将羽毛角蛋白(FK)、聚乙烯醇(PVA)及聚氧化乙烯(PEO)共混,利用静电纺丝加工技术制备FK纳米纤维膜,并使用戊二醛对其进行交联改性。利用扫描电子显微镜、傅里叶变换红外光谱仪、X射线衍射光谱仪、热重分析仪、差示扫描量热仪、接触角测量仪及电子万能试验机对交联前后纤维膜的形貌、结构、热稳定性、抗水性以及力学性能进行了测试和表征。结果表明:交联前纳米纤维膜的纤维结构均匀且光滑;随着交联剂戊二醛含量的增加,纤维膜形貌变化不大,热稳定性有所提高,接触角及力学性能增加较明显。当戊二醛质量占纺丝液溶质质量的15%时,纳米纤维膜的接触角大约是交联前的4倍,抗拉强度增至交联前的2.8倍。
Feather keratin (FK) was successfully blended with poly(vinyl alcohol) (PVA) and poly(ethylene oxide)(PEO).Then FK/PVA/PEO blend nanofibers were fabricated through electrospinning process.The glutaraldehyde was used as a crosslinker to improve the performance of blend nanofibers.The crosslinked nanofibers were characterized using scanning electron microscopy (SEM),fourier transform infrared (FT-IR) spectroscopy,X-ray diffraction (XRD),thermogravimetric analysis (TGA),water contact angle and universal testing machine.The results indicated that when the content of glutaraldehyde increased,the fiber morphology did not show any significant differences,whereas the fiber diameters were bigger than the uncrosslinked nanofibers.When the content of glutaraldehyde increased,the thermal stability increased,the contact angle and mechanical properties increased more obviously.The blend nanofibers with 15%-glutaraldehyde showed good water resistance properties and mechanical properties.The contact angle and tensile strength of nanofiber membrane were about 4 times and 2.8 times than the uncrosslinked nanofibers,respectively.
[1] 陈循军,尹国强,崔英德.羽毛角蛋白综合开发利用新进展[J].化工进展,2008,27(9):1390-1392.
[2] 王海洋.羽毛角蛋白/羧甲基纤维素钠共混薄膜的性能及应用研究[D].广州,仲恺农业工程学院,2014.
[3] 何明,尹国强,王品,等.羽毛蛋白接枝丙烯酸-丙烯酰胺高吸水性树脂的吸附性能[J].化工新型材料,2010,38(8):69-72.
[4] Na Ayutthaya S I,Wootthikanokkhan J.Extraction of keratin from chicken feather and electrospinning of the keratin/PLA blends[J].Advanced Materials Research,2013,747:711-714.
[5] 黄睿,朱静.静电纺丝参数对聚乙酸乙烯酯纤维形貌的影响[J].材料导报,2010,24(12):1-4.
[6] Zhang Y,Ouyang H,Lim C T,et al.Electrospinning of gelatin fibers and gelatin/PCL composite fibrous scaffolds[J].Journal of Biomedical Materials Research,2005,72(1):156-165.
[7] 徐晓红.纤维蛋白基纳米纤维的交联、表征及生物相容性研究[D].上海:东华大学,2010.
[8] 李佳.静电纺人发角蛋白-PEO纳米纤维支架制备与性能研究[D].天津,天津工业大学,2015.
[9] 李帅.羊毛角蛋白/聚乙烯醇纳米纤维膜的制备与表征[D].苏州,苏州大学,2014.
[10] 王雪娟,唐屹,吴炜誉,等.戊二醛交联胶原蛋白/PVA复合纤维的结构与性能[J].纺织学报,2007,28(11):13-16.
[11] 李春利,萨莎.戊二醛交联聚乙烯醇膜在醇/水介质中溶胀性能的研究[J].河北工业大学学报,2005,34(6):35-38.
[12] Rockland L B.Saturated salt solutions for static control of relative humidity between 5 and 40 C[J].Analytical Chemistry,1960,32(10):1375-1376.
[13] 朱永号,王闻宇,金欣,等.静电纺淀粉纳米纤维的交联改性研究[J].功能材料,2015,46(5):5048-5051.
[14] 张恒.角蛋白纳米复合功能纤维制备及其应用[D].上海:东华大学,2015.
[15] 刘雍,翟培羽,雷通达,等.高角蛋白含量的角蛋白/PEO纳米纤维的制备及其性能表征[J].天津工业大学学报,2016,35(6):1-7.
[16] Fan J,Lei T,Li J,et al.High protein content keratin/poly (ethylene oxide) nanofibers crosslinked in oxygen atmosphere and its cell culture[J].Materials & Design,2016,104:60-67.
[17] 邓湘文.羽毛角蛋白膜的制备及其交联改性研究[D].广州:仲恺农业工程学院,2014.
[18] 关曼.壳聚糖/大豆分离蛋白复合膜的制备、性能及应用[D].上海:上海海洋大学,2016.
[19] Li S,Yang X.Fabrication and characterization of electrospun wool keratin/poly(vinyl alcohol) blend nanofibers[J].Advances in Materials Science and Engineering,2014,2014:1-7.
[20] Choi J,Panthi G,Liu Y,et al.Keratin/poly (vinyl alcohol) blended nanofibers with high optical transmittance[J].Polymer,2015,58:146-152.
[21] Park M,Shin H K,Panthi G,et al.Novel preparation and characterization of human hair-based nanofibers using electrospinning process[J].International Journal of Biological Macromolecules,2015,76:45-48.
[22] Liu Y,Yu X,Li J,et al.Fabrication and properties of high-content keratin/poly (ethylene oxide) blend nanofibers using two-step cross-linking process[J].Journal of Nanomaterials,2015,2015(11):1-7.
[23] Liu Y,Li J,Fan J,et al.Preparation and characterization of electrospun human hair keratin/poly (ethylene oxide) composite nanofibers[J].Revista Materia,2014,19(4):382-388.
[24] 吕梦青,曹鼎,石艳,等.静电纺丝PET/PVA复合纳米纤维膜的制备及性能[J].化工进展,2012,31(11):2531-2534.
[25] Spei M,Holzem R.Thermoanalytical investigations of extended and annealed keratins[J].Colloid & Polymer Science,1987,265(11):965-970.
基金资助
广东省科技计划项目(2013B010403029);广东省自然科学基金项目(2016A030313371)
PDF
(4920KB)