通过高温热蒸发硅粉工艺,以鳞片石墨、膨胀鳞片石墨、纳米炭黑和微米炭黑为碳源制备SiC晶须,研究了碳源结构对SiC晶须生长的影响。采用X射线衍射、扫描电镜和透射电镜等手段对不同碳源和制得样品的微观形貌和结构进行表征。结果表明:SiC晶须更容易在膨胀鳞片石墨和纳米炭黑表面生长,碳源具有乱层堆垛石墨结构和合适的晶粒尺寸是SiC晶须生长的决定性因素。
Using graphite flake,expanded graphite flake,nanosized pyrolytic carbon black and microsized thermal carbon black as carbon sources,SiC whiskers were prepared by thermal evaporation of silicon powders at high temperature and the effect of carbon source microstructure on the growth of SiC whiskers was investigated.The morphology and microstructure of different carbon sources and the as-obtained product were characterized by X-ray diffraction,scanning electron microscopy and transmission electron microscopy.The results showed that SiC whiskers was prefer to grow on the surface of expanded graphite flake and nanosized pyrolytic carbon black.The critical factors for promoting the formation of SiC whiskers were that the carbon sources should possess turbostratically stacked graphite structure and appropriate grain size.
[1] Liu X F,Liu H L,Huang C Z,et al.High temperature mechanical properties of Al2O3-based ceramic tool material toughened by SiC whiskers and nanoparticles[J].Ceram Int,2017,43(1):1160-1165.
[2] Wu R B,Zhou K,Yue C Y,et al.Recent progress in synthesis,properties and potential applications of SiC nanomaterials[J].Prog Mater Sci,2015,72:1-60.
[3] Men J,Liu Y S,Luo R,et al.Growth of SiC nanowires by low pressure chemical vapor infiltration using different catalysts[J].J Eur Ceram Soc,2016,36(15):3615-3625.
[4] 袁观明,李保六,李轩科,等.碳化硅纳米线的制备及表征[J].化工新型材料,2015,43(11):98-101.
[5] 谢定方,杭志喜,李传宗.稻壳制备哑铃状碳化硅晶须仿生模型[J].化工新型材料,2014,42(5):150-152.
[6] Xin L P,Shi Q,Chen J J,et al.Morphological evolution of one-dimensional SiC nanomaterials controlled by sol-gel carbothermal reduction[J].Mater Charact,2012,65(1):55-61.
[7] Tang C C,Fan S S,Dang H Y,et al.Growth of SiC nanorods prepared by carbon nanotubes-confined reaction[J].J Cryst Growth,2000,210(4):595-599.
[8] Chen J J,Pan Y,Wu R B.Growth mechanism of twinned SiC nanowires synthesized by a simple thermal evaporation method[J].Physica E,2010,42(9):2335-2340.
[9] Wei J,Li K Z,Li H J,et al.Photoluminescence performance of SiC nanowires,whiskers and agglomerated nanoparticles synthesized from activated carbon[J].Physica E,2009,41(8):1616-1620.
[10] Zhao H S,Shi L M,Li Z Q,et al.Silicon carbide nanowires synthesized with phenolic resin and silicon powders[J].Physica E,2009,41(4):753-756.
[11] Chen J J,Wu R B,Yang G Y,et al.Synthesis and photoluminescence of needle-shaped 3C-SiC nanowires on the substrate of PAN carbon fiber[J].J Alloys Compd,2008,456(1-2):320-323.
[12] Zhou D,Seraphin S.Production of silicon carbide whiskers from carbon pyrolyticclusters[J].Chem Phys Lett,1994,222(3):233-238.
[13] Li Y W,Wang Q H,Fan H B,et al.Synthesis of silicon carbide whiskers using reactive graphite as template[J].Ceram Int,2014,40(1):1481-1488.
[14] Wu Y J,Qin W,Yang Z X,et al.Preparation of high-quality β-SiC nanowhiskers by using carbon fibres as carbon source[J].J Mater Sci,2004,39:5563-5565.
[15] Tu C H,Chen W,Fang H C,et al.Heteroepitaxial nucleation and growth of graphene pyrolyticwalls on silicon[J].Carbon,2013,54:234-240.
[16] Zhu H,Li X K,Han F,et al.The effect of pitch-based carbon fiber microstructure and composition on the formation and growth of SiC whiskers via reaction of such fibers with silicon sources[J].Carbon,2016,99:174-185.
基金资助
国家自然科学基金(51372177)
PDF
(6896KB)