为解决塔河油田在注水开发过程中因地层水不配伍而出现的碳酸垢和硫酸垢结垢问题,以自制三羟乙基烯丙基溴化铵(THAAB)、马来酸酐(MA)和2-丙烯酰胺基-2-甲基丙磺酸(AMPS)为反应单体,采用水溶液聚合,制得了多羟基聚合物型阻垢剂聚三羟乙基烯丙基溴化铵/马来酸酐/2-丙烯酰胺基-2-甲基丙磺酸(PTMAS)。对产物进行红外光谱与凝胶色谱分析,结果表明其分子结构符合预期设计且分子量大小适中,分子量在2×104～5×104之间,适于作为聚合物阻垢剂。热重分析证明其抗温性能较强,在250℃之前质量保留率高达80%,并未出现大的质量损失。在碳酸钙阻垢实验中,PTMAS添加量不低于25mg/L,适用温度为20～80℃,pH不超过10,有效阻垢时间不小于18h,阻垢率可高达92%,表明PTMAS的适用工况极为宽泛。室内实验结果表明对于硫酸钙、硫酸钡与硫酸锶垢的析出成垢亦有良好阻垢效果。
Abstract
In order to solve the problem of scale in the process of water flooding development in Tahe oilfield due to incompatibility of formation water.A polyhydroxy polymer scale inhibitor trihydroxyethyl allyl ammonium bromide/maleic anhydride/2-acrylamido-2-methylpropanesulfonic acid (PTMAS) was prepared vis aqueous solution by using trihydroxyethyl allyl ammonium bromide(THAAB),maleic anhydride (MA) and 2-acrylamido-2-methylpropanesulfonic acid (AMPS) as reaction monomers.The product was characterized by FT-IR and gel chromatography.The results showed that the molecular structure was in accordance with the expected design and the molecular weight was moderate.The molecular weight was between 2×104～5×104,and was suitable as a polymer scale inhibitor.Thermogravimetric analysis showed that the temperature resistance was strong,and the mass retention rate was as high as 80% before 250℃,and there was no heavy weight loss occurred.In the calcium carbonate scale inhibition experiment,PTMAS dosage was not less than 25mg/L,temperature was 20～80℃,pH value does not exceed 10,effective scale inhibition time was not less than 18h,and the scale inhibition rate can be up to 92%,indicating the extremely broad application of PTMAS.The results of laboratory experiments showed that there was a good scale inhibition effect on the precipitation of calcium sulfate,barium sulfate and strontium sulfate scale.
关键词
多羟基
/
阻垢剂
/
阻垢性能
/
水溶液聚合
Key words
polyhydroxy group
/
scale inhibitor
/
scale inhibitive property
/
aqueous solution polymerization
多羟基阻垢剂PTMAS的研制与应用[J].
化工新型材料, 2018, 46(8): 285-289 DOI:
[1] Li J B,Tang M J,Ye Z R,et al.Scale formation and control in oil and gas fields:a review[J].J Disper Sci Technol,2017,38(5):661-670.
[2] Yi T,Jin Z,Li X C,et al.A bohai sea SZ36-1 oil field formation scaling experimental study and scale inhibitor optimization[J].Petrol Sci Technol,2014,32(20),2512-2519.
[3] Gu T,Su P C,Liu X Y,et al.A composite inhibitor used in oilfield:MA-AMPS and imidazoline[J].J Petrol Sci Eng,2013,102(1):41-46.
[4] 金绍娣,朱驯,周秀芹.一种磺化苯乙烯/N-马来酰-L-谷氨酸共聚物的合成及阻垢性能研究[J].化工新型材料,2015,43(3):184-186.
[5] Sanders L,Hu X M,Mavredaki E,et al.Assessment of combined scale/corrosion inhibitors-a combined jar test/bubble cell[J].J Petrol Sci Eng,2014,118(3):126-139.
[6] Li M D,Dai C L,Yang B,et al.New and green multi-component scaling and corrosion inhibitor for the cooling water of central air conditioners[J].J Mater Eng Perform,2017,26(2):764-772.
[7] Rahman F.Calcium sulfate precipitation studies with scale inhibitors for reverse osmosis desalination[J].Desalination,2013,319(12):79-84.
[8] 黄伯芬.水溶性高分子材料ZG-3丙烯酸共聚物阻垢分散剂[J].化工新型材料,2002,30(9):33-34,40.
[9] Gu T,Liu X Y,Chai W B,et al.A preliminary research on polyvinyl alcohol hydrogel:a slowly-released anti-corrosion and scale inhibitor[J].J Petrol Sci Eng,2014,122(1):453-457.
[10] Li G,Guo S H,Zhang J W,et al.Inhibition of scale buildup during produced-water reuse:optimization of inhibitors and application in the field[J].Desalination,2014,351(3):213-219.
[11] 蒲晓林,都伟超,孙金声,等.多羟基有机铵黏土防膨剂的合成及应用[J].石油化工,2016,45(5):595-600.
[12] 都伟超.黏土水化抑制剂Gemini-DHEDB和PDWC的合成及作用机理研究[D].成都:西南石油大学,2017.
基金资助
“十三五”国家科技重大专项(2016ZX05053)