为实现批量制备性能优异的纤维膜,设计了一种针片辊式微分静电纺丝装置,以聚乙烯醇(PVA)静电纺丝为例,讨论了PVA溶液浓度和针片间距对纤维直径分布和纤维产能的影响。研究结果表明:随着PVA溶液浓度的增大(8%～11%,wt,质量分数),纤维平均直径越粗,直径分布范围也越大;针片间距主要影响针片尖端的电场强度分布,随着针片间距的增大,针片间电场强度分布更加均匀,当针片间距为10mm条件下,各个针片尖端的电场强度分布均匀性明显改善,制备的纤维膜直径分布范围较小,PVA溶液浓度为8%(wt,质量分数)条件下的纤维直径为(161±67)nm;纤维膜产量随PVA溶液浓度的增大逐渐升高,针片间距10mm,PVA溶液浓度为11%(wt,质量分数)条件下,获得最高的纺丝产能为12.8g/h。
Abstract
In order to efficiently prepare high quality fiber membrane,a new type of needle roller differential electrospinning device was designed.The effect of spinning solution concentration and the needle piece spacing on fiber diameter distribution and fiber productivity were examined by taking PVA as a model polymer.The results showed that with the increase in the concentration of spinning solution (8wt%～11wt%),the average diameter of fibers was larger and the range of diameter distribution was wider.The electric field intensity distribution at the tip of the needle piece was mainly affected by the spacing of needle piece.With the increase in the needle piece spacing,the uniformity of electric field intensity distribution at each tip of needle piece were obviously improved,and the range of fiber diameter distribution was narrower.When the needle piece spacing was 10mm,spinning solution concentration was 8wt%,the fiber diameter was (161±67)nm.The fiber productivity increased with the increase in the concentration of spinning solution.The maximum spinning efficiency was 12.8g/h when the needle piece spacing was 10mm and the spinning solution concentration was 11wt%.
关键词
微分静电纺丝
/
PVA纤维膜
/
针片
/
电场强度
Key words
differential electrospinning
/
PVA fiber membrane
/
needle roller
/
electric field intensity
针片辊式溶液微分电纺批量制备PVA纤维研究[J].
化工新型材料, 2018, 46(10): 207-209 DOI:
[1] 王策.有机纳米功能材料:高压静电纺丝技术与纳米纤维[M].北京:科学出版社,2011,4-28.
[2] 马贵平,方大为,刘洋,等.电纺丝制备纳米纤维及其应用[J].材料科学与工程学报,2012,30(2):312-323.
[3] Theron S A,Zussman E,Yarin A L.Experimental investigation of the governing parameters in the electrospinning of polymer solutions[J].Polymer,2004,45(6):2017-2030.
[4] Kim G H,Cho Y S,Wan D K.Stability analysis for multi-jets electrospinning process modified with a cylindrical electrode[J].European Polymer Journal,2006,42(9):2031-2038.
[5] Ramakrishnan R,Gimbun J,Samsuri F,et al.Needleless electrospinning technology-an entrepreneurial perspective[J].Indian Journal of Science & Technology,2016,9(15):1-11.
[6] Yarin A L,Zussman E.Upward needleless electrospinning of multiple nanofibers[J].Polymer,2004,45(9):2977-2980.
[7] Liu Y,He J H.Bubble electrospinning for mass production of nanofibers[J].International Journal of Nonlinear Sciences & Numerical Simulation,2007,8(3):393-396.
[8] Wang X,Niu H,Lin T,et al.Needleless electrospinning of nanofibers with a conical wire coil[J].Polymer Engineering & Science,2009,49(8):1582-1586.
[9] Jiang G,Zhang S,Qin X.High throughput of quality nanofibers via one stepped pyramid-shaped spinneret[J].Materials Letters,2013,106(106):56-58.
[10] Niu H,Wang X,Lin T.Needleless electrospinning:influences of fibre generator geometry[J].Journal of the Textile Institute Proceedings & Abstracts,2012,103(7):787-794.
[11] Niu H T,Lin T,Wang X G.Needleless electrospinning(1),a comparison of cylinder and disk nozzles[J].Journal of Applied Polymer Science,2009,114(6):3524-3530.
[12] Wang X,Niu H,Wang X,et al.Needleless electrospinning of uniform nanofibers using spiral coil spinnerets[J].Journal of Nanomaterials,2012,2012(10):1-3.
基金资助
国家自然科学基金(51603009);国家重点研发计划(2016YFB0302002)