采用溶胶-凝胶自蔓延燃烧法制备了漂珠/钡铁氧体磁性粉体,并以此为核,再利用原位掺杂聚合法制备出兼具电性能和磁性能的漂珠/钡铁氧体/聚苯胺复合材料。通过扫描电镜(SEM)、红外光谱(FT-IR)、X射线衍射(XRD)、振动样品磁强计(VSM)和矢量网络分析仪(VNA)等表征手段,分析了该材料的微观形貌、结构、电磁性能及吸波性能。结果表明,制备的漂珠/钡铁氧体/聚苯胺复合材料表层呈珊瑚状结构,存在聚苯胺和钡铁氧体的特征衍射峰;复合材料的磁性能随聚苯胺掺杂量的增加而减弱,但吸波性能却随之增强;当吸波层厚度为1.2mm、频率为16.4GHz时,样品的吸收峰值可达-42.94dB。
The magnetic composites of cenosphere/barium ferrite were prepared by a sol-gel auto-combustion method.Then,the electromagnetic composite materials of cenosphere/barium ferrite/polyaniline were successfully synthesized using in-situ doping polymerization deposition technique.The morphology,structure,electromagnetic and microwave absorption properties of composite powders were characterized by scanning electron microscope (SEM),fourier transform infrared spectroscopy (FT-IR),X-ray diffraction (XRD),vibrating sample magnetometer (VSM) and vector network analyzer (VAN).The results showed that the composites had characteristic diffraction peaks of polyaniline and barium ferrite,and the cenospheres surfaces were covered with coral-like coating.In addition,the magnetic properties decreased with increasing the amount of polyaniline,while the microwave absorption properties were enhanced.The maximum microwave reflection loss reached -42.94dB at 16.4GHz with a sample thickness of 1.2mm.
[1] 景红霞,李巧玲,叶云,等.羰基铁/钛酸钡复合材料的制备及吸波性能[J].材料工程,2015,43(7):38-42.
[2] 刘渊,刘祥萱,王煊军.铁氧体基核壳结构复合吸波材料研究进展[J].材料工程,2014,42(7):98-106.
[3] 冯辉霞,王果,陈姣,等.聚苯胺/钴铁氧体电磁复合材料的制备及其性能[J].化工进展,2015,34(9):3374-3378.
[4] Yan S F,Xie Y,Liu J M,et al.Preparation of Nd-doped manganese-zinc-ferrite/polyaniline composite materials[J].Materials Research Innovations,2014,18(3):225-230.
[5] Ting T H,Jau Y N,Yu R P.Microwave absorbing properties of polyaniline/multi-walled carbon nanotube composites with various polyaniline contents[J].Applied Surface Science,2012,258(7):3184-3190.
[6] Zhu Y F,Zhang L,Natsuki T,et al.Synthesis of hollow poly(aniline-co-pyrrole)-Fe3O4 composite nanospheres and their microwave absorption behavior[J].Synthetic Metals,2012,162(3/4):337-343.
[7] Belaabed B,Wojkiewicz J L,Lamouri S,et al.Synthesis and characterization of hybrid conducting composites based on polyaniline/magnetite fillers with improved microwave absorption properties[J].Journal of Alloys and Compounds,2012,527(12):137-144.
[8] Li Q,Pang J F,Wang B,et al.Preparation,characterization and microwave absorption properties of barium-ferrite-coated fly-ash cenospheres[J].Advanced Powder Technology,2013,24(1):288-294.
[9] 庞建峰,李建.漂珠/钡铁氧体/聚苯胺复合材料的制备及吸波性能研究[J].电子元件与材料,2012,31(3):40-44.
[10] 徐平.导电聚合物及其纳米复合材料的制备和性能研究[D].哈尔滨:哈尔滨工业大学,2010.
[11] 姜静静.导电聚苯胺/钡铁氧体复合材料的制备及吸波性能[D].哈尔滨:哈尔滨工业大学,2007.
[12] Mali A,Ataie A.Structural characterization of nano-crystalline BaFe12O19 powders synthesized by sol-gel combustion route[J].Scripta Materialia,2005,53(9):1065-1070.
[13] Yu H F,Liu P C.Effects of pH and calcination temperatures on the formation of citrate-derived hexagonal barium ferrite particles[J].Journal of Alloys and Compounds,2006,416(1):222-227.
[14] 李元勋.M型钡铁氧体及其复合材料的应用基础研究[D].成都:电子科技大学,2008.
[15] 牟国洪.空心微球/钡铁氧体轻质复合粉末的制备和吸波性能研究[D].上海:上海交通大学,2008.
[16] Tang X,Yang Y.Surface modification of M-Ba-ferrite powders by polyaniline:towards improving microwave electromagnetic response[J].Applied Surface Science,2009,255(23):9381-9385.
基金资助
淮阴工学院自然科学基金项目(16HGZ001);淮安市科技计划项目(HAS2015008)
PDF
(2899KB)