采用剑麻纳米纤维素与吡咯通过原位化学氧化法制备聚吡咯(PPy)@剑麻纳米纤维素(CNF)(PPy@CNF)复合材料,采用扫描电子显微镜(SEM)、X射线衍射仪(XRD)和能谱仪(EDS)对PPy@CNF进行形貌和结构表征,研究PPy@CNF在溶液中对偶氮类有机阴离子染料甲基橙(MO)的吸附效果,结果表明,在聚合时吡咯单体浓度为6.0g/L时,PPy@CNF对MO吸附容量最大,达到335.1mg/g。
Polypyrrole@sisal nanocellulose (PPy@CNF) composites were prepared with sisal nanocellulose and pyrrole via a simple in-situ chemical oxidation polymerization.The morphology and structure of PPy@CNF were analyzed by SEM,XRD and EDS respectively.And the adsorption properties of PPy@CNF on methyl orange (MO) which was azo organic anionic dyes were investigated,the results indicated that the best adsorption effect was 335.1mg/g when the concentration of pyrrole monomer was 6.0g/L.
[1] 鄂学礼,凌波.饮水污染对健康的影响[J].中国卫生工程学,2006,5(1):3-5.
[2] 李婧.化学-生物组合工艺处理印染废水的应用研究[D].长春:吉林大学,2011.
[3] Gupta Vinod K,Suhas Dr.Application of low-cost adsorbents for dye removal-a review[J].Journal of Environmental Management,2009,90:2313-2342.
[4] Omastová M,Trchová M,Kovárová J,et al.Synthesis and structural study of polypyrroles prepared in the presence of surfactants[J].Synthetic Metals,2003,138(3):447-455.
[5] Bhaumik M,McCrindle R,Maity A.Efficient removal of Congo red from aqueous solutions by adsorption onto interconnected polypyrrole-polyaniline nanofibres[J].Chemical Engineering Journal,2013,228:506-515.
[6] Wang S Q,Wei C,Gong Y Y,et al.Cellulose nanofiber-assisted dispersion of cellulose nanocrystals@polyaniline in water and its conductive films[J].RSC Advances,2016,6:10168-10174.
[7] Muller D,Rambo C R,Porto L M,et al.Structure and properties of polypyrrole/bacterial cellulose nanocomposites[J].Carbohydrate Polymers,2013,94(1):655-662.
[8] Sghaier A E O B,Chaabouni Y,Msahli S,et al.Morphological and crystalline characterization of NaOH and NaOCl treated agave americana L.fiber[J].Industrial Crops and Products,2012,36(1):257-266.
[9] Ramesan M T.Synthesis,characterization,and conductivity studies of polypyrrole/copper sulfide nanocomposites[J].Journal of Applied Polymer Science,2013,128(3):1540-1546.
基金资助
国家自然科学基金(21264005);广西自然科学基金(2013GXNSFDA019008);广西有色金属及特色材料加工国家重点实验室培育基地开放基金(13AA-6)
PDF
(2115KB)