119-153.