以醋酸为催化剂,乙醇为分散剂,先将偶联剂KH-570经溶胶-凝胶过程,生成表面带烯键的硅溶胶,再将其与工业化生产的常见硅溶胶共混,经过两种硅溶胶的交换、陈化等过程,使得工业化生产的常见硅溶胶的表面带上烯键,实现对工业化硅溶胶表面的烯键修饰。通过傅里叶红外光谱(FT-IR)、扫描电子显微镜(SEM)和热重分析(TGA)等表征手段对修饰改性前后的硅溶胶样品进行了表征。结果表明:硅烷偶联剂KH-570的不饱和烯键成功接枝到纳米硅溶胶的表面。
The silica sol with unsaturated double bond on the surface has been successfully prepared by sol-gel process of KH570 with acetate and water as catalyst and dispersant respectively.And the prepared silica sol was used to modify the industrialized silica sol by the exchange and aging process.Modified silica sol and unmodified silica sol were characterized by SEM,FT-IR and TGA.The results showed that unsaturated double bond of KH570 was successfully grafted to the surface of silica sol.
[1] 马纯超,郑典模.硅溶胶的制备与应用[J].山东化工,2008,37(5):26-29.
[2] 马纯超.硅溶胶的制备新工艺研究[D].南昌:南昌大学,2008.
[3] 段晓娜,孙羊羊,张海红,等.硅溶胶的研究进展及应用[J].硅酸盐通报,2014,33(4):836-840.
[4] 田立朋,孙道兴,王力.硅溶胶的制备及其在涂料中的应用[J].上海涂料,2006,44(11):23-25.
[5] 殷馨,戴媛静.硅溶胶的性质、制法及应用[J].化学推进剂与高分子材料,2005,3(6):35-40.
[6] 田华,陈连喜,刘全文.硅溶胶的性质、制备和应用[J].国外建材科技,2007,28(2):8-11.
[7] 王自新,赵冰.硅溶胶制备与应用[J].化学推进剂与高分子材料,2003,1(5):34-39.
[8] 黄月文,刘伟区,任昕.水性纳米硅溶胶的表面改性及其应用研究[J].广州化学,2009,34(1):14-21.
[9] 段辉.掺杂氟化聚合物/硅溶胶超疏水复合涂层的制备及性能研究[D].武汉:武汉科技大学,2006.
[10] 蒲泽佳,侯建硕,陈迎春,等.涤纶织物的有机硅改性硅溶胶超疏水整理[J].印染,2015,41(20):1-4.
[11] 李洁,陈连喜,张中明,等.硅溶胶的表面改性及应用研究进展[J].建材世界,2012,33(3):1-4.
[12] 叶雨佐,李红强,卢俊杰,等.KH-570改性硅溶胶的制备及反应稳定性研究[J].有机硅材料,2011,25(3):153-156.
[13] 吴丹华,于杰,秦舒浩,等.表面改性纳米硅溶胶的制备与表征[J].现代化工,2012,32(7):70-73.
基金资助
福建省科技厅引导性项目(2016H0012);福建省教育厅产学研项目(JA15101);福州市区域科技重大项目(2015QC0043);福建师范大学泉港石化研究院探索性项目(2015YJY02)
PDF
(2254KB)