在溶剂热条件下,以硅中心四齿配体四(4-羧基苯基)硅烷和1-(四唑-5-基)-4-(三唑-1-基)-苯2种有机配体,成功制得新型的金属有机骨架结构材料(MOFs),为含有钴的金属有机骨架结构[Co3O(H2O)3L(ttb)]·3H2O(MOF-Co)],并对其进行了测试。研究结果表明,制得的MOF-Co结构为纯相,具有良好的热稳定性、化学稳定性和大的孔道,在亚甲基蓝溶液浓度为12mg/L,MOF-Co用量为10mg,吸附6h条件下,MOF-Co对亚甲基蓝的吸附率最高达到62.3%。
Abstract
Under the solvothermal conditon,a tetrahedral silicon-centred linker with space-directed was employed to successfully construct one novel MOFs,namely,[Co3O(H2O)3L(ttb)]·3H2O (MOF-Co).It was structurally confirmed by test.The adsorption ability of dye molecules in dye aqueous solution was also tested.The results showed that the structure of MOF-Co was pure phase and had good thermal stability,chemical stability and large pore channels.Under the conditions of 12mg/L of methylene blue solution,10mg of MOF-Co and 6h of adsorption,the maximum adsorption rate of methylene blue was 62.3%.
关键词
金属有机骨架结构材料
/
吸附
/
表征
/
染料
Key words
MOFs
/
adsorption
/
characterization
/
dye
新型MOFs材料的制备与表征及处理染料废水的研究[J].
化工新型材料, 2019, 47(3): 264-266 DOI:
[1] Zhu Qilong,Xu Qiang.Metal-organic framework composites[J].Chem Soc Rev,2014,43(16):5468-5512.
[2] Li Hailian,Eddaoudi Mohamed,OKeeffe M,et al.Design and synthesis of an exceptionally stable and highly porous metal-organic framework[J].Nature,1999,402(6759):276-279.
[3] Chung Kingthorn,Edward Stevens S,Cerniglia Carl E.The reduction of azo dyes by the Intestinal[J].Micro Crit Reviews Microbiology,2008,25:175-190.
[4] Liu Xiaoxia,Gong Wenpeng,Luo Jing,et al.Selective adsorption of cationic dyes from aqueous solution by polyoxometalate-based metal-organic framework composite[J].Appl Surf Sci,2016,362:517-524.
[5] Duan Shengxia,Li Jiaxing,Liu Xia,et al.HF-free synthesis of nanoscale metal-organic framework NMIL-100(Fe) as an efficient dye adsorbent[J].ACS Sustainable Chem Eng,2016,4(6):3368-3378.
[6] Zhang Caili,Li Pei,Cao Bing,et al.Selective adsorption and separation of organic dyes in aqueous solutions by hydrolyzed PIM-1 microfibers[J].Chem Eng Res Des,2016,109:76-85.
基金资助
吉林化工学院博士基金启动项目“MOFs材料对染料废水处理研究”(2017012)