腰果酚基聚氨酯的合成及性能研究

张菲, 耿爱芳, 阎敬灵, 李云辉, 王震

作者信息 +

Synthesis and property of cardanol-based polyurethane

Author information +

文章历史 +

Received		Published
2017-01-05		2018-04-20
Issue Date	Revised Date
2018-05-17	2017-01-05

PDF (1276K)

摘要

以环氧化柠檬酸三(2-腰果酚氧基乙基)酯(ET3)和甲醇反应制备了三臂型腰果酚基多元醇,用核磁共振波谱仪(¹H-NMR)确定了该多元醇的结构。用腰果酚基多元醇和六亚甲基二异氰酸酯(HDI)、异氟尔酮二异氰酸酯(IPDI)等反应合成了腰果酚基聚氨酯,并通过动态热机械分析(DMTA)和热重分析(TGA)考察了固化膜的玻璃化转变温度(T_g)和热稳定性,通过拉伸测试考察固化膜的机械力学性能。结果发现,该树脂玻璃化转变温度最高可达43℃,拉伸强度最高可达940MPa,有较高的生物基含量和良好的综合性能,具有一定的应用价值。

Abstract

Cardanol-based polyol was prepared via the ring-open reaction between methanol and epoxidized tri(2-cardanoxyethyl) citrate,and its structural was confirmed by proton nuclear magnetic resonance (¹H-NMR).Bio-based thermosets were then formulated using cardanol-based polyol and commercial isocyanate (hexamethylene diisocyanate (HDI,isophorone disiocyanate (IPDI),etc.) as the raw materials.The property of polyurethane was studied through dynamic thermal mechanical analysis (DMTA),thermogravimetric analysis (TGA) and tensile testing.The results revealed that the glass transition temperature of polyurethane was 43℃,The tensile strength was 940MPa.They possessed a good combination of high bio-based content and overall properties.

关键词

生物基聚氨酯 / 腰果酚基多元醇 / 热性能 / 力学性能

Key words

bio-based polyurethane / cardanol-based polyol / thermal property / mechanism

引用本文

引用格式 ▾

张菲, 耿爱芳, 阎敬灵, 李云辉, 王震. 腰果酚基聚氨酯的合成及性能研究[J]. 化工新型材料, 2018, 46(4): 251-253 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Campanella A,Bonnaillie L M,Wool R P.Polyurethane foams from soyoil-based polyols[J].Journal of Applied Polymer Science,2009,112(4):2567-2578.
[2] Balachandran V S,Jadhav S R,Vemula P K.Recent advances in cardanol chemistry in a nutshell:from a nut to nanomaterials[J].Chemical Society Reviews,2013,42(2):427-438.
[3] 刘国际,张勇,刘伟.腰果酚的应用研究进展[J].材料导报,2012,26(9):90-94.
[4] Huang K,Zhang Y,Li M.Preparation of a light color cardanol-based curing agent and epoxy resin composite:cure-induced phase separation and its effect on properties[J].Progress in Organic Coatings,2012,74(1):240-247.
[5] Mythili C V,Retna A M,Gopalakrishnan S.Synthesis,mechanical,thermal and chemical properties of polyurethanes based on cardanol[J].Bulletin of Materials Science,2004,27(3):235-241.
[6] Sathiyalekshmi K,Gopalakrishnan S.Evaluation of performance of polyurethanes based on hydroxy alkylated cardanol formaldehyde resins under aging conditions[J].Advances in Polymer Technology,2004,23(2):91-102.
[7] Mythili C V,Malar Retna A,Gopalakrishnan S.Physical,mechanical,and thermal properties of polyurethanes based on hydroxyalkylated cardanol-formaldehyde resins[J].Journal of Applied Polymer Science,2005,98(1):284-288.
[8] Suresh K I,Kishanprasad V S.Synthesis,structure,and properties of novel polyols from cardanol and developed polyurethanes[J].Industrial and Engineering Chemistry Research,2005,44(13):4504-4512.
[9] Ionescu M,Petrović Z S,Wan X.Ethoxylated soybean polyols for polyurethanes[J].Journal of Polymers and the Environment,2007,15(4):237-243.
[10] 冯卫炜.柠檬酸腰果酚酯热固性树脂的合成[D].无锡:江南大学化学与材料工程学院,2015.